Lubricating antistatic high-performance oil for drawing production of carbon fibre

A production process, carbon fiber technology, applied in the fields of lubricating antistatic high-performance oils and chemical materials, to prevent friction and wear, prevent adhesion and parallel wires, and avoid defects

Inactive Publication Date: 2012-07-18
李元杰
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] At present, the domestic spinning oils are mainly Tween-Span, and the main disadvantages are the smoothness of the silk,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The total weight of raw materials in this example is 1000 kg, including 3 kg of quaternary ammonium cationic surfactant, 1 kg of polyoxyethylene-polyoxypropylene polyether, 8 kg of ammonia-modified silicone oil, 8 kg of epoxy-modified silicone oil, 8 kg of polyether modified silicone oil, 20 kg of fluorosilicone oil, 1 kg of polyoxyethylene laurate, 3 kg of polyoxyethylene lauryl ether, 20 kg of polyoxyethylene hydrogenated castor oil, and the balance is high-purity deionized water.

[0025] 1. Ammonia modified silicone oil

[0026] Ammonia-modified silicone oil considers the following indicators:

[0027] ⑴Modified ammonia mass fraction. NH 2 Calculated as 0.001 to 0.05. When it is less than 0.001, the hydrophilicity of the oil agent is poor; when it exceeds 0.05, the heat resistance decreases.

[0028] (2) The viscosity after modification is 10-3~5×10-3 m2 / s (25°C).

[0029] ⑶ After modification, the Si / C ratio should be above 0.01%.

[0030] ⑷ The degree of the...

Embodiment ２

[0054] The total weight of raw materials in this example is 1000 kg, including 10 kg of quaternary ammonium cationic surfactant, 3 kg of polyoxyethylene-polyoxypropylene polyether, 2 kg of ammonia-modified silicone oil, 2 kg of epoxy-modified silicone oil, 2 kg of polyether modified silicone oil, 10 kg of fluorosilicone oil, 3 kg of polyoxyethylene laurate, 1 kg of polyoxyethylene lauryl ether, 4 kg of polyoxyethylene hydrogenated castor oil, and the balance is high-purity deionized water. Stir in the reaction kettle for 3 to 5 hours, and control the temperature within the range of 56 to 60°C to obtain the finished oil agent.

Embodiment ３

[0056]The total weight of raw materials in this example is 1000 kg, including 5 kg of quaternary ammonium cationic surfactant, 2 kg of polyoxyethylene-polyoxypropylene polyether, 6 kg of ammonia-modified silicone oil, 5 kg of epoxy-modified silicone oil, 3 kg of polyether modified silicone oil, 15 kg of fluorosilicone oil, 2 kg of polyoxyethylene laurate, 2 kg of polyoxyethylene lauryl ether, 10 kg of polyoxyethylene hydrogenated castor oil, and the balance is high-purity deionized water. Stir in the reaction kettle for 3 to 5 hours, and control the temperature within the range of 56 to 60°C to obtain the finished oil agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention relates to the chemical materials of the new material field, in particular to a high-performance anti-static lubricating finish oil used in the carbon fiber wire-drawing production process. The composition of the raw materials is calculated with the weight percentage. The quaternary ammonium salt type cationic surfactant of 3 to 10, the polyoxyethylene-polyoxy-propylene-polyether of1 to 3, the ammonia modified silicone oil of 2 to 8, the epoxy-modified silicone oil of 2 to 8, the polyether modified silicone oil of 2 to 8, the fluoride silicon oil of 10 to 20, lauric acid polyoxyethylene ester of 1 to 3, the laurinol polyoxyethylene of 1 to 3, the polyoxyethylene hydrogenerated castor oil of 4 to 20, and the rest of high-purity deionized water are stirred in a reaction kettle for 3 to 5 hours with the temperature controlled within the range of 56 to 60 DEG C, thus the finish oil product can be produced. The invention is applied in the carbon fiber wiredrawing production process, in which the finish oil is in the formation of a membrane on a monofilament surface, not only the adhesion and merging between the monofilaments can be avoided, but also the friction and wear of the fiber surface with the roller during the production process can be prevented. Therefore, the finish oil has excellent smoothness, antistatic property, collection property and self-emulsifying property as well.

Description

technical field [0001] The invention belongs to chemical materials in the field of new materials, in particular to a lubricating and antistatic high-performance oil agent used in the production process of carbon fiber wire drawing. Background technique [0002] Polyacrylonitrile (PAN)-based carbon fiber, as the main reinforcing fiber for advanced composite materials, is an indispensable high-tech material in aerospace and defense industries. Due to the important use of high-performance carbon fiber in the military, foreign countries have imposed a technical blockade and product embargo on my country in recent years. At the same time, the market demand for carbon fiber has increased significantly, carbon fiber is expensive, and the price of related carbon fiber accessories has also soared. In recent years, my country has only increased its investment in the research and development of carbon fiber and its accessories. During the "Eleventh Five-Year Plan" period, my country fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F11/06D01F6/18D01F9/22
Inventor 李元杰
Owner 李元杰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com