Solder using for impregnated barium-tungsten cathode and method for using same

A barium tungsten cathode and solder technology, applied in welding/cutting media/materials, welding media, manufacturing tools, etc., can solve the problems of Mo tube cracking, low cathode yield and falling off, and achieve long and stable service life. Good performance, strong welding effect

Inactive Publication Date: 2008-11-12
HUADONG PHOTOELECTRIC TECHN INST OF ANHUI PROVINCE
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Laser beam welding was also used, but due to improper use of shielding gas, the Mo cylinder was cracked, brittle, and even fell off.
Whether it is electron beam welding or laser beam welding, it is necessary to maintain a close fit between the welded mother bodies, otherwise the Mo cylinder will first melt and shrink, and cannot be welded firmly.
And after welding, it is difficult to ensure that the W base and the Mo cylinder are tightly bonded everywhere, although the surface of the two is well welded
Due to the above reasons, the cathode yield is low due to improper welding. At the same time, the cathode can not adapt to complex weather and terrain, and the service life is not long.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solder using for impregnated barium-tungsten cathode and method for using same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The cathode body prepared by the present invention has a diameter of 3.6mm and a thickness of 2mm.

[0024] Process 1:

[0025] 1) Put the palladium powder, molybdenum powder and ruthenium powder into a 500°C hydrogen furnace for annealing to thoroughly purify and enhance their plasticity.

[0026] 2) take by weighing 1 gram of palladium powder, 20 gram of molybdenum powder, 10 gram of ruthenium powder, (all converted into 100%, the purity of palladium powder is 95.4%, the purity of molybdenum powder is 95%, the purity of ruthenium powder is 96.2% ), the three materials are ground to 300 mesh, mixed and pressed;

[0027] 3) Spread the solder on the junction of the non-emitting surface W base and the molybdenum cylinder, with a thickness of 2-3 mm. Put the coated cathode into the hydrogen furnace, raise the temperature to 1900°C and keep it for 120 seconds, and then lower it to 1000°C. Keep warm for 3 minutes and cool to room temperature;

[0028] 4) Place the cathode...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a barium tungsten cathode solder. Wherein, it is formed by palladium, molybdenum and cobalt at 1:5-70:5-60, while their purities are 95-100%. And its application comprises annealing, grinding, compressing, welding and salt emerging. The invention has low steam pressure, long service life, and stable cathode.

Description

technical field [0001] The invention relates to a cathode brazing material on an electron tube device and a method for using the same, in particular to an impregnated barium-tungsten cathode and a method for using the same. Background technique [0002] As an electron source, barium tungsten cathodes are widely used in various microwave devices. In its production process, the welding between the W-based sponge and the molybdenum cylinder (Mo cylinder) supporting it is an essential process to complete the cathode as a whole. Electron beam welding is very expensive and uneconomical. Laser beam welding was also used, but due to improper use of shielding gas, the mold cylinder was cracked, brittle, and even fell off. Whether electron beam welding or laser beam welding is used, it is necessary to maintain a close fit between the welded mother bodies, otherwise the Mo cylinder will first melt and shrink, and cannot be welded firmly. And after welding, it is difficult to ensure ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/32B22F3/02B23K1/00
Inventor 吴华夏方卫沈旭东张红卫
Owner HUADONG PHOTOELECTRIC TECHN INST OF ANHUI PROVINCE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com