NiAl-Cr(Mo) biphase eutectic crystal intermetallic compound modified by Co

A technology of intermetallic compounds and eutectic metals, which is applied in the field of NiAl-Cr dual-phase eutectic intermetallic compounds, can solve the problems of little improvement in high-temperature strength and failure to meet the use requirements, and achieve the effect of improving high-temperature strength

Inactive Publication Date: 2008-03-26
BEIHANG UNIV
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the high-temperature strength of NiAl-Cr(Mo) dual-phase eutectic intermetallic compounds has not been greatly improved, and it still cannot meet the requirements of the new generation of gas turbine engines at 1150 °C. An effective approach to the comprehensive properties of NiAl intermetallic compounds

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • NiAl-Cr(Mo) biphase eutectic crystal intermetallic compound modified by Co
  • NiAl-Cr(Mo) biphase eutectic crystal intermetallic compound modified by Co
  • NiAl-Cr(Mo) biphase eutectic crystal intermetallic compound modified by Co

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Example 1: Preparation of 33Ni-25Al-30Cr-4Mo-8Co intermetallic compound

[0034] The ingredients are formulated according to the composition of 33Ni-25Al-30Cr-4Mo-8Co (atomic percentage), and the purity of the raw materials is 99.999%.

[0035] Use non-consumable vacuum electric arc furnace to melt 33Ni-25Al-30Cr-4Mo-8Co alloy ingot, and the vacuum degree is greater than 5×10 -3 Pa, smelting temperature 3000°C, smelting 4 times, the raw materials are smelted evenly.

[0036] The obtained intermetallic compound rod was kept at 1200° C. for 12 hours in a high-temperature heat treatment furnace, and then cooled to room temperature with the furnace.

[0037] A cylinder sample with a diameter of 6mm and a height of 9mm and a square cylinder with a diameter of 6mm×6mm×30mm were cut from the heat-treated 33Ni-25Al-30Cr-4Mo-8Co ingot by wire cutting method for mechanical property testing.

[0038] Accurate to 10 with Model 1111 -4 The mass M of the sample is measured by an ...

Embodiment 2

[0040] Example 2: Preparation of 33Ni-22Al-30Cr-4Mo-11Co Intermetallic Compound

[0041] The ingredients are formulated according to the composition of 33Ni-22Al-30Cr-4Mo-11Co (atomic percentage), and the purity of the raw materials is 99.999%.

[0042] Melting 33Ni-22Al-30Cr-4Mo-11Co alloy ingots in a non-consumable vacuum electric arc furnace with a vacuum degree of 5×10 -3 Pa, the melting temperature is 2700°C, smelting 6 times, and the raw materials are smelted evenly.

[0043] The obtained intermetallic compound rod was kept at 1200° C. for 12 hours in a high-temperature heat treatment furnace, and then cooled to room temperature with the furnace.

[0044] The mechanical property testing conditions of 33Ni-22Al-30Cr-4Mo-11Co intermetallic compound are the same as in Example 1, and its density is 6.70g / cm 3 ; See Figure 2, room temperature yield strength of 2200MPa, compression plasticity greater than 20%; 800 ° C yield strength of 620MPa, compression plasticity greate...

Embodiment 3

[0045] Example 3: Preparation of 33Ni-30Al-30Cr-4Mo-3Co intermetallic compound

[0046] The ingredients are 33Ni-30Al-30Cr-4Mo-3Co (atomic percentage), and the purity of the raw materials is 99.999%.

[0047] Melting 33Ni-30Al-30Cr-4Mo-3Co alloy ingots in a non-consumable vacuum electric arc furnace with a vacuum degree of 4×10 -3 Pa, smelting temperature 2800°C, smelting 3 times, the raw materials are smelted evenly.

[0048] The obtained intermetallic compound rod was kept at 1200° C. for 12 hours in a high-temperature heat treatment furnace, and then cooled to room temperature with the furnace.

[0049] The mechanical property testing conditions of 33Ni-30Al-30Cr-4Mo-3Co intermetallic compound are the same as in Example 1, and its density is 6.15g / cm 3 As shown in Figure 3, the yield strength at room temperature is 1900MPa, and the compressive plasticity is greater than 21%; the yield strength at 700°C is 1000MPa, and the compressive plasticity is greater than 60%; the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Compressive plasticityaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The present invention discloses one kind of Co modified two-phase eutectic intermetallic NiAl-Cr(Mo) compound comprising Ni in 33 at.%, Cr in 30 at.%, Mo in 4 at.%, Co in 1-16 at.% and Al for the rest. By means of lowering Al content in the two-phase eutectic intermetallic NiAl-Cr(Mo) alloy, and adding Co element with solid solution reinforcing effect to modify and introduce one third plastic phase, the Co modified two-phase eutectic intermetallic NiAl-Cr(Mo) compound has further raised high temperature strength and room temperature toughness and plasticity. The Co modified two-phase eutectic intermetallic NiAl-Cr(Mo) compound has yield strength at 1150 deg.c of 110-130 MPa and density of 6.02-7.06 g / cu cm.

Description

technical field [0001] The invention relates to a Co-modified NiAl-Cr(Mo) dual-phase eutectic intermetallic compound. Background technique [0002] At present, in the industrial fields of power, petrochemical, transportation, especially aviation and aerospace, the metal structural materials used above 600 °C are usually nickel-based, iron-based and cobalt-based superalloys. These materials have a higher density (generally at 8.0g / cm 3 Above), the components and equipment made are heavy. In order to reduce structural weight, improve efficiency, and reduce energy consumption, it is necessary to develop new high-temperature alloys with low density and high specific strength to meet the needs of future development in related industrial fields. What is more urgent is that currently the superalloys represented by Ni base and Co base are close to the limit temperature of their use due to the limitation of melting point. Even for the third-generation superalloy single crystal with...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C30/00C22C1/02
Inventor 徐惠彬孙跃军李世超汤林志张志刚刘先斌宫声凯
Owner BEIHANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com