A resin composite and decorative board technology, applied in lamination devices, lamination, layered products, etc., can solve the problems of poor compatibility, high cost, and can not be widely used, and achieve good brightness, high flatness, excellent comprehensive performance effect

Inactive Publication Date: 2007-08-01

王依岳

0 Cites 3 Cited by

AI-Extracted Technical Summary

Problems solved by technology

Although the natural board has the characteristics of green environmental protection and easy processing, in actual use, it is greatly affected by the external environment, especially in a humid environment, it is easy to be deformed by moisture, and it is more likely to be damaged by insects; the metal board will not be deformed by moisture, be ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine

Abstract

The invention involves a resin composite decorative plate, it mainly consists of wood plate and resin coating the plate. Its characteristics are that it is prepared through the following method: daubing ceresin wax on the base seat and frame, wiping until dry; adding accelerator, color paste and curing agent into resin, stirring uniformly, pumping the foam fully; pouring the resin into frame on said base seat plate, laying and forming solidified resin layer; then pouring stirred materials on the solidified resin layer in frame, laying wood plate and curing; pouring stirred materials on the wood plate to making the gap between the wood plate and the frame is full of stirred materials and the a stirred materials layer is formed on the wood plate, laying and curing; then pouring the stirred materials on the solidified layer and covering transparent cladding paper, strickling and curing; putting it into oasthouse drying and demolding. The resin composite decorative plate is completely waterproof, and has high planeness, good brightness and no seams, the surface can beproduced for any pattern, it can be used in architectural and indoor and outdoor decorative areas as decorative sheet materials widely.

Application Domain

LaminationLamination apparatus +1

Technology Topic

Paper sheetCeresin +7

Examples

Experimental program(3)
Effect test(1)

Example Embodiment

[0023] Example 1

[0024] ①Apply paraffin wax evenly on the base plate and wipe it dry after 10 minutes;

[0025] ②Use slats around the base plate to frame a frame larger than 1mm of the wood board, and fix it on the base plate with calipers;

[0026] ③Apply paraffin wax evenly on the inner wall of the frame, dry it after 10 minutes, and set aside;

[0027] ④Pour 1 kg of resin into the mixing drum, then add 5ml of accelerator, add red color paste, and stir evenly, then add 6ml of curing agent, stir evenly to make a mixing material, and then vacuum for 3 minutes to add Exhausted bubbles

[0028] ⑤ Pour the mixing material into the frame on the base plate to a thickness of 0.5mm, and place it to form a cured resin layer;

[0029] ⑥ Pour the mixing material on the cured resin layer in the frame to a thickness of 0.5mm, and then put it on the wooden board and place it for curing;

[0030] ⑦Pour the mixing material on the board to fill the gap between the board and the frame and form a 0.5mm thick layer on the board, and place it to solidify;

[0031] ⑧ Pour the mixing material on the solidified layer, cover it with transparent coated paper, scrape it flat, and solidify;

[0032] ⑨ Put it in the drying room and warm it up from room temperature for 20 minutes to 60°C, place it at a constant temperature for 1 hour, then cool it down to room temperature for 30 minutes, and then demold the red resin composite decorative board.

Example Embodiment

[0033] Example 2

[0034] ①Apply paraffin wax evenly on the glass base plate and wipe it dry after 20 minutes;

[0035] ② Use metal slats to frame a frame larger than the wooden board 2mm around the glass base plate, and fix it on the glass base plate with calipers;

[0036] ③Apply paraffin wax evenly on the inner wall of the frame, dry it after 20 minutes, and set aside;

[0037] ④Pour 1 kg of unsaturated resin into the mixing drum, then add 20ml of cobalt isooctanoate, and add the green color paste, stir evenly, then add 20ml of solid oxide methyl ethyl copper, stir evenly to make a stirring material, and then vacuum for 5 minutes. Exhaust the bubbles in the mixing material;

[0038] ⑤ Pour the mixing material into the frame on the glass base plate to a thickness of 1.5mm, and place it to form a cured resin layer;

[0039] ⑥ Pour the mixing material on the cured resin layer in the frame to a thickness of 1mm, and then put it on the wooden board and place it for curing;

[0040] ⑦Pour the mixing material on the board to fill the gap between the board and the frame and form a 2mm thick layer on the board, and place it to solidify;

[0041] ⑧ Pour the mixing material on the solidified layer, cover it with plastic film paper, scrape it flat, and solidify;

[0042] ⑨ Put it in the drying room and raise it from room temperature for 20 minutes to 80°C, place it at a constant temperature for 1 hour, then cool it down to room temperature for 30 minutes, and then demold to obtain a green resin composite decorative board.

Example Embodiment

[0043] Example 3

[0044] ①Apply paraffin wax evenly on the metal base plate and wipe it dry after 15 minutes;

[0045] ② Use plastic slats to frame a frame larger than 1.5mm of the wooden board around the metal base plate, and fix it on the metal base plate with calipers;

[0046] ③Apply paraffin wax evenly on the inner wall of the frame, dry it after 15 minutes, and set aside;

[0047] ④Pour 1 kg of unsaturated resin into the mixing drum, then add 12ml of cobalt isooctanoate, and add yellow color paste, and stir evenly, then add 13ml of solid oxide methyl ethyl copper, stir evenly to make a stirring material, and then vacuum for 4 minutes. Exhaust the bubbles in the mixing material;

[0048] ⑤ Pour the mixing material into the frame on the metal base plate to a thickness of 1mm, and place it to form a cured resin layer;

[0049] ⑥ Pour the mixing material on the cured resin layer in the frame to a thickness of 0.7mm, and then put it on the wooden board and place it for curing;

[0050] ⑦Pour the mixing material on the board to fill the gap between the board and the frame and form a 1.5mm thick layer on the board, and place it to solidify;

[0051] ⑧ Pour the mixing material on the solidified layer, cover it with transparent pattern paper, scrape it, and solidify;

[0052] ⑨ Put it in the drying room and warm it up from room temperature for 20 minutes to 70°C, place it at a constant temperature for 1 hour, then cool it down to room temperature for 30 minutes, and then demold the yellow resin composite decorative board.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine

Login to view more

PUM

Description & Claims & Application Information

We can also present the details of the Description, Claims and Application information to help users get a comprehensive understanding of the technical details of the patent, such as background art, summary of invention, brief description of drawings, description of embodiments, and other original content. On the other hand, users can also determine the specific scope of protection of the technology through the list of claims; as well as understand the changes in the life cycle of the technology with the presentation of the patent timeline. Login to view more.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine

Login to view more

Classification and recommendation of technical efficacy words

Improve flatness
Good brightness

Composite resin ornamental board

A resin composite and decorative board technology, applied in lamination devices, lamination, layered products, etc., can solve the problems of poor compatibility, high cost, and can not be widely used, and achieve good brightness, high flatness, excellent comprehensive performance effect

AI-Extracted Technical Summary

Problems solved by technology

Abstract

Examples

Example Embodiment

Example Embodiment

Example Embodiment

PUM

Description & Claims & Application Information

Similar technology patents

Method for producing silicon carbide substrate and silicon carbide substrate

Efficient mechanical laying device for block-shaped turf

Method for fabricating semiconductor device and semiconductor device

Method for removing surface compressive stress of toughened glass through chemical ion exchange

Asphalt modifying additive containing carbon black obtained from thermal cracking of waste tire

Classification and recommendation of technical efficacy words

Display module

Cutting insert with curved cutting edge

Mask film plate and manufacturing method thereof

P-channel power MIS field effect transistor and switching circuit

Support structure and display device

X-ray illuminators with high flux and high flux density

Exposure control method for human face image acquisition system under near-infrared condition

Halogen-free low-smoke flame-retardant cable material and preparation method thereof

Preparation method of water-based floor paint and construction process of water-based floor paint

Double-color burnt-out sofa fabric technology