Method for increasing medical embedded stainless steel tube inner surface quality

A stainless steel and inner surface technology, applied in the field of materials, can solve the problems that the inner surface of the pipe cannot be processed, and the stainless steel pipe is not suitable for medical implantation, etc., and achieve the effect of good polishing effect, good corrosion resistance, and high surface roughness

Inactive Publication Date: 2009-07-22
CHANGSHU MICROTUBE TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, such a method cannot deal with the inner surface of the pipe, and is not suitable for the inner surface of medical implant stainless steel pipes with small diameter features.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A medical implant stainless steel pipe (vascular stent pipe) with an outer diameter of 1.575mm, a wall thickness of 0.127mm, and a component grade of 316L is processed through the following steps:

[0014] (1) Immerse the self-made treatment solution in the treatment tank. The treatment solution is obtained by mixing ordinary stainless steel pickling solution and 1% by volume of nano-alumina particles.

[0015] (2) Put the pipe into a treatment tank and heat to 50°C.

[0016] (3) Use a water pump to inject the treatment hydraulic pressure into the pipe and make it circulate. The treatment time is 0.5 minutes.

[0017] (4) After taking it out, rinse it with running water.

[0018] The inner surface of the pipe obtained through the above steps is bright, the surface roughness is less than 5um, and the polishing thickness is about 1um, which is basically close to the mirror effect.

Embodiment 2

[0020] A medical implant stainless steel pipe (vascular stent pipe) with an outer diameter of 1.575mm, a wall thickness of 0.127mm, and a component grade of 316L is processed through the following steps:

[0021] (1) Immerse the self-made treatment solution in the treatment tank. The treatment liquid is obtained by mixing ordinary stainless steel pickling liquid and 10% by volume of nano-alumina particles.

[0022] (2) Put the pipe into a treatment tank and heat to 80°C.

[0023] (3) Use a water pump to inject the treatment hydraulic pressure into the pipe and make it circulate. The treatment time is 30 minutes.

[0024] (4) After taking it out, rinse it with running water.

[0025] The inner surface of the pipe obtained through the above steps is very bright, the surface roughness is less than 0.5um, and the thickness is reduced by about 10um by polishing to achieve a perfect mirror effect.

Embodiment 3

[0027] A medical implant stainless steel pipe (vascular stent pipe) with an outer diameter of 1.575mm, a wall thickness of 0.127mm, and a component grade of 316L is processed through the following steps:

[0028] (1) Immerse the self-made treatment solution in the treatment tank. The treatment liquid is obtained by mixing ordinary stainless steel pickling liquid and 20% by volume of nano-alumina particles.

[0029] (2) Put the pipe into a treatment tank, and heat to 100°C.

[0030] (3) Use a water pump to inject the treatment hydraulic pressure into the pipe and make it circulate. The treatment time is 60 minutes.

[0031] (4) After taking it out, rinse it with running water.

[0032] The inner surface of the pipe obtained through the above steps is very bright, the surface roughness is less than 0.2um, and the thickness is reduced by about 50um by polishing to achieve a perfect mirror effect.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The process of treating medical implanted stainless steel pipe in high inner surface quality includes soaking medical implanted stainless steel pipe in mixed treating fluid comprising stainless steel pickling solution and nanometer alumina particle inside a treating trough, heating the treating fluid to 50-100 deg.c, pressing the treating fluid into the pipe and circulating with a water pump, treating for 0.5-60 min, and flushing the taken out pipe with flowing water. Compared with available technology, the present invention has the advantages of high polishing effect, excellent anticorrosive performance, wide application range and other features.

Description

technical field [0001] The invention relates to a method for improving surface quality in the field of materials, in particular to a method for improving the inner surface quality of medically implanted stainless steel pipes. Background technique [0002] Various types and specifications of stainless steel metal materials have been widely used in the medical field. For example, vascular stents for interventional therapy are made of fine stainless steel tubes, which are then manufactured by laser cutting and electrochemical polishing. However, at present, the stainless steel pipes produced by the general process have various defects or deficiencies such as dimensional accuracy and surface quality, especially micro-oxidation, small burrs, processing marks or wrinkles on the inner surface, and are not easy to handle, which restricts They are used in many implant medical fields such as interventional medicine. Therefore, it is of great significance to improve the surface quality...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23F3/06A61F2/82A61F2/91
Inventor 张小农
Owner CHANGSHU MICROTUBE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com