Method for appraising sphere nickel median voltage performance

A ball nickel and voltage technology, applied in the field of evaluating the median voltage performance of ball nickel, can solve problems such as long cycle, reduce production costs, reduce testing and inspection costs, and save manpower and material resources.

Inactive Publication Date: 2008-02-27
BYD CO LTD
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a method that can quickly and effectively evaluate the median voltage performance of sph

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for appraising sphere nickel median voltage performance
  • Method for appraising sphere nickel median voltage performance
  • Method for appraising sphere nickel median voltage performance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] This example is used to illustrate the method for evaluating the median voltage performance of spherical nickel provided by the present invention.

[0020] Instrument: D / MAX2200PC X-ray powder diffractometer produced by Rigaku Corporation;

[0021] Instrument configuration and test conditions: Copper X-ray source, wavelength λ=1.54056 angstroms, Cu / Kα1, Cu target power is 40 kV, 20 mA; graphite monochromator is used; goniometer scan rate is 4 degrees / minutes, the scanning range is 2θ=15°-65°, the scanning method is θ / 2θ linkage scanning; the scanning step is 0.02 degrees / step; the optical path divergence slit is 1°, the anti-scattering slit is 10mm, Change the slit to automatic adjustment of the instrument, and the receiving slit is 0.3mm;

[0022] Instrument data processing software: MDI-JADE (5.0);

[0023] Spherical nickel sample: cadmium-added spherical nickel sample (D03 cadmium-added type, Jiangmen Changyou Industrial Co., Ltd.), numbered A;

[0024] Specific s...

Embodiment 2-6

[0030] This group of examples 2-6 is used to illustrate the method for evaluating the median voltage performance of spherical nickel provided by the present invention.

[0031]Add cadmium spherical nickel sample B (SY-1 adds cadmium type, Xiamen Fangyuan Chemical Industry Co., Ltd.), C (D03 adds cadmium type, Jiangmen Changyou Industrial Co., Ltd.), D respectively according to the test method described in Example 1. (D03 cadmium-added type, Jiangmen Changyou Industrial Co., Ltd.), E (D03 cadmium-added type, Jiangmen Changyou Industrial Co., Ltd.) and F (SY-2 cadmium-added type, Xiamen Fangyuan Chemical Industry Co., Ltd.) XRD diffraction test , to obtain the I of the sample 101 / I 001 , and evaluate the electrochemical performance of the spherical nickel sample according to the method described in Example 1. Obtain the diffractogram of sample as shown in B, C, D, E, F in Fig. 1, measurement result is as shown in B, C, D, E, F in table 1, wherein, sample A, C, D, E Both are ...

Embodiment 7-12

[0036] This group of examples is used to prepare batteries.

[0037] Preparation of positive electrode sheet

[0038] Weigh 42.5 parts by weight of spherical nickel samples A, B, C, D, E, F and 10 parts by weight of conductive agent nickel powder, 3.5 parts by weight of improver CoO, and 1 part by weight of binder polytetrafluoroethylene , 20 parts by weight of water mixed and stirred evenly to prepare positive electrode slurry, respectively coated on the foamed nickel mesh with drainage fluid, dried and calendered at 150 ° C to grow 200 mm, 30 mm wide, and 0.75 mm thick positive electrode sheet Z1, Z2 , Z3, Z4, Z5, Z6, wherein the contents of the positive electrode active material in the positive electrode sheets Z1, Z2, Z3, Z4, Z5, Z6 are all 3.75 grams.

[0039] Preparation of negative electrode sheet

[0040] Weigh 40 parts by weight of CdO powder, 10 parts by weight of Cd powder, and 25 parts by weight of water, mix and stir evenly to prepare negative electrode slurry, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method to appraise the ball nickel median voltage performance of positive material in secondary nickel-hydrogen/nickel-cadmium battery. The method includes: it gets the parameter of ball nickel crystal and sets the parameter field of ball nickel crystal; comparing the ball nickel crystal parameter to the setting ball nickel crystal parameter, if the getting value is in the range of setting value, the median voltage can satisfy the battery. The ball nickel crystal parameter is the ratio of at least two different crystal surface diffraction maximums. The method in invention can determine if the ball nickel median voltage good or bad quickly, it is especially proper for appraising the ball nickel material of factory.

Description

technical field [0001] The invention relates to a method for evaluating the median voltage performance of spherical nickel, in particular to a method for evaluating the median voltage performance of spherical nickel used as the positive electrode material of a secondary nickel-hydrogen / nickel-cadmium battery. Background technique [0002] Spherical nickel (that is, spherical nickel hydroxide, usually with a β-crystal structure) is the main positive electrode active material used in secondary nickel-metal hydride / nickel-cadmium batteries, and its electrochemical performance directly determines or indirectly affects the electrochemical performance of the battery. Electrochemical properties such as specific capacity, cycle life, median voltage, fast charge and discharge capacity, self-discharge performance, and storage performance. [0003] For manufacturers of secondary NiMH / NiCd batteries, it is very important to accurately understand and correctly evaluate the median voltage...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01R31/36G01R31/00
Inventor 李永胜
Owner BYD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap