High temperature separating material for preventing cinder and steel from staining to cinder ladle

A high-temperature, slag-stained technology, applied in the directions of mold composition, coating, casting and molding equipment, etc., can solve the problems of consuming manpower and material resources, easy to stick slag and steel, affecting the time rhythm of steel, etc., to achieve high turnover rate and construction performance. Good, the effect of high automatic slag turnover rate in the slag tank

Inactive Publication Date: 2006-04-05
武汉钢实星源工业总公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most of the ordinary high-temperature separation materials (also known as high-temperature coatings) used in slag tanks by domestic metallurgical iron and steel enterprises are prone to sticking to slag and steel.
When the slag tank is overturned, the slag and steel slag are often not poured out smoothly, and people are forced to use mechanical methods or oxygen melting and cutting methods to remove the residual steel, which consumes a lot of manpower and material resources, and directly affects the steel production process. time rhythm

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1: A kind of high-temperature separation material that prevents slag tank from staining slag and steel, consists of 45kg dolomite, 36kg bentonite, 22.5kg clay, 1.5kg sodium tripolyphosphate, 2kg carboxymethyl cellulose, 1.8kg graphite, and 200kg Water is prepared by uniform mixing.

Embodiment 2

[0018] Embodiment 2: A kind of high-temperature separating material that prevents slag tank from staining slag and steel, by 40kg dolomite, 30kg bentonite, 23kg clay, 2kg sodium tripolyphosphate, 2kg carboxymethyl cellulose, 3kg graphite, and 140kg water, through Prepared by mixing evenly.

Embodiment 3

[0019] Embodiment 3: A kind of high-temperature separating material that prevents slag tank from staining slag and steel, consists of 35kg dolomite, 35kg bentonite, 20kg clay, 1.8kg sodium tripolyphosphate, 1.5kg carboxymethyl cellulose, 0.8kg graphite, and 150kg Water is prepared by uniform mixing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention makes public a kind of high temperature separating material which can prevent dregs from adhering the dregs pot. The material includes 30~50 units of dolomite, 30~45 units of bentonite, 18~28 units of clay, 1.0~2.5 units of trimer sodium phosphate, 0.5~3.0 units of carboxymethyl cellulose and 135~220 units of water in proportion of weight. All water-fast particles' size should not lesser than 180 eyes. And about 0.5~5 units of black lead can be joined in the material. The material has good property of high temperature, dregs proof, and anti-strip. It can prevent the pot from being dregs adhered effectively, so it can make sure turning dregs automatically and high velocity of the pot. Adhering degree of the material is moderate, and no deposition and delamination in 72 hours. The material has good working performance.

Description

technical field [0001] The invention relates to the protection technology of a slag tank container for storing hot slag and residual steel in the metal smelting process, in particular to a high-temperature separation material for preventing the slag tank from sticking to slag and steel. Background technique [0002] When iron and steel enterprises produce various metal products, they will inevitably produce various high-temperature furnace slags and steel slags. For example, 8-10% slag can be produced in the oxygen converter smelting process. Usually, these molten steel slags are poured into the slag tank and then transported to the slag yard to be turned out for processing. The slag pot is actually an intermediate transition metal container. In order to reduce damage to the slag tank, ensure safety, speed up turnover, and stabilize production, a layer of high-temperature-resistant separation material must be coated on the inner wall of the slag ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D41/02B22C3/00C04B35/03C04B35/66
Inventor 杨焕祥陈静吴永法曹芳
Owner 武汉钢实星源工业总公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products