Copper welding paste for automatic brazing and its preparing method

A brazing paste and brazing technology, which is applied in the direction of mixing methods, welding equipment, chemical instruments and methods, etc., can solve the problems of increasing wettability, easy drying, low boiling point, etc., achieve good fluidity, and increase surface bonding force , to ensure the effect of the apparent status quo

Inactive Publication Date: 2007-02-07
GUANGZHOU RES INST OF NON FERROUS METALS
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent CN1029407C discloses a copper-based solder paste and a welding method for copper ornaments. Although the patent CN1029407C and the product of this patent invention are all composed of copper solder, copper-based solder and organic paste, both The copper brazing flux, copper-based brazing filler metal and organic paste are obviously different in composition and preparation process. The brazing flux mentioned in patent CN1029407C is traditional FB102 and FB103, which have moisture absorption; in terms of brazing filler metal, this patent adds Trace elements increase wettability, corrosion resistance, etc. In terms of paste formation, the paste mentioned in patent CN1029407C has a low boiling point and is easy to dry, which is not suitable for automatic feeding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0050] A kind of preparation method of above-mentioned copper solder paste, at first respectively make solder, brazing flux and paste body, its respective preparation steps are as follows:

[0051] a. Brazing material:

[0052] (1) According to the composition of the solder;

[0053] (2) Smelting under vacuum conditions;

[0054] (3) Refining and purification;

[0055] (4) Ultrasonic inert airflow pulverizes the molten metal flow into droplets;

[0056] (5) The liquid droplets are solidified and cooled under a protective atmosphere;

[0057] (6) Powder particle size classification;

[0058] (7) vacuum treatment;

[0059] (8) Intermediate products.

[0060] b. Flux:

[0061] Quickly condense the molten flux and grind at a high speed to prepare -160 mesh flux.

[0062] c, into a paste:

[0063] Select low, medium and high molecular weight polyisobutylene mixtures and organic solvents, non-ionic

[0064] Surfactant and additives are mixed and heated to 80-150°C and fully ...

Embodiment approach

[0068] The further principle of the present invention and technical scheme and embodiment are as follows:

[0069] (1) Solder

[0070] Brazing material is the main component of solder paste, which has a key influence on the brazing process and welding strength. The solder involved in the present invention uses Cu as the matrix, adds appropriate amount of alloy elements and adopts an original powder making process, so that the solder powder has the characteristics of fine structure, uniform composition, smooth and spherical surface of powder particles, etc. The defects of brazing filler metal, such as high weld brittleness, low strength, poor air tightness and poor electroplating performance due to the existence of P, are greatly improved, and the mechanical properties and brazing process performance of the brazing filler metal are well improved.

[0071] The brazing filler metal used in this solder paste is prepared by vacuum smelting ultrasonic airflow atomization powder mak...

Embodiment 1

[0090] The components in the solder of Example 1 are: P: 5.5%, Sn: 6%, Ni: 0.5%, B and a small amount of rare earth elements, and the balance of Cu. In the flux after melting, B: 13.5%, K: 30.2%, F: 45.6%, O: balance. Polyisobutylene mixed in organic paste (7.75%): 15.6%, C 6 -C 15 : 82.3%, Surfactant: 1.2%, Additive: 0.9%. Brazing filler metal: brazing flux = 84.5: 15.5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The copper base welding paste for automatic brazing includes brazing material, brazing agent and paste forming material. The brazing material has Cu as main material and added alloy elements P, Sn, Ni, B, Ti, In and RE; the brazing agent consists of chemically synthesized intermediate polyboride M, potassium fluoroborate N and flux Q; and the paste forming material consists of mixture of polyisobutylene in different molecular weight and organic solvent. The copper base welding paste has good flowability, wetability and gap-filling performance, etc. and is suitable for industrial production.

Description

technical field [0001] The invention relates to a copper soldering paste for automatic brazing, in particular to a composition of the copper soldering paste-copper-phosphorous-tin-based solder, copper flux, components for forming a paste and a preparation method thereof. Background technique [0002] With the advancement of brazing science and technology and the miniaturization, diversification and complexity of the shape of brazing workpieces, the brazing processing industry has gradually replaced backward manual production with highly efficient automated production lines. The brazing operation process is to manually dip the wire-shaped, strip-shaped or sheet-shaped solder with flux, and then fix the solder coated with flux to the part of the workpiece to be brazed, and then heat the workpiece to melt the solder. The welding of the workpiece has extremely low production efficiency, which is extremely disharmonious with the modern high-speed economic development. It will be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/30B23K35/365C22C1/02B01F3/18B01F3/20B01F23/70
Inventor 陈志祥杨凯珍曾燕刘宏江刘凤美黄齐博蔡志红蔡沛沛刘福平陈平周美霞黄云帅张碧波钟文晨
Owner GUANGZHOU RES INST OF NON FERROUS METALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com