Electrically conductive slag concrete

A technology of conductive concrete and steel slag, which is applied in the direction of conductive materials, conductive materials, conductors, etc., can solve the problems of inability to balance the requirements of mechanical and conductive properties, the difficulty of conductive materials in contact with each other, and low conductivity, and achieve excellent physical and mechanical properties. Raw materials Wide range of sources and good electrical conductivity

Inactive Publication Date: 2004-11-17
CHONGQING UNIV
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] (1). The performance requirements of both mechanics and conductivity cannot be taken into account
For the existing conductive concrete, when granular or powdery graphite powder, carbon powder, coke and steel chips are used as the conductive aggregate, due to its small aspect ratio, when the dosage is small, the conductive materials are difficult to contact each other , can not form a good conductive network, so its conductivity is poor; in order to improve the conductivity, when increasing the amount of conductive aggregate, on the one hand, due to the low strength of carbon black, coke, etc., on the other hand, due to the conductive aggregate The strong water absorption will increase the water demand (water-cement ratio) when concrete is mixed, so that the strength of concrete will be greatly reduced, and it is difficult to meet the needs of civil engineering for mechanical strength.
If carbon fiber is used as conductive aggregate, although a low dosage can form a conductive network, but due to the small contact surface of carbon fiber, its electrical conductivity is low, and it is necessary to increase the dosage of carbon fiber to improve its conductivity.
Excessive carbon fiber content will cause the fibers to agglomerate and form bundles during stirring, making it difficult to disperse; it is easy to introduce a large number of air bubbles during molding, which will reduce the strength of concrete
When steel fiber is used as conductive aggregate, due to its thicker diameter, it is difficult to form an overlapping conductive network. When the content of steel fiber is low, the conductivity is poor; but when the content of steel fiber is high, its workability is low. Poor, it is difficult to construct with conventional methods
Therefore, at present, various conductive concretes cannot better take into account the requirements of both mechanical and electrical properties.
[0005] (2). The cost is generally higher

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] mix ratio

Embodiment 2

[0021] mix ratio

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A steel slag conductive concrete comprising silicate cement, steel slag and water, the weight percentage is, comprising silicate cement 10-60, steel slag 20-80, water 8-25. The invention can be widely applied to the fields of industrial antistatic, electric appliances ground work, electromagnetic interference screening and reinforced bar cathode protection.

Description

technical field [0001] The invention belongs to the technical field of concrete, and particularly relates to the technology of conductive concrete materials. Background technique [0002] Concrete is the most widely used building material in civil engineering. Ordinary concrete is a poor conductor of electricity. By mixing a certain amount of conductive components into ordinary concrete, its conductivity can be improved, thereby becoming a conductor with certain electrical conductivity. [0003] Conductive concrete mainly relies on the mutual contact of the conductive phase materials in the concrete to conduct electricity. Therefore, the application of conductive materials with various electrical properties and different particle sizes, lengths, shapes, gradations and dosages is the main way to change the conductive properties of concrete. technical measures. At present, the conductive components used to make conductive concrete at home and abroad mainly include graphite p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B18/14C04B28/04H01B1/00
CPCY02W30/91
Inventor 唐祖全钱觉时王智李长太
Owner CHONGQING UNIV
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More