Drip glue encapsulation method of solar paster component

An encapsulation method and solar energy technology, which are applied to electrical components, semiconductor devices, circuits, etc., can solve the problems that do not involve the process flow of the glue board, and the control parameters are different in preparation methods. beautiful effect

Inactive Publication Date: 2008-09-03
JIAWEI SOLAR WUHAN
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent authorization number CN1825633A discloses the sealing process of solar photovoltaic cell panels, but it does not involve the comp

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] 1) Select the main components produced by Dongguan Liduo Electronic Materials Co., Ltd. as glue A of epoxy resin and glue B as a curing agent; take by weight at 2:1, at an ambient temperature of 25°C and an ambient temperature of 60%. Under the condition of humidity, use a mixer to fully stir until it is completely transparent visually and the viscosity is 25 seconds, that is, the ready-to-use mixed glue is obtained. At the same time, fix the silicon crystal plate on a special glass tray, fix it with screws, put it in an oven and heat it to 80°C for 10 minutes;

[0031] 2) After baking, take out the silicon crystal plate together with the tray and place it on the workbench, and use a glue pot to drip glue, and the coating amount is 850g / m 2 ;

[0032] 3) Use a glass rod to make the mixed glue on the silicon crystal plate even;

[0033] 4) Put the glued silicon crystal plate together with the tray into the vacuum box smoothly, and vacuumize to -1×10 5 Pa and maintain ...

Embodiment 2

[0037] 1) Select glue A with epoxy resin as the main component and glue B as curing agent produced by Dongguan Liduo Electronic Materials Co., Ltd., and weigh them at a weight ratio of 2:1. Under humidity conditions, use a mixer to fully stir until it is completely transparent visually, and the viscosity is 28 seconds, that is, the ready-to-use mixed glue is obtained. At the same time, fix the silicon crystal plate on a special glass tray, fix it with screws, and bake it in an oven at 80°C for 10 minutes;

[0038] 2) Take out the baked silicon crystal plate together with the tray and place it on the workbench, inject glue with a syringe, and the coating amount is 920g / m 2 ;

[0039] 3) Use a glass rod to make the mixed glue on the silicon crystal plate even;

[0040] 4) Put the glued silicon crystal plate together with the tray into the vacuum box smoothly, and vacuumize to -1×10 5 Pa and maintain for 5 minutes;

[0041] 5) Take out the silicon crystal plate together with ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses a dripping adhesive encapsulation method of a solar paster component, the steps are: A, placing the solar paster plate in the bake oven for baking; B, the mix gum is stirred to colloid transparent by stirring implement after the A gum and the B gum are mixed by volume ratio; C, the homogeneous mix gum is injected into dripping gum tools to inject mix gum on the front face of the paster; D, the mix gum on the paster plate is uniform by the glass rod; E, the dripping rubber plate is arranged in the vacuum box to start-up the vacuum switch; F, the dripping slab rubber with a vacuum treating is placed in the bake oven to solid the dripping slab rubber in the bake oven; G, the dripping slab rubber is taken out from the bake oven, and the redundant gum is removed at the temperature below 50EDG C. The method of present invention is good, the produced dripping rubber plate has high light transmittance ratio, good sealability, beautiful external shape, long length of life, reasonable process design, easy operations, short curing time, tight combination between the colloid and the silicon plate.

Description

technical field [0001] The invention belongs to the technical field of semi-finished product processing of solar photovoltaic cell components, and more specifically relates to a method for encapsulating solar patch components with glue, and is especially suitable for the processing of semi-finished solar photovoltaic cell components. Background technique [0002] Solar cell modules refer to solar photovoltaic devices composed of solar cells, packaging materials, junction boxes, etc. Solar patch components refer to silicon crystal panel components made by welding silicon-based solar cells to epoxy resin plates or plastic plates through the patch process. There are no welding spots on the surface, and the gaps between the solar battery sheets are small and uniform, which can improve the photoelectric conversion rate of the solar battery module. The silicon crystal plate can be a single crystal silicon plate or a polycrystalline silicon plate. [0003] At present, there are t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01L31/18
Inventor 丁孔奇
Owner JIAWEI SOLAR WUHAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap