A technology of nitrile rubber and nitrile rubber, applied in the direction of rolling resistance optimization, road transportation emission reduction, etc., can solve the problems of cold resistance, oil resistance, poor mildew resistance, and no mechanical properties of nitrile rubber materials, and achieve mildew resistance. Good, small compression set, the effect of improving tensile strength

Pending Publication Date: 2022-08-05
SHENYANG RUBBER RES & DESIGN INST CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The above-mentioned nitrile rubber material has obvious reduction in hardness and significant increase in elongation at break through the addition of reinforcing filler white carbon black, but the above-mentioned nitrile rubber material has no good mechanical properties, cold resistance, oil resistance, and mildew resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mildew-proof cold-resistant nitrile rubber material and preparation method thereof
  • Mildew-proof cold-resistant nitrile rubber material and preparation method thereof
  • Mildew-proof cold-resistant nitrile rubber material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0052] For example, please refer to the appendix Figure 1-8 , a mildew-proof and cold-resistant nitrile rubber material, comprising the following substances by weight:

[0053] No. 1 Nitrile rubber 65 parts

[0054] The second nitrile rubber 35 parts

[0055] 5 parts zinc oxide

[0056] 1 part stearic acid

[0057] Anti-aging agent 4020 3 parts

[0058] 23 parts of dibutyl sebacate

[0059] Spray carbon black 120 parts

[0060] Pre-dispersed sulfur 0.4 part

[0061] Accelerator TMTD 2 parts

[0062] Accelerator CZ 2 parts

[0063] 2 parts of mildew inhibitor;

[0064] It should be noted that, in this embodiment, the first NBR is made of NBR1704 NBR with acrylonitrile content of 17-20%, and the second NBR is made of NBR1704 with acrylonitrile content of 27-30%. NBR2707 nitrile rubber.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a mildewproof cold-resistant nitrile rubber material and a preparation method thereof. The mildewproof cold-resistant nitrile rubber material comprises the following substances in parts by weight: 65 parts of first nitrile rubber, 35 parts of second nitrile rubber, 5 parts of zinc oxide, 1 part of stearic acid, 203 parts of an anti-aging agent 403, 23 parts of dibutyl sebacate, 120 parts of spray carbon black, 0.4 part of pre-dispersed sulfur, 2 parts of an accelerant TMTD, 2 parts of an accelerant CZ and 2 parts of a mildewproof agent. The nitrile rubber material has mechanical properties, cold resistance, oil resistance and mildew resistance at the same time.

Description

technical field [0001] The invention mainly relates to the technical field of preparation of NBR, in particular to a mildew-proof and cold-resistant nitrile rubber material and a preparation method thereof. Background technique [0002] Nitrile rubber is a copolymer of acrylonitrile and butadiene monomers, mainly produced by low temperature emulsion polymerization. [0003] According to a flexible nitrile rubber material and its preparation method provided by the patent document with the application number of CN201410377659.9, it can be known that the material comprises the following components in parts by weight: nitrile rubber 100, pyrophyllite 15-80, silane Coupling agent 0.5~3, zinc oxide 0.5~5, magnesium oxide 0.5~5, antioxidant 4020RD0.5~1, antioxidant 402040100.5~1, stearic acid 1~2, accelerator DPTT0.5~1, accelerator BZ0.5~1, vulcanizing agent 1~3. The flexible nitrile-butadiene rubber material may also contain one or both of anti-fatigue agents and dioctyl phthala...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08K5/11B29B7/74
CPCC08L9/02B29B7/74C08L2205/025C08K5/11Y02T10/86
Inventor 卢天骥郭力卜庆伟
Owner SHENYANG RUBBER RES & DESIGN INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products