Rapidly-cured UV water-based solid color finish paint and preparation method thereof

A fast-curing, water-based technology, used in coatings, polyurea/polyurethane coatings, etc., can solve the problems of easy scratching, long curing time, low production efficiency, etc., to avoid VOC emissions, film-forming surface performance, The effect of fast production efficiency

Active Publication Date: 2022-07-19
上海君子兰新材料股份有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002]As people pay more and more attention to their health, the solvent-based UV spray topcoat used in the wood coating industry is gradually abandoned by people, and they begin to turn their attention to Water-based coatings, but the interaction between water-based coatings and wood substrates is not good, which cannot meet people's pursuit of wood product performance
[0003] Chinese invention patent CN202011195315.8 discloses a water-based UV-curable polyurethane coating, which forms a cross-linked three-dimensional network structure through the reaction of polyurethane acrylate and phosphoric acid-modified acrylic resin. Improved adhesion between coating and substrate, but longer cure time and lower productivity
Chinese invention patent CN201911165845.5 discloses a light-curable water-based coating resin, which uses water-based polyurethane acrylate and acrylate compounds containing hydrophilic groups to shorten the curing time of the coating, but the hardness of the coating is low. It is easy to be scratched, which shortens the service life of the wood

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rapidly-cured UV water-based solid color finish paint and preparation method thereof
  • Rapidly-cured UV water-based solid color finish paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] A fast-curing UV water-based solid color topcoat, the raw materials for preparation include, in parts by weight: 70 parts of polyurethane acrylate emulsion, 15 parts of acrylic emulsion, 3 parts of film-forming auxiliary, 8 parts of water, 3 parts of wetting and dispersing agent, 1.5 parts of defoamer, 1.5 parts of leveling agent, 6 parts of matting powder, 1.5 parts of thickener, 4 parts of photoinitiator, 0.5 part of antifungal agent, and 6 parts of white pulp.

[0057] Described urethane acrylate emulsion is the combination that the functionality is 6 and the functionality is 2, and the weight ratio is 1:1; the urethane acrylate emulsion that the functionality is 6, the model is Zhaoqing Baojun 2036W, purchased from Zhaoqing Baojun Chemical Co., Ltd. ; Polyurethane acrylate emulsion with a functionality of 2, model POL YCL-5003, purchased from Shanghai Chang-Chain New Material Technology Co., Ltd.

[0058] The viscosity of the acrylic emulsion at 30°C is 180mPas, and...

Embodiment 2

[0073] A fast-curing UV water-based solid color topcoat and a preparation method thereof, the specific steps are the same as those in Example 1, the difference is that the functionality of the polyurethane acrylate emulsion is 6, and the model is Zhaoqing Baojun 2036W, purchased from Zhaoqing Baojun Chemical Co., Ltd. limited company

Embodiment 3

[0075] A fast-curing UV water-based solid color topcoat and a preparation method thereof, the specific steps are the same as those in Example 1, the difference is that the film-forming aid is dipropylene glycol methyl ether.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a rapidly cured UV water-based solid color finish paint, which is prepared from the following raw materials in parts by weight: 40 to 80 parts of polyurethane acrylate emulsion, 10 to 20 parts of acrylic emulsion, 1 to 5 parts of coalescing agent, 5 to 10 parts of water, 1 to 5 parts of wetting dispersant, 1 to 2 parts of defoaming agent, 1 to 2 parts of flatting agent, 1 to 10 parts of matting powder, 1 to 2 parts of thickening agent, 3 to 5 parts of photoinitiator, 0.1 to 1 part of mildew preventive and 5 to 10 parts of white paste. According to the invention, the strength of a finish paint film is improved, the bottom layer of the paint is thoroughly cured, the adhesive force of the paint is improved, the coalescing agents with different volatilization rates enable water in the paint to be rapidly volatilized, miliaria bubbles are avoided, the film-forming surface performance is good, and meanwhile, the paint is a novel environment-friendly paint, is high in curing speed, and has the advantages of fingerprint prevention, non-sticking, stain resistance, scratch resistance and the like. Self-repairing is realized; and the production efficiency is high.

Description

technical field [0001] The invention relates to a fast-curing UV water-based solid color topcoat, relates to C09D, and in particular relates to the field of coating compositions. Background technique [0002] As people pay more and more attention to physical health, the solvent-based UV spray topcoat used in the wood coating industry is gradually abandoned, and people begin to turn their attention to water-based coatings, but the interaction between water-based coatings and wood substrates is not sufficient. Well, it cannot satisfy people's pursuit of the performance of wood products. [0003] Chinese invention patent CN202011195315.8 discloses a water-based UV-curable polyurethane coating, which forms a cross-linked three-dimensional network structure through the reaction of polyurethane acrylate and phosphoric acid-modified acrylic resin, which improves the adhesion between the coating and the substrate, but the curing time longer and less productive. Chinese invention p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D133/00C09D7/63C09D7/62C09D7/00C09D7/80
CPCC09D175/14C09D7/63C09D7/62C09D7/00C09D7/80C08K2003/2241C08L33/00C08K5/06C08K9/04C08K3/22
Inventor 范新强叶国庆崔新磊邓文根刘伟王海军
Owner 上海君子兰新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products