Method for synthesizing phenyloxalate from dicthyl oxalate and phenol

A technology of diethyl oxalate and diphenyl oxalate, which is applied in the field of raw materials for the preparation of diphenyl carbonate, can solve problems such as difficult separation of products and catalysts, achieve the effect of saving separation processes and equipment, and reducing production costs

Active Publication Date: 2007-05-09
TIANJIN UNIV
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the synthesis of diphenyl oxalate by transesterification of dimethyl oxalate and phenol with a supported oxide catalyzes the shortcoming that the product and the catalyst are not easy to separate when using a homogeneous catalyst, the intermediate product methyl phenyl oxalate (MPO) generation, the selectivity of the product diphenyl oxalate is only about 20%, which needs to be improved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for synthesizing phenyloxalate from dicthyl oxalate and phenol
  • Method for synthesizing phenyloxalate from dicthyl oxalate and phenol
  • Method for synthesizing phenyloxalate from dicthyl oxalate and phenol

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The present invention takes diethyl oxalate and phenol as raw material preparation diphenyl oxalate technical method under the condition of heterogeneous catalytic reaction, carries out in the there-necked flask of 250 milliliters, heat-collecting type electromagnetic stirring heating, is furnished with thermometer, to display the temperature of the reaction system. The amount of chemically pure DEO is 0.1 mole, the amount of chemically pure phenol is 0.5 mole, and the supported metal oxide catalyst SnO 2 / SiO 2 The consumption amount of is 1.8 grams, adds under normal pressure, wherein the load of metal tin is 1% (mass, the same below). Stir and heat up, the reaction temperature is controlled at 180.0±2°C, and the reaction time is 2 hours. The reaction equilibrium constant of reaction (1) is very little, for breaking the limitation of thermodynamic equilibrium, improve the transformation rate of raw material, the reflux condenser of the constant temperature circulati...

Embodiment 2-6

[0020] Changing the Supported Metal Oxide Catalyst SnO 2 / SiO 2 The load capacity of middle tin is respectively 2%, 4%, 8%, 12%, 16%, and under the situation that other conditions are identical with embodiment 1, carry out transesterification reaction, form embodiment 2-6 respectively, investigate Response results.

[0021] Example

Embodiment 7-14

[0023] The catalyst is changed to TiO 2 / SiO 2 Series of catalysts, supported metal oxide catalyst TiO 2 / SiO 2 The loaded amount of titanium in the middle is respectively 1%, 2%, 4%, 6%, 8%, 10%, 12%, 14%, 16%, under the completely identical situation of other conditions and embodiment 1, carry out ester Exchange reaction, form embodiment 7-14 respectively, examine reaction result.

[0024] Example

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a method for catalytically synthesizing phenyloxalate by utilizing diethyl acetate and phenol as raw material. The mole ratio of diethyl acetaet and phenol is 1:20-20:1, its reaction time is 1-8 hr, reaction temperature is 160-240 deg.C and autogeneous reaction pressure is 0-1.0 MPa. Under the action of load metal oxide catalyst the above-mentioned raw material are undergone the process of ester-interchange reaction so as to obtain the invented phenyloxalate.

Description

technical field [0001] The present invention relates to a kind of processing method that is used to prepare the raw material of diphenyl carbonate (DPC), specifically, relate to be catalyzer with supporting metal oxide, pass diethyl oxalate (DEO) and phenolic ester under heterogeneous condition Exchange reaction, catalyze the method for synthesizing diphenyl oxalate (DPO). Background technique [0002] The preparation of diphenyl oxalate from diethyl oxalate and phenol is a key technology for the preparation of diphenyl carbonate from diethyl oxalate and phenol. The reaction steps experienced by this key technology are as follows: [0003] [0004] About the synthesis of diphenyl oxalate by transesterification of oxalate and phenol, the preparation process of diphenyl oxalate and then decarbonylation of diphenyl carbonate began to appear in the 1990s, but it developed rapidly. Japan's Ube company has been committed to this aspect Research, and applied for many patents, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07C69/36C07C67/03
Inventor 马新宾王胜平
Owner TIANJIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com