Method for preparing stainless steel lining paper

A technology of stainless steel and lining paper, which is applied in the pulp beating method, pulp beating/refining method, paper, etc., can solve the problems of low product qualification rate and insufficient tear resistance index, and achieve the advantages of folding resistance and good performance , the effect of stable quality

Inactive Publication Date: 2007-03-28
樊运民
View PDF0 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem of low product qualification rate caused by the insufficient strength, smoothness and tear resistance index of the backing paper in the high-speed production process of stainless steel plates, the purpose of the present invention is to provide a high-strength, tear-resistant Cracked, ultra-smooth, high-cleaning, low-weight stainless steel backing paper with high temperature resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The production of high-strength, tear-resistant, ultra-smooth, high-clean high-temperature resistant stainless steel liner paper includes the selection of raw wood pulp, pulping, sand removal, washing, deflaking, refining, pulping, papermaking and other processes.

[0019] Proportioning is carried out according to the ratio of white kraft softwood pulp: white kraft hardwood pulp=75%: 25% (percentage by weight), requiring wood pulp whiteness more than 90%, beating concentration 3.5~4.5%, beating degree 58~ 63°SR, wet weight 5-7g, average fiber length 1.2-2.0mm.

[0020] Use 330 disc grinding basalt stone grinding discs for refining. After refining, add whitening agent and whitening agent VBL to the slurry tank, add cationic starch 1.2%, paraffin emulsion 10%, and AKD 0.8% in the slurry tank; Add 1.2% of emulsified silicone oil to the pulping box; add 0.3% of CPAM and 0.35% of PAE to the head box (the above percentages are the same as the ratio of the added wood pulp).

...

Embodiment 2

[0023] Production of high-strength, tear-resistant, ultra-smooth, high-clean high-temperature resistant stainless steel liner paper, including the selection of raw material pulp, pulping, sand removal, washing, deflaking, refining, pulping, papermaking and other processes.

[0024] Proportioning is carried out in the ratio of white sulphate softwood pulp: white sulphite hardwood pulp=75%: 25% (percentage by weight), and the wood pulp requires the same embodiment one.

[0025] Use 330 disc grinding basalt stone grinding discs for refining. After refining, add whitening agent and whitening agent VBL to the slurry tank, add 5% paraffin emulsion, 1.0% cationic starch, and 1.0% AKD to the slurry tank; Add 2.0% of emulsified silicone oil to the pulping box; add 0.3% of CPAM and 0.75% of PAE to the high-level box (the above percentages are the same as the proportion of wood pulp added). Other conditions are the same as in Example 1.

Embodiment 3

[0027] Proportioning is carried out according to the ratio of white kraft softwood pulp: white soda hardwood pulp=75%: 25% (percentage by weight), and the requirements of wood pulp are the same as in Example 1.

[0028] Use 330 disc grinding basalt stone grinding discs for refining. After refining, add whitening agent and whitening agent VBL to the slurry tank, add 20% paraffin emulsion, 0.5% cationic starch, and 0.8% AKD to the slurry tank; Add 1.0% of emulsified silicone oil to the pulping box; add 0.5% of CPAM and 0.25% of PAE to the high-level box (the above percentages are the same as the proportion of wood pulp added). Other conditions are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
strengthaaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing method for a stainless steel lining paper that includes the following steps: adopting white wood pulp as raw material, and white sulfate softwood pulp: white hardwood pulp =70-80wt%: 30-20wt%; adopting short fiber shiny beating method, and 330 disc mill basalt stone lapping to take jordaning; using chemical auxiliary agent that adding 5-20wt% olefin emulsion, 0.5-1.0wt% positive ion starch, 0.5-1.0wt% AKD, 1.0-2.0wt% silicone emulsion, 0.3-0.5wt% CPAM, and 0.25-0.75wt% PAE. It has the advantages of high intension, laceration endurable, super smooth, clean and high temperature endurable. It could fit different manufacture technology requests of stainless steel.

Description

technical field [0001] The invention relates to a special paper, in particular to a preparation method of stainless steel backing paper. Background technique [0002] Stainless steel lining paper is a new type of special industrial paper that is gradually matched with the domestic and foreign stainless steel industry to protect the quality of stainless steel plate products with the vigorous development of the stainless steel industry in recent years. According to the different stainless steel production process, stainless steel lining paper can be divided into: high temperature resistant stainless steel lining paper suitable for hot-pressed stainless steel plate and ordinary stainless steel lining paper suitable for cold-rolled stainless steel plate. In July 2006, it was found through a science and technology search that there are currently domestic manufacturers that provide stainless steel lining paper, but most of the stainless steel lining paper provided are imported fro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/10D21H11/00D21D1/02D21D1/30D21H17/60D21H17/29D21H17/17D21H21/16D21H17/52D21H21/18
Inventor 樊运民樊军民冯海全阎伟青
Owner 樊运民
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com