Quick soluble dispersive emulsoid powder and its producing method

A manufacturing method and technology of latex powder, which are applied in the field of instant dispersing latex powder and its manufacturing, can solve problems such as inability to store, difficult to guarantee quality, and incapability of mass production in factories, and achieve easy transportation, stable quality, and packaging. easy effect

Inactive Publication Date: 2003-11-26
韩金顺
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, this method of using polymer emulsion to mix cement has many defects. It can only be prepared and used immediately, cannot be mass-produced in a factory, cannot be stored and is not conducive to environmental protection and long-distance transportation, and polymer cement materials are prepared on site. There is also a lack of scientific monitoring methods, and its quality is difficult to be guaranteed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] ① Purchase and weigh the following raw materials:

[0028] EVA emulsion 35kg,

[0029] PAA emulsion 30kg,

[0030] EDTA 1kg,

[0031] Cellulose ether 15kg,

[0032] Silicone emulsion 3kg,

[0033] Magnesium silicate 9kg,

[0034] Dolomite powder 7kg,

[0035] Triethanolamine 0.0008kg,

[0036] Add the two polymer emulsions of EVA emulsion and PAA emulsion into the reaction kettle, start the mixer, add 42kg of cellulose ether, EDTA, silicone emulsion and water in turn under stirring, raise the temperature to 95°C, and keep it warm at this temperature for 2.5 hours, the intermediate dispersion was obtained,

[0037] Turn on the hot air stove to keep the atomizing dryer at a hot air temperature of 265°C to atomize and dry the intermediate dispersion to obtain rubber powder. The exhaust temperature of the induced draft fan should be ≤90°C, otherwise the activity of the rubber powder will decrease.

[0038] The atomized and dried rubber powder is sent to the refriger...

Embodiment 2

[0041] ① Purchase and weigh the following raw materials:

[0042] EVA emulsion 20kg,

[0043] PAA emulsion 40kg,

[0044] EDTA 1.5kg,

[0045] Polyvinyl alcohol 12kg,

[0046] Silicone emulsion 0.5kg,

[0047] Magnesium silicate 16kg,

[0048] Dolomite powder 10kg, triethanolamine 0.0005kg,

[0049] Add the two polymer emulsions of EVA emulsion and PAA emulsion into the reaction kettle, start the mixer, add polyvinyl alcohol, EDTA, silicone emulsion and 20kg of water in turn under stirring, raise the temperature to 95°C, and keep it warm at this temperature After 2.5 hours, the intermediate dispersion was obtained,

[0050] Turn on the hot air stove to keep the atomizing dryer at a hot air temperature of 265°C to atomize and dry the intermediate dispersion to obtain rubber powder. The exhaust temperature of the induced draft fan should be ≤90°C, otherwise the activity of the rubber powder will decrease.

[0051] The atomized and dried rubber powder is sent to the refrig...

Embodiment 3

[0054] ① Purchase and weigh the following raw materials:

[0055] EVA emulsion 50kg,

[0056] PAA emulsion 20kg,

[0057] EDTA0.5kg,

[0058] Polyacrylamide 17.5kg,

[0059] Silicone emulsion 6kg,

[0060] Magnesium silicate 3kg,

[0061] Dolomite powder 3kg,

[0062] Triethanolamine 0.001kg,

[0063] Add the above two polymer emulsions of EVA emulsion and PAA emulsion into the reaction kettle, start the mixer, add polyacrylamide, EDTA, silicone emulsion and 55kg of water in turn under stirring, raise the temperature to 95°C, and keep it warm at this temperature After 2.5 hours, the intermediate dispersion was obtained,

[0064] Turn on the hot air stove to keep the atomizing dryer at a hot air temperature of 265°C to atomize and dry the intermediate dispersion to obtain rubber powder. The exhaust temperature of the induced draft fan should be ≤90°C, otherwise the activity of the rubber powder will decrease.

[0065] The atomized and dried rubber powder is sent to the re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The emulsoid powder is produced with EVA emulsion and PAA emulsion as main material and EDTA, cellulose ether or PVA or polyacrylamide, organic silica emuilsion, magnesium silicate, dolomite powder and triethanolamine as supplementary material, and through stirring, mixing, atomizing to dry, cooling and other steps. It may be dissolved in water and dispersed fast to form homogeneous emulsion. It may be mixed with several kinds of binding material, such as cement, hemihydratd gypsum, etc. to form mixture with specific performance and use, such as dry mixed polymer-cement mortar, rendering polymer-gypsum, etc. for building.

Description

technical field [0001] The present invention relates to a kind of instant dispersible latex powder and its manufacturing method, in particular to a kind of latex which can be quickly dissolved in water, can be quickly and evenly dispersed, and can also re-form latex with stock solution properties, and can improve cement properties powder and its production method. Background technique [0002] At present, the large-scale production and application of cement materials has a history of more than 100 years. It is as hard as stone and has high compressive strength. Convenient, but it has low extensibility, poor impermeability, and easy shrinkage and cracking. [0003] In order to improve the impermeability, frost resistance and heat resistance of cement materials, reduce or completely eliminate the cracking of cement materials, since some polymer emulsions came out one after another in the 1950s, scientists have mixed polymer emulsions into cement Succe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J3/05C08L23/08
Inventor 韩金顺
Owner 韩金顺
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More