A technology for vacuum coating and plastic parts, applied in vacuum evaporation coating, surface pretreatment, metal material coating process, etc., can solve the problems of restricting the safe use of plastic parts, semi-mirror effect that the film layer does not have a metallic texture, etc. The effect of achieving good insulation effect

Inactive Publication Date: 2007-06-27
MITAC PRECISION TECH CO LTD SHUNDE DISTRICT FOSHAN CITY
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional coating methods include: (1) Coating aluminum, nickel or chromium metal films on transparent plastic parts by vacuum sputtering to obtain plastic parts with metallic luster and semi-mirror effect, but because the film is a metal film However, it is conductive, which limits the safe use of plastic parts
(2) The electron gun vacu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plastic surface vacuum plating process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] After cleaning the surface of the PC plastic part 1 by ultrasonic cleaning, spray a layer of UV primer 2 for vacuum sputtering, control the thickness of the paint layer to 5-20 μm, and then cure it under ultraviolet light; use zirconium metal as the target material for vacuum Sputtering, the sputtering process conditions are: coating power 9Kw, Ar flow rate 140Sccm, N 2 The flow rate is 65Sccm, and the coating time is 5 seconds. A zirconium nitride coating 3 with a film thickness of 10-30 nm was obtained. The coating had a metallic color and a semi-mirror texture, and its resistance value was determined to be infinite.

Embodiment 2

[0023] After cleaning the surface of the PC plastic part 1 by ultrasonic cleaning, spray a layer of UV primer 2 for vacuum sputtering, control the thickness of the paint layer to 5-20 μm, and then cure it under ultraviolet light; use zirconium metal as the target material for vacuum Sputtering, the sputtering process conditions are: coating power 9Kw, Ar flow rate 140Sccm, N 2 The flow rate is 150Sccm, and the coating time is 5 seconds. A zirconium nitride coating 3 with a film thickness of 10-30 nm was obtained. The coating had a metallic color and a semi-mirror texture, and its resistance value was determined to be infinite.

Embodiment 3

[0025] After cleaning the surface of the PC plastic part 1 by ultrasonic cleaning, a layer of primer layer 2 with a thickness of 5-20 μm is coated on the surface by immersion plating, and then cured by ultraviolet light; zirconium metal is used as the target material. Vacuum sputtering, the sputtering process conditions are: coating power 9Kw, Ar flow rate 140Sccm, N 2 The flow rate is 70Sccm, and the coating time is 5 seconds. A zirconium nitride coating 3 with a film thickness of 40-70 nm was obtained. The coating had a metallic color and a semi-mirror texture, and its resistance value was determined to be infinite.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The vacuum plating process for plastic surface includes the following steps: ultrasonic cleaning of the plastic workpiece surface, applying one 5-20 microns thick primer onto the surface of the plastic workpiece, ultraviolet ray curing, and vacuum sputtering with metal Zr target material in Ar flow rate of 140 Sccm, plating power of 2-9 Kw and N2 flow rate of 50 Sccm for 3-5 sec to obtain zirconium nitride film of 10-70 nm thickness. The plated film on the surface of plastic part has semi-mirror texture and excellent insulating effect.

Description

technical field [0001] The invention relates to a coating process on the surface of plastic parts, more specifically, to a vacuum coating process on the surface of plastic parts. Background technique [0002] Plastic parts are used more and more widely in daily life. In order to beautify the surface appearance of plastic parts, the surface of plastic parts is usually coated with a film, especially a film with a semi-mirror glossy texture. The traditional coating methods are: (1) Coating aluminum, nickel or chromium metal films on transparent plastic parts by vacuum sputtering to obtain plastic parts with metallic luster and semi-mirror effect, but because the film is a metal film However, it is conductive, which limits the safe use of plastic parts. (2) The electron gun vacuum evaporation coating method is used to coat the surface of plastic parts with SiO 2 / TiO 2 The transparent film with high and low refractive index composed of the same composition can form a semi-tra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C14/02C23C14/12C23C14/54B08B3/12B05B3/00B05B5/00B05D3/06
Inventor 林壮坤
Owner MITAC PRECISION TECH CO LTD SHUNDE DISTRICT FOSHAN CITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap