Trielement ethyl propylric rubber waterproofing coiled material and production process thereof

A technology of EPDM rubber and waterproof membrane, which is applied in the direction of chemical instruments and methods, and other chemical processes, can solve the problems of affecting the vulcanization process time, poor formula matching, and slow vulcanization speed, so as to increase the appearance quality, Effect of increasing specific surface area and improving performance

Inactive Publication Date: 2006-06-28
何霖
View PDF1 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Moreover, the material cost of EPDM waterproof membrane produced by the current process is high, the formula is not well matched, it is easy to

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Embodiment 1: EPDM waterproof roll material, the raw material proportion of waterproof roll material is:

[0034] EPDM EP35 or 4045 80;

[0035] carbon black 30;

[0036] light calcium 50;

[0037] ZnO3;

[0038] Stearic acid 0.8;

[0039] rhine wax 1;

[0040] Antiaging agent RD 1;

[0041] Antiaging agent 4020 1;

[0042] Accelerator M 1;

[0043] Accelerator TE 1;

[0044] Accelerator TT 0.8;

[0045] Accelerator PZ 0.8;

[0046] paraffin oil 20;

[0047] S (insoluble) 1.5;

[0048] RX-80 1

[0049] The production method of EPDM waterproof membrane, the steps of the production method are as follows:

[0050] (1) Coordination: ingredients according to the above ratio;

[0051] (2) Mixing: pressure: 0.4Mpa, temperature 100°C, time 12min, the order of adding raw materials is EP35, and then adding ZnO, stearic acid, antioxidant RD, antioxidant 4020, Rhine after 1.5min Wax, accelerator M, TE, TT, PZ after 1.5min, then add carbon black, light calcium, add pa...

Embodiment 2

[0057] Embodiment 2: EPDM waterproof coiled material, the raw material ratio of waterproof coiled material is:

[0058] EPDM 4045 120;

[0059] carbon black 50;

[0060] light calcium 80;

[0061] ZnO8;

[0062] Stearic acid 1;

[0063] Rhine Wax 2;

[0064] Antiaging agent RD 2;

[0065] Antiaging agent 4020 2

[0066] Accelerator M 1.5;

[0067] Accelerator TE 2;

[0068] Accelerator TT 1.5;

[0069] Accelerator PZ 1.2;

[0070] paraffin oil 25;

[0071] S (insoluble) 2.5;

[0072] RX-80 3

[0073] The production method of EPDM waterproof membrane, the steps of the production method are as follows:

[0074] (1) Coordination: ingredients according to the above ratio;

[0075] (2) Mixing: pressure: 0.5Mpa, temperature 110°C, time 12min, the order of adding raw materials is EPDM 4045, and then adding ZnO, stearic acid, antioxidant RD, antioxidant 4020, Rhine after 1.5min Wax, accelerator M, TE, TT, PZ after 1.5min, then add carbon black, light calcium, add paraff...

Embodiment 3

[0081] Embodiment 3: EPDM waterproof roll material, the raw material ratio of waterproof roll material is:

[0082] EPDM EP35 100;

[0083] carbon black 50;

[0084] light calcium 80;

[0085] ZnO5;

[0086] Stearic acid 0.9;

[0087] Rhine wax 1.5;

[0088] Antiaging agent RD 1.5;

[0089] Antiaging agent 4020 1.5

[0090] Accelerator M 1;

[0091] Accelerator TE 1;

[0092] Accelerator TT 0.8;

[0093] Accelerator PZ 1;

[0094] paraffin oil 23;

[0095] S (insoluble) 2;

[0096] RX-80 2

[0097] The production method of EPDM waterproof membrane, the steps of the production method are as follows:

[0098] (1) Coordination: ingredients according to the above ratio;

[0099] (2) Mixing: pressure: 0.5Mpa, temperature 100°C, time 12min, the order of adding raw materials is EP35, and then adding ZnO, stearic acid, antioxidant RD, antioxidant 4020, Rhine after 1.5min Wax, accelerator M, TE, TT, PZ after 1.5min, then add carbon black, light calcium, add paraffin oil af...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses tri-ethylene-propylene rubber water proof coiled material that uses tri-ethylene-propylene rubber EP35 or 4045, carbon, fine particle calcium carbonate, ZnO, stearic acid, Rhine wax, anti-aging agent, accelerating agent, vulcanizing agent as raw material. The advantage of the invention is that it is water proof, damp proof, mould proof, pressure proof, acid, alkali, and salt resistant, strong adhesive force, good extension, and strong ageing resistance.

Description

technical field [0001] The invention relates to a waterproof coiled material and a production method thereof, in particular to an EPDM waterproof coiled material and a production method thereof. technical background [0002] At present, the production method of rubber waterproof membrane generally adopts the traditional one-stage vulcanization method of rubber drum vulcanization or pressure tank vulcanization. One-stage vulcanization makes the product press flat, no pattern on the surface, and the specific surface area of ​​the bonding surface is small. Moreover, the material cost of the EPDM waterproof membrane produced by the current process is high, the formula is not well matched, it is easy to bloom, which affects the bonding, and the vulcanization speed is slow during the processing, which affects the vulcanization process time. Contents of the invention [0003] The purpose of the present invention is to overcome the shortcomings of the prior art, to provide an EPDM...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/16C08K5/09C09K3/18
Inventor 何霖
Owner 何霖
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap