Biomass-base and waterproof wooden adhesive without formaldehyde and its production
A wood adhesive and biomass technology, applied in the direction of lignocellulosic material adhesives, adhesive types, etc., can solve the problems of high price, high price and thin profit of wood adhesives, and achieve a wide range of biomass sources and superior water resistance. , the effect of good practical performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example
[0031] Example 1:
[0032] Weigh 50 parts of corn stalks, add 30 parts of xylitol, 20 parts of propylene carbonate, liquefy for 55 minutes at 195°C and 1.5 atm pressure after removing impurities and crushing pretreatment, and then add 20 parts after colloid milling. Parts of tartaric acid and 20 parts of phthalic anhydride, heat to melt, stir evenly. After cooling, add 1 part of iron stearate and mix well. A new type of wood adhesive can be obtained.
[0033] Conditions of Use
[0034] Wood moisture content / %
Example
[0035] Example 2:
[0036] Weigh 100 parts of yellow-aged rice, after pretreatment, add 30 parts of xylitol, 20 parts of propylene carbonate, liquefy at 180℃ and 1.0atm pressure for 35min, after colloid milling, add 20 parts of tartaric acid And 20 parts of phthalic anhydride, heat to melt, stir evenly. After cooling, add 0.8 parts of magnesium stearate and mix well. A new type of wood adhesive can be obtained.
[0037] Conditions of Use
Example
[0038] Example 3:
[0039] Weigh 60 parts of waste paper, after pretreatment of impurity removal and pulverization, add 40 parts of xylitol, 20 parts of propylene carbonate, liquefy for 55 minutes at 190℃ and 1.2atm pressure, and then add 20 parts after colloid milling. Parts of tartaric acid and 20 parts of phthalic anhydride, heat to melt, stir evenly. After cooling, add 0.8 parts of iron stearate and mix well. A new type of wood adhesive can be obtained.
[0040] Conditions of Use
[0041] Glue amount (double-sided)
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap