High Strength Thin-Gauge Steel Sheet Excellent in Elongation and Hole Expandability and Method of Production of Same

a thin-gauge steel sheet, high-quality technology, applied in the direction of manufacturing tools, furnaces, heat treatment equipment, etc., can solve the problems of obstructing the precision of parts, and sometimes demanding complicated shapes, etc., to achieve high strength, and excellent elongation and hole expandability

Inactive Publication Date: 2008-01-03
NIPPON STEEL CORP
View PDF2 Cites 60 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0007] The present invention has as its object to solve the problems of the prior art as explained above and realize high strength thin-gauge steel sheet with excellent elongation and hole expandability and a method of production for the same on an industrial scale. Specifically, it has as its object to realize high strength thin-gauge steel sheet exhibiting the above performance by a tensile strength of 500 MPa or more and a method of production of the same on an industrial scale.

Problems solved by technology

From the aesthetic design and chassis design requirements, complicated shapes are sometimes demanded.
On the other hand, the phenomenon of springback or other elastic recovery after working a part occurs more readily the higher the strength of the steel sheet and obstructs securing the precision of the part.
In this way, these working methods require stretch flangeability, hole expandability, bendability, and other local formability of the steel sheet, but conventional high strength steel sheet do not have sufficient performance, cracks and other defects occur, and stable working of the products is not possible.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0080] Comparing Experiment No. [8] with the same operating conditions as the past as a comparative example and Experiment Nos. [2], [6], and [9] of invention examples, it is learned that the invention examples exhibit better values of the hole expansion rate and elongation.

[0081] Further, as a comparison of sheets with the same level of tensile strength and generally the same ingredients, but satisfying formula (A) and not satisfying it, among the steel types B and C, E and F, and K and L, the C, F, and L satisfying formula (A) exhibited larger ferrite area fractions and better elongation.

example 2

[0082] Further changing and comparing the tempering conditions, the drop in strength was large and the elongation also conversely dropped. The drop in elongation is believed due to the formation of pearlite. Experiment Nos. [1], [2], [5], [6], and [9] of the invention examples all exhibited good results.

TABLE 3(Example 1)Experiment No. [8] (Comparative Examples)Underlined, bold-face, italics indicate rejectionHoleTemperedSteelTSexpansionFerriteResidual γmartensiteOthertype(MPa)EL (%)TS × ELratearea (%)vol. (%)area (%)compositionClassA59830.9184784181.83.6≦0.1MainlyComp. Ex.B60230.2181804084.12.9≦0.1martensiteComp. Ex.C61332.3198004084.33.6≦0.1Comp. Ex.D66529.2194183873.02.7≦0.1Comp. Ex.E70327.1190513862.13.7≦0.1Comp. Ex.F72228.6206493866.82.7≦0.1Comp. Ex.G79924.7197353859.33.3≦0.1Comp. Ex.H81123.6191403758.62.9≦0.1Comp. Ex.I83621.8182253457.13.1≦0.1Comp. Ex.J87520.7181133352.32.7≦0.1Comp. Ex.K93119.6182483337.74≦0.1Comp. Ex.L95620.5195983244.33.4≦0.1Comp. Ex.M98418.8184993035.53.6...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
elongationaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The present invention provides high strength thin-gauge steel sheet with excellent elongation and hole expandability having a tensile strength of 500 MPa or more and a method of production of high strength thin-gauge steel sheet with excellent elongation and hole expandability enabling production of this on an industrial scale, that is, high strength thin-gauge steel sheet comprised of, by mass %, C: 0.03 to 0.25%, Si: 0.4 to 2.0%, Mn: 0.8 to 3.1%, P≦0.02%, S≦0.02%, Al≦2.0%, N≦0.01%, and a balance of Fe and unavoidable impurities and having a microstructure comprised of ferrite with an area fraction of 10 to 85% and residual austenite with a volume fraction of 1 to 10%, an area fraction of 10% to 60% of tempered martensite, and a balance of bainite.

Description

TECHNICAL FIELD [0001] The present invention relates to high strength thin-gauge steel sheet excellent in elongation and hole expandability and a method of production thereof. BACKGROUND ART [0002] Recently, due to the need for reducing the weight of automobiles and improving collision safety, high strength steel sheet excellent in formability into chassis frame members and reinforcement members, seat frame parts, and the like are being strongly demanded. From the aesthetic design and chassis design requirements, complicated shapes are sometimes demanded. High strength steel sheet having superior working performance is therefore necessary. [0003] On the other hand, due to the increasingly higher strength of steel sheet, the working method is frequently shifting from the conventional drawing using wrinkle elimination to simple stamping and bending. Especially, when the bending ridge is an arc or other curve, stretch flanging where the end face of the steel sheet is elongated is somet...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(United States)
IPC IPC(8): C22C38/06C21D9/46
CPCB21B3/02C22C38/14C21D8/041C21D8/0426C21D8/0436C21D8/0473C21D9/46C21D2211/001C21D2211/002C21D2211/005C21D2211/008C22C38/02C22C38/04C22C38/06C22C38/12C22C38/001C22C38/002C21D1/25C22C38/005C22C38/18C22C38/22C22C38/26C22C38/28C22C38/32C22C38/38
Inventor NONAKA, TOSHIKITANIGUCHI, HIROKAZUGOTO, KOICHI
Owner NIPPON STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap