Method for preparing ultra-fine white carbon black and nano alumina by using kaolinite as raw material

A technology of nano-alumina and fine white carbon black, which is applied in the preparation of alumina/hydroxide, silicon oxide, etc., can solve the problem of low comprehensive utilization efficiency of kaolin, achieve high added value of products, good product indicators, and reduce corrosion and damaging effects

Inactive Publication Date: 2008-08-27
中国高岭土有限公司
View PDF1 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a method for preparing superfine white carbon black and nano-alumina with k

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0044] Example: A method for preparing ultrafine white carbon black and nano alumina using kaolin as a raw material, which consists of the following process steps in sequence:

[0045] (1) calcination

[0046] The kaolin is calcined at 610℃ to dehydrate the kaolin contained in the kaolin to produce metakaolinite. The reaction formula is: Al 2 O 3 ·2SiO 2 ·2H 2 O→Al 2 O 3 ·SiO 2 +H 2 O;

[0047] (2) Extraction

[0048] Add the calcined kaolin to the hydrochloric acid solution at 95°C, then add sodium hexametaphosphate with 0.95% of the kaolin mass, and stir it, so that the chemical component alumina contained in the metakaolinite reacts with the hydrochloric acid to generate trichloride Aluminum, its reaction formula is: Al 2 O 3 +6HCl=2AlCl 3 +3H 2 O, so that silica can be dissolved from metakaolinite into amorphous silica, most of the amorphous silica exists in a colloidal state; wherein the mass percentage concentration of the hydrochloric acid solution is 20%, and the alumina T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Disclosed is a process for preparing superfine silica and nano-alumina by utilizing kaolin as raw materials. In the method, the kaolin is calcined, lixiviated and filtered, filter liquor containing silicon dioxide and a filter cake containing aluminum trichloride are obtained, then, the filter liquor and the filter cake are removed by impurity and post-treated, and finally the final product of the powder of the nano-alumina and the powder of the superfine silica are obtained. The process can prepare the superfine silica and the nano-alumina simultaneously, thereby achieving the comprehensive application of the kaolin, and the prepared two products are fine in product index and high in added value of products.

Description

technical field [0001] The invention relates to a method for preparing superfine white carbon black and nano-alumina by using kaolin as a raw material, and belongs to the technical field of preparation, purification and crystal form control of inorganic materials. Background technique [0002] Kaolin is an important non-metallic mineral resource, and it is called the four major non-metallic minerals together with mica, quartz and calcium carbonate. Kaolin is mainly composed of kaolinite minerals (kaolinite, dickite, pearlite, halloysite, etc.) in the crystal form of micro flakes, tubes, and laminations less than 2 microns. The ideal chemical formula is Al 2 o 3 -2SiO2 2 -2H 2 O, whose chemical composition is mainly composed of a large amount of Al 2 o 3 , SiO 2 and a small amount of Fe 2 o 3 、TiO 2 and a small amount of K 2 O, Na 2 Composed of O, CaO and MgO, pure kaolin contains SiO 2 46.51%, Al 2 o 3 was 39.53%. [0003] For a long time, most of the developm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01B33/113C01F7/30
Inventor 冯杰李勇张忠飞吴铭敏周竹发陈丽昆何琴朱明秀
Owner 中国高岭土有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap