Environmentally friendly track rubber, and its production method and track construction method using same

A construction method and runway technology, applied in the field of plastic runway construction and polyurethane runway adhesive, can solve the problems of unenvironmental plastic runway materials, social anxiety, people's health harm, etc., and achieve easy transportation and construction, complete polymerization reaction, and construction. good effect

Active Publication Date: 2006-08-16
深圳市奥顺达体育有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The current plastic track mainly has the following problems: (1) Since the raw materials contain an excessive amount of volatile TDI, and it usually takes about 2-3 days to cure after construction, there will be more free TDI during or after construction. Volatile release of TDI into the environment
(3) At present, solvents such as toluene and xylene are used to varying degrees in the construction process of plastic runways, which will also cause pollution to the environment
[0005] Sports is for health, but the current non-environmental protection of plastic track materials has hidden dangers of harming people's health, so it has caused great anxiety in all walks of life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environmentally friendly track rubber, and its production method and track construction method using same
  • Environmentally friendly track rubber, and its production method and track construction method using same
  • Environmentally friendly track rubber, and its production method and track construction method using same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] The environment-friendly runway rubber of the present embodiment is produced from the raw materials of following parts by weight:

[0057]Polyether diol 400, polyether triol 60, TDI40, PAPI60, filler 100, and additives made of the following raw materials in parts by weight: modifier 60, ester plasticizer 100, oil softener 100 , Phosphoric acid pH regulator 5, UV absorber (light stabilizer) 2, aging agent 1.5.

[0058] Its production method refers to figure 1 As shown, it consists of the following production process:

[0059] (1) Polyether diol and polyether triol are heated to 110°C for dehydration;

[0060] (5) Mix the above-mentioned polyether polyol after dehydration with TDI and PAPI according to the above ratio and heat it to 80°C to polymerize it into a prepolymer, control the polymerization time to 2 hours, and add a phosphoric acid pH value regulator during the polymerization The pH value of the adjustment reaction is 6.5-7.5, preferably 7;

[0061] (6) Mix ...

Embodiment 2

[0071] The environment-friendly runway rubber of the present embodiment is produced from the raw materials of following parts by weight:

[0072] Polyether diol 500, polyether triol 50, TDI50, PAPI100, pH regulator 10, filler 120, and additives consisting of the following raw materials: bentonite modifier 50, ester plasticizer 150, Oil softener 80, light stabilizer 3, aging agent 1 part, and part of wetting agent.

[0073] Its production method refers to figure 1 As shown, it consists of the following production process:

[0074] (1) heating polyether diol and polyether triol to 120°C for dehydration;

[0075] (2) The above-mentioned polyether polyol after dehydration is mixed with TDI and PAPI according to the amount of the above-mentioned raw materials and heated to 75°C to polymerize it into a prepolymer. The polymerization time is controlled to be 2 hours, and the pH value is adjusted by adding a pH regulator. neutral;

[0076] (3) Mix the filler and additives with the...

Embodiment 3

[0086] The environment-friendly runway rubber of the present embodiment is produced from the raw materials of following parts by weight:

[0087] Polyether diol 450, polyether triol 55, TDI45, PAPI90, bentonite modifier 55, BINT (phthalate) ester plasticizer 130, paraffin oil softener 90, pH regulator 7. Light stabilizer 2.5, inorganic filler 110 parts.

[0088] Its production method refers to figure 1 As shown, it consists of the following production process:

[0089] (1) heating polyether diol and polyether triol to 115°C for dehydration;

[0090] (5) The above-mentioned polyether polyol after dehydration is mixed with TDI and PAPI according to the above ratio and heated to 80°C to polymerize it into a prepolymer. The polymerization time is controlled to be 2 hours, and a pH regulator is added during the reaction to adjust its pH value;

[0091] (6) Mix the filler and additives with the prepolymer, and then vacuumize to -0.09MPa, so that the bubbles in the mixed solution...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention publishes a kind of environmental plastic raceway. It is composed by polyether diatomic alcohol, polyether triatomic alcohol, TDI, PAPI, filling, ph chain cutting agent and others accessory ingredient. The invention also publishes the manufacturing methods. The process contains polyalcohol water after polyether, prepolymerization, adding filling and accessory ingredient, filtering and packaging. The construction contains cleaning up the base, lay down bottom, laying down frade lamella, spinkling colloidal particle, coating surface glue and marking out. The invention, environmental plastic raceway, has many advantages, such as innocuity, convenient manufacture, transport and construction, and good physics capability.

Description

technical field [0001] The invention relates to a material for laying a plastic track, specifically a polyurethane track glue; the invention also relates to a production method of the polyurethane track glue and a construction method of a plastic track using the track glue. Background technique [0002] The known plastic runway, that is, the main component of the polyurethane runway is polyurethane glue, which adopts first and second components. Component A is a prepolymer polymerized by excess isocyanate and polyether polyol, and Component B is composed of chain extender (or crosslinking agent or curing agent), filler, and auxiliary agent. Some types of agents also require a catalyst. In order to improve the physical and mechanical properties of the runway, the additives used are mostly one or more of plasticizers, stabilizers, aging agents, light stabilizers, modifiers, wetting agents, etc. During construction, the components A and B are mixed on site, and the prepolymer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/10C09D175/08E01C13/06
Inventor 罗植春
Owner 深圳市奥顺达体育有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More