Super-hydrophobic timber and preparation thereof

A super-hydrophobic, wood technology, applied in the direction of wood compression, wood layer products, wood processing appliances, etc., can solve the problems of difficult industrialization, expensive materials, etc., and achieve the effects of stable properties, good corrosion resistance, and simple operation technology.

Inactive Publication Date: 2008-08-06
成都新红鹰家具有限公司
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these existing methods either use expensive materials, or require special processing equipment or complex processes, making it difficult to industrialize

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The preparation method of superhydrophobic wood, preparation step comprises:

[0019] (1), put the log into the circular steel cylinder mould;

[0020] (2), weigh a certain amount of beeswax powder and add it to the circular steel cylinder mold, and submerge the wood, then raise the pressure in the circular steel cylinder mold to 50MPa on the press, and heat up to 80°C, and keep it warm for 0.5 hours , and then release the pressure to 0MPa, and take out the wood when the temperature is raised to 110°C;

[0021] (3), the taken-out wood is cooled to room temperature, and the beeswax on the surface is scraped off to obtain the superhydrophobic wood, the pores of the superhydrophobic wood are filled with beeswax. The contact angle between the superhydrophobic wood and water is between 150° and 170°, and the rolling angle of water droplets on the wood surface is less than 10°.

[0022] The circular steel cylinder mold is required to withstand the pressure of 1-50Mpa and is...

Embodiment 2

[0024] The preparation method of superhydrophobic wood, preparation step comprises:

[0025] (1), put the log into the circular steel cylinder mould;

[0026] (2), weigh a certain amount of beeswax powder and add it to the circular steel cylinder mold, and submerge the wood, then raise the pressure in the circular steel cylinder mold to 30MPa on the press, and raise the temperature to 100°C, and keep it warm for 10 hours , and then release the pressure to 0MPa, and take out the wood when the temperature is raised to 108°C;

[0027] (3), the taken-out wood is cooled to room temperature, and the beeswax on the surface is scraped off to obtain the superhydrophobic wood, the pores of the superhydrophobic wood are filled with beeswax. The contact angle between the superhydrophobic wood and water is between 150° and 170°, and the rolling angle of water droplets on the wood surface is less than 10°.

[0028] The circular steel cylinder mold is required to withstand the pressure of ...

Embodiment 3

[0030] The preparation method of superhydrophobic wood, preparation step comprises:

[0031] (1), put the solid wood board into the circular steel cylinder mould;

[0032] (2), weigh a certain amount of beeswax powder and add it to the circular steel cylinder mold, and submerge the wood, then raise the pressure in the circular steel cylinder mold to 1MPa on the press, and heat up to 90°C, and keep it warm for 20 hours , and then release the pressure to 0MPa, and take out the wood when the temperature is raised to 105°C;

[0033] (3), the taken-out wood is cooled to room temperature, and the beeswax on the surface is scraped off to obtain the superhydrophobic wood, the pores of the superhydrophobic wood are filled with beeswax. The contact angle between the superhydrophobic wood and water is between 150° and 170°, and the rolling angle of water droplets on the wood surface is less than 10°.

[0034] The circular steel cylinder mold is required to withstand the pressure of 1-5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a super-hydrophobic wood with the pores of a wood body filled with super-hydrophobic substances. The preparation steps comprise: (1) the wood is put into a die; (2) certain amount of super-hydrophobic substance powder is added into the die to submerge the wood; the pressure in the die is lifted to 1-50MPa on a press; the temperature rises to 80-100 DEG C and is maintained for 0.5-20h; then the pressure is lowered to 0MPa; the material is taken out when the temperature rises to 105-110 DEG C; (3) the taken-out wood is cooled to the room temperature and scraped the super-hydrophobic substance on the surface to derive the super-hydrophobic wood. The contact angle between the super-hydrophobic wood and the water is 150 degrees and the roll angle is less than 10 degrees. The layer is tasteless and nontoxic, thereby having a broad application prospect in the fields such as lossless transportation of liquid, self-cleaning, water and damp resistance, etc. The method for preparing super-hydrophobic wood provided by the invention has the advantages of simple operation technology, good controllability, low cost, no complicated chemical treatment, no expensive equipment and industrialization facilitating.

Description

technical field [0001] The invention relates to a superhydrophobic wood, and also relates to a preparation method of the superhydrophobic wood. Background technique [0002] Inspired by the lotus leaf effect, solid materials with superhydrophobic surfaces (the contact angle between the surface of the material and water is greater than 150°, and the water droplets have a small rolling angle on the surface) have attracted extensive interest. Due to the characteristics of waterproof, anti-fog, anti-oxidation and self-cleaning, superhydrophobic surfaces have broad application prospects in scientific research, industrial and agricultural production, and daily life. For example, it can be applied to building materials and exterior wall coatings with self-cleaning function, textiles with self-cleaning function, loss-free transportation of liquids, moisture-proof packaging materials, biomedical materials that inhibit blood coagulation and blood pollution, etc. [0003] It is well k...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27M1/08B27M1/02B32B21/04
Inventor 彭万喜吴义强卿彦
Owner 成都新红鹰家具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap