Feather pulling wax for poultry and prepartion method

Abstract

This invention involves a process for preparing a defeathering wax for domesticated poultry. Raw materials for this defeathering wax are: 10-90 wt. % of wax, 1-30 wt. % of viscosity increaser, 1-70 wt. % plasticizer and 0-5 wt. % of disperser. The process for preparing the defeathering wax comprises the steps of: melting the wax and then adding the viscosity increaser, the plasticizer and the disperser in it; raising the temperature to 110-160 deg.C and stirring the said mixture with a rotational speed of 5-10 rpm; raising the rational speed to 30-60 rpm after complete melting of the mixture, and stirring it for another 30-60 min; releasing the material and moulding. Compared with the present processes, this invention has such advantages as nontoxic, nonodorous, safe and thermally stable.

Description

technical field

[0001] The invention relates to a compound and a preparation method thereof, in particular to a poultry depilation wax and a preparation method thereof. Background technique

[0002] China is a big country for raising and consuming poultry, especially waterfowl such as ducks and geese. It is a very time-consuming and labor-intensive process to pull out the fine fluff on the skin of poultry during slaughtering and processing. The purely manual method cannot meet the requirements of industrialized large-scale processing products. Now most processing manufacturers use rosin or special wax containing rosin to complete the depilation process, which greatly improves production efficiency.

[0003] Compared with rosin plucking, special wax plucking containing rosin has the advantages of low energy consumption, no pollution to the environment, high yield, reusable use, and compliance with national health standards.

[0004] China's "Petroleum Refining and Chemical I...

Examples

Embodiment 1

[0021] Heat and melt 52 parts of 62# fully refined paraffin wax and 24 parts of glyceryl tristearate, then add 0.7 parts of Span 60, 2 parts of cellulose acetate, 9 parts of polypropylene wax and 15 parts of propylene-isobutylene copolymer. High temperature to 150°C, stirring at a speed of 30 rpm for about 60 minutes, discharging and forming the product.

Embodiment 2

[0023] Heat and melt 11 parts of 85# microcrystalline wax, 14 parts of 70# Fischer-Tropsch synthetic wax and 40 parts of 54# paraffin wax, then add 1.2 parts of calcium dodecylbenzenesulfonate, 7 parts of copolyester resin, 12 parts of polyethylene Wax and 15 parts of ethylene-vinyl acetate copolymer are heated up to 140°C, first stirred at a speed lower than 10 rpm, and after they are completely melted, stirred at a speed of 50 rpm for 15 minutes and then discharged to form a product.

Embodiment 3

[0025] Heat and melt 5 parts of 70# Fischer-Tropsch synthetic wax and 60 parts of 58# paraffin wax, then add 5 parts of polybutene, 8 parts of terpene resin, 16 parts of cracked polyethylene and 12 parts of refined oxidized microcrystalline wax, and heat up to 120 ℃, stirred at a speed of 60 rpm for 15 minutes, and then discharged to form a product.

technical field

[0001] The invention relates to a compound and a preparation method thereof, in particular to a poultry depilation wax and a preparation method thereof. Background technique

[0002] China is a big country for raising and consuming poultry, especially waterfowl such as ducks and geese. It is a very time-consuming and labor-intensive process to pull out the fine fluff on the skin of poultry during slaughtering and processing. The purely manual method cannot meet the requirements of industrialized large-scale processing products. Now most processing manufacturers use rosin or special wax containing rosin to complete the depilation process, which greatly improves production efficiency.

[0003] Compared with rosin plucking, special wax plucking containing rosin has the advantages of low energy consumption, no pollution to the environment, high yield, reusable use, and compliance with national health standards.

[0004] China's "Petroleum Refining and Chemical I...

Examples

Embodiment 1

[0021] Heat and melt 52 parts of 62# fully refined paraffin wax and 24 parts of glyceryl tristearate, then add 0.7 parts of Span 60, 2 parts of cellulose acetate, 9 parts of polypropylene wax and 15 parts of propylene-isobutylene copolymer. High temperature to 150°C, stirring at a speed of 30 rpm for about 60 minutes, discharging and forming the product.

Embodiment 2

[0023] Heat and melt 11 parts of 85# microcrystalline wax, 14 parts of 70# Fischer-Tropsch synthetic wax and 40 parts of 54# paraffin wax, then add 1.2 parts of calcium dodecylbenzenesulfonate, 7 parts of copolyester resin, 12 parts of polyethylene Wax and 15 parts of ethylene-vinyl acetate copolymer are heated up to 140°C, first stirred at a speed lower than 10 rpm, and after they are completely melted, stirred at a speed of 50 rpm for 15 minutes and then discharged to form a product.

Embodiment 3

[0025] Heat and melt 5 parts of 70# Fischer-Tropsch synthetic wax and 60 parts of 58# paraffin wax, then add 5 parts of polybutene, 8 parts of terpene resin, 16 parts of cracked polyethylene and 12 parts of refined oxidized microcrystalline wax, and heat up to 120 ℃, stirred at a speed of 60 rpm for 15 minutes, and then discharged to form a product.