Anti-corrosive paint of epoxy resin based on aqueous bitumen, and preparation method

A technology based on epoxy resin and anti-corrosion coatings, applied in epoxy resin coatings, anti-corrosion coatings, asphalt coatings, etc., can solve the problems of low hardness, low corrosion resistance, and low softening point of petroleum asphalt coatings, and achieve good economy Benefits and application prospects, less equipment investment, and the effect of reducing construction procedures

Inactive Publication Date: 2006-04-19
NORTHWEST NORMAL UNIVERSITY
View PDF0 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, petroleum asphalt coatings have disadvantages such as low hardness, low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-corrosive paint of epoxy resin based on aqueous bitumen, and preparation method
  • Anti-corrosive paint of epoxy resin based on aqueous bitumen, and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Described asphalt-based epoxy resin anticorrosion coating is made up of the raw material of following parts by weight:

[0037] 1) 40 parts of modified asphalt emulsion;

[0038] 2) 45 parts of epoxy resin emulsion;

[0039] 3) 33 parts of curing agent emulsion;

[0040] 4) 20 parts of filler;

[0041] 5) 3 parts of auxiliary agent;

[0042] 6) 8 parts of water;

[0043] 50% epoxy resin is solidly contained in the epoxy resin emulsion; 50% organic amine is solidly contained in the described curing agent emulsion, and the organic amine is triethanolamine; the filler is precipitated barium sulfate; the auxiliary The agent is polycarboxylate sodium salt type dispersant SN-5040;

[0044] The preparation method of a kind of water-based asphalt base epoxy resin anticorrosion coating of the present invention is as follows:

[0045] 1. First, prepare modified asphalt emulsion: the raw materials in the following parts by weight: 55 parts of base asphalt, 2 parts of styrene...

Embodiment 2

[0051] Described asphalt-based epoxy resin anticorrosion coating is made up of the raw material of following parts by weight:

[0052] 1) 41 parts of modified asphalt emulsion;

[0053] 2) 46 parts of epoxy resin emulsion;

[0054] 3) 34 parts of curing agent emulsion;

[0055] 4) 21 parts of filler;

[0056] 5) 4 parts of auxiliary agent;

[0057] 6) 9 parts of water;

[0058] 50% epoxy resin is solidly contained in the epoxy resin emulsion; 50% organic amine is solidly contained in the curing agent emulsion, and the organic amine is condensate of phenol, formaldehyde and diethylenetriamine; the filler It is calcium carbonate; the auxiliary agent is polycarboxylate sodium salt type dispersant DP-270;

[0059] The preparation method of a kind of water-based asphalt base epoxy resin anticorrosion coating of the present invention is as follows:

[0060] 1. First, prepare modified asphalt emulsion: the raw materials in the following parts by weight: 56 parts of base asphalt, ...

Embodiment 3

[0066] Described asphalt-based epoxy resin anticorrosion coating is made up of the raw material of following parts by weight:

[0067] 1) 42 parts of modified asphalt emulsion;

[0068] 2) 47 parts of epoxy resin emulsion;

[0069] 3) 35 parts of curing agent emulsion;

[0070] 4) 22 parts of filler;

[0071] 5) 5 parts of auxiliary agent;

[0072] 6) 10 parts of water;

[0073] Solid-containing 50% epoxy resin in the epoxy resin emulsion; Solid-containing 50% organic amine in the described curing agent emulsion, and described organic amine is 2,4,6 three (dimethylaminomethyl) Phenol; the filler is calcined kaolin; the auxiliary agent is polycarboxylate sodium salt type dispersant FS-2006;

[0074] The preparation method of a kind of water-based asphalt base epoxy resin anticorrosion coating of the present invention is as follows:

[0075] 1. First, prepare modified asphalt emulsion: the raw materials in the following parts by weight: 57 parts of base asphalt, 4 parts of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A kind of anticorrosion asphalt-based epoxy resin water paint is proportionally prepared from modified asphalt emulsion, epoxy resin emulsion, solidifying agent emulsion, filler, assistant and water. Its advantages are high hardness, resistance to corrosion and abrasion, adhesion and softening point, and low pollution.

Description

technical field [0001] The invention relates to an anti-corrosion paint and a preparation method thereof, in particular to a water-based asphalt-based epoxy resin anti-corrosion paint and a preparation method thereof. Background technique [0002] In recent years, as various countries in the world have higher and higher requirements for emission restrictions on organic volatile compounds, the coatings industry has begun to develop in the direction of high solid content, powder coatings, water-based coatings, and light-curing coatings. To some extent, the amount of volatile organic compounds has become a criterion for evaluating whether a coating is an environmentally friendly coating. Water replaces toxic and harmful organic solvents. It has the advantages of non-toxicity, flame retardancy, no pollution to the environment, and energy saving. It is gradually replacing traditional solvent-based coatings and represents the development direction of coatings. [0003] Petroleum ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00C09D5/08C09D195/00
Inventor 王云普刘东杰张继王有朋
Owner NORTHWEST NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap