A positive active material and lithium battery technology, applied in electrode manufacturing, battery electrodes, circuits, etc., can solve the problems of complex process, unstable product performance, high cost, etc., and achieve high platform capacity, enhanced conductivity, and uniform grinding high effect

Inactive Publication Date: 2007-11-14
SHENZHEN B&K TECH
View PDF0 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a lithium battery positive electrode active material, a positive electrode dressing and a preparation method thereof. By using ternary materials, lithium cobalt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lithium cell anode active substance, anode dressing and its preparing method
  • Lithium cell anode active substance, anode dressing and its preparing method
  • Lithium cell anode active substance, anode dressing and its preparing method

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0039] Example 1

[0040] Using the ternary material: lithium cobalt oxide with a proportion of 5:5, the ball milling is carried out according to the following steps:

[0041] 1) Add the ternary material, lithium cobalt oxide and graphite conductive agent into the ball milling tank, and use the speed of 1000-1500r / min for ball milling, and the milling time is 4 hours. The diameters of the zirconium balls used in the ball milling are 3mm, 6.5mm, 10mm, 15mm, and 20mm respectively, and they are placed in the ball milling tank according to the number ratio of 2:3:3:4:4.

[0042] 2). After the first step is completed, let it stand for 30 minutes, add carbon black conductive agent into the ball milling tank, and then ball mill at 1000r / min for 2 hours. Let stand for 1 hour.

[0043] Chemical mixing process:

[0044] 1). The mixed materials are continuously and slowly added to the colloid, and the addition is completed within half an hour, followed by thick mixing for 2 hours, thick mixi...

Example Embodiment

[0047] Example 2

[0048] With a ternary material: lithium cobalt oxide ratio of 6:4, the ball milling is carried out in the following steps:

[0049] 1): Add the ternary material, lithium cobalt oxide and graphite conductive agent into the ball milling tank, and use the speed of 1000-1500r / min for ball milling. The milling time is 4 hours. The diameters of the zirconium balls used in the ball mill are 3mm, 6.5mm, 10mm, 15mm, and 20mm respectively, and they are placed in the ball mill tank at a ratio of 2:3:3:4:4.

[0050] 2): After the first step is completed, let it stand for 30 minutes, add carbon black conductive agent into the ball milling tank, and then ball mill at 1000r / min for 2 hours. Let stand for 1 hour.

[0051] Chemical mixing process:

[0052] 1): The mixed materials are continuously and slowly added to the colloid, and the addition is completed within half an hour, followed by thick mixing for 2 hours, thick mixing, and the mixer speed is 3600r / min.

[0053] 2): Adju...

Example Embodiment

[0055] Example 3

[0056] According to the ternary material: lithium cobalt oxide composition ratio of 7:3, follow the steps below:

[0057] 1). Add the ternary material, lithium cobalt oxide and graphite conductive agent into the ball milling tank, and use the rotation speed of 1000-1500r / min for ball milling, and the milling time is 4 hours. The diameters of the zirconium balls used in the ball mill are 3mm, 6.5mm, 10mm, 15mm, and 20mm respectively, and they are placed in the ball mill tank at a ratio of 2:3:3:4:4.

[0058] 2). After the first step is completed, let it stand for 30 minutes, add carbon black conductive agent into the ball mill tank, and then ball mill at 1000r / min for 2 hours. Let stand for 1 hour.

[0059] Chemical mixing process:

[0060] 1). The mixed materials are continuously and slowly added to the colloid, and the addition is completed within half an hour, followed by thick mixing for 2 hours, thick mixing, and the mixer speed is 3600r / min.

[0061] 2) Adj...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Viscosityaaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention is a lithium battery anode active matter, and anode dressing and the preparing method thereof. And the anode active matter comprises trinary material LiNixCoyMn1-x-yO2 and lithium cobaltate; the anode dressing comprises anode active matter, graphite conductive agent, charcoal black conductive agent, and adhesive; and the preparing method comprises: 1. ball-milling: a. ball-milling the trinary material, lithium cobaltate and graphite conductive agent in proportion; b. after a, adding the charcoal black conductive agent into ball-mill tank in proportion; and blending: a. taking the adhesive in proportion and blending with organic solvent, and when blending until no bubbles, stilling and serving; b. adding mixed material and other additives to colloid and blending thickly; and c. filtering for coating.

Description

technical field [0001] The invention relates to a method for making a positive electrode of a lithium battery, and mainly refers to a positive electrode active material of a lithium battery, a positive electrode dressing and a preparation method thereof. Background technique [0002] Lithium battery is a high-performance secondary battery, which has the advantages of high working voltage, high volume and energy density, long service life, low self-discharge rate, etc. It is widely used in various digital products, power tools and other fields. In recent years, the application range of lithium batteries has become more and more extensive, and the end-use products have different requirements for them. Therefore, the positive electrode materials used in lithium batteries have also changed from simple lithium cobalt oxide to physical or chemical methods of various positive electrode materials. Doping, including lithium manganese oxide and lithium cobalt oxide doping, nickel-cont...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/58H01M4/48H01M4/62H01M4/04H01M4/505H01M4/525
CPCY02E60/10
Inventor 阳海鹰江岩曹建华蓝俊方
Owner SHENZHEN B&K TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap