Metallic oxide coating electrode and manufacture method thereof

An oxide coating and metal technology, applied in the field of electrochemical engineering, can solve the problems of narrow electrode application range, short electrode life, and limited improvement of electrode life, and achieve strong anodic oxidation resistance, high electrocatalytic activity, and noble metal The effect of low dosage

Active Publication Date: 2014-05-07
OCEAN UNIV OF CHINA
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Regarding the inhibition of the oxidation-induced passivation of the titanium substrate to cause electrode failure, the relevant literature has proposed the use of tantalum as the intermediate layer, but a fatal shortcoming of this method is that the cost of manufacturing the electrode is too high, and the application value is lost.
It is also pointed out in the literature that the oxidation passivation time of the titanium substrate can be reduced by increasing the number of coatings of the catalytic layer and increasing the thickness of the catalytic layer, but this undoubtedly greatly increases the manufacturing cost of the electrode, and in terms of the final effect, it affects the life of the electrode. Improvement is also limited
A Chinese patent application with application number 2006101441469 discloses a SnO 2 / IrO 2 -Ta 2 o 5 -SnO 2 / Ti electrode, a kind of titanium is disclosed in CN 03133317 as substrate, is coated with PbO 2 or SeO 2 In addition to the narrow scope of application, the above-mentioned electrodes all have the problems of high manufacturing cost and short electrode life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metallic oxide coating electrode and manufacture method thereof
  • Metallic oxide coating electrode and manufacture method thereof
  • Metallic oxide coating electrode and manufacture method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The structure of the metal oxide electrode of the present invention is as figure 1 As shown, it is coated with an intermediate layer 2 on the metal substrate 1, and coated with a metal oxide coating 3 on the intermediate layer 2; the metal substrate 1 is titanium, tantalum, niobium, zirconium, tungsten, aluminum or One of stainless steel; the intermediate layer 2 is prepared by impregnating the nano-powder of titanium-based cermet compound with a solution containing a platinum group metal compound to prepare an intermediate layer coating liquid, which is coated on the metal substrate, dried, oxidized The product obtained by thermal decomposition. The metal base 1 is treated with degreasing and acid etching. The middle layer 2 is a solution containing a platinum group metal compound impregnated with a nano-powder of a titanium-based cermet compound to form a middle layer coating liquid, which is coated on the metal substrate 1, and then oxidized and thermally decomposed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a metal oxide coating electrode, which comprises a metal base body and a metal oxide coating. The metal oxide coating electrode is characterized in that an intermediate layer is arranged between the metal base body and the metal oxide coating; the intermediate layer is coated on the metal base body, and the metal oxide coating is coated on the intermediate layer; the intermediate layer is the product which is obtained from the intermediate layer coating fluid manufactured from the nanometer powder of the titanium based ceramal compound soaked in the platinum group metal compound solution, coated on the metal base body, dried, oxidized and pyrolyzed. The invention also discloses a metal oxide coating electrode preparation method. The invention has the advantages that the precious metal consumption is less, the electric catalyzing activity is high, the electric conductivity is good, the anode oxidation resistance is strong, the service life is long, the manufacture is simple, and the production cost is low.

Description

technical field [0001] The invention relates to a metal oxide electrode and a preparation method thereof, in particular to a metal oxide coating electrode provided with an intermediate layer and a preparation method thereof, belonging to the field of electrochemical engineering. Background technique [0002] Both the electrochemical industry and the electrometallurgical industry are inseparable from electrodes, and the selection of electrode materials is extremely important. The direction and kinetics of the electrode process, the structure type of the electrode and the electrolytic cell and the life of the cell, the maintenance cost and labor consumption, and the dynamic index of the process all depend to a large extent on the structure of the electrode and the materials used, especially The electrode type and cell structure design are closely related to the durability, conductivity, electrocatalytic activity and power consumption of the electrode material. The continuous d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C25B11/00C25B11/04
Inventor 徐海波芦永红
Owner OCEAN UNIV OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products