A resistive, polymer technology, used in instruments, scientific instruments, analytical materials, etc., can solve the problems of performance that cannot meet the needs of market segments, narrow test range, poor stability, etc., to achieve excellent anti-pollution performance, good electricity Aging performance and mechanical aging performance, the effect of excellent water resistance

Inactive Publication Date: 2006-06-14
北京龙邦科技发展有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In recent years, with the wide application of humidity measurement and control technology in industrial and civil fields, the performance of domestic humidity sensors, especially the performance of resistive humidity sensors, has made great progress, but their performance cannot meet the needs of market segments
The reason is that the traditional conventional humidity sensor has poor long-term stability, narrow test range, large hysteresis, low linearity, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing composite thick film sensor of high molecular resistance type
  • Method for preparing composite thick film sensor of high molecular resistance type
  • Method for preparing composite thick film sensor of high molecular resistance type

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] 1. Embodiment

[0013] 1. Clean the dense ceramic sheet 1 of 6mm×5mm×0.5mm in acetone solution for 10min with ultrasonic waves, filter out the ceramic sheet, air-dry it at 50°C, and dry it at 120°C for 0.5hr, and then screen the ceramic sheet with a spacing of 0.5mm, symmetrical porous graphite electrode 2 with a size of 4.5mm×2mm, screen-print 2mm×1mm gold paste on the lower part of the ceramic sheet, then dry at 140°C for 0.5hr, and then transfer it to a box furnace at a temperature of 900°C±50°C Next sintering.

[0014] 1.1 Fabrication of porous graphite electrodes

[0015] Ultrasonic cleaning of 7mm×5mm×0.5mm dense ceramic sheet in acetone solution for 10min, filter out the ceramic sheet, air-dry at 50°C, and dry at 120°C for 0.5hr, then screen-print the ceramic sheet with a spacing of 0.5mm, the size It is a symmetric porous graphite electrode of 4.5mm×2mm, and a gold paste of 2mm×1mm is screen-printed on the lower part of the ceramic sheet, then dried at 140°C f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The invention supplies a preparation method for macromolecule resistance thermal detection compound heavy film sensor. The features of the invention are: it has dense ceramic substrate, symmetry silk-screen rectangle porous graphite pole on one side of densifying ceramics, silk-screen gold paste on the terminal of the pole, soldering pins after metallization, distribution droplets response type humidity sense media, heating and concentrating to net polymer and complete physical entanglement and nail rivet with porous electrode. The positive effects of the invention are: (1) improving resistivity against water, electrical ageing, and mechanism aging resistance of the component;(2) supplying both physical entanglement and nail rivet point of network polymer, as well as proper space to contain pollutant; (3) the humidity sense media adopting environment protection solvent, and adopting high precision point glue machine, technique of mass production is simple and convenient; (4) component having high linearity, low wet stagnant, wide range, and suitable sensitivity.

Description

technical field [0001] The invention relates to a method for preparing a humidity sensor, in particular to a method for preparing a high-molecule resistive compound thick-film humidity sensor with wide range, low hysteresis, high linearity and small drift. Background technique [0002] In recent years, with the wide application of humidity measurement and control technology in industrial and civil fields, the performance of domestic humidity sensors, especially the performance of resistive humidity sensors, has made great progress, but their performance cannot meet the needs of market segments. The reasons are that traditional conventional humidity sensors have poor long-term stability, narrow test range, large hysteresis, and low linearity. Contents of the invention [0003] The purpose of the present invention is to provide a method for preparing a polymer resistive composite thick-film sensor. The humidity sensor prepared by the method has the characteristics of wide ra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G01N27/12G01N27/00H05K3/12
Inventor 刘积奎
Owner 北京龙邦科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap