Water-soluble metal fluorocarbon coatings with acid rain resistant function for external wall

A water-based fluorocarbon and acid rain-resistant technology, applied in coatings, latex paints, etc., can solve the problems that water-based coatings cannot meet the protection requirements, and achieve the effect of lasting protection from acid rain corrosion

Inactive Publication Date: 2009-04-01
上海三银制漆有限公司
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The use of ordinary water-based coatings cannot meet the protection requirements of harsh acid rain for decorated buildings. How to manufacture a water-based coating with acid rain resistance is a problem for technicians to solve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] Preparation of water-based glitter paint:

[0034] Pretreatment of aluminum silver paste or pearlescent pigment;

[0035] Stir the aluminum silver paste or pearlescent pigment, solvent, and wetting agent into a uniform paste, soak for more than 4 hours for later use;

[0036] Mix part of deionized water, antifreeze, and other additives (such as dispersant, defoamer, leveling agent) one by one, disperse at a slow speed for 20 minutes, slowly add fluorocarbon emulsion, and stir evenly;

[0037] Add film-forming aids and some deionized water one by one, and stir evenly;

[0038] Slowly add the well-stirred mixed solution into the soaked metal pigment slurry, and stir evenly at a slow speed.

[0039] performance comparison

[0040] Ordinary water-based glitter paint Product of the present invention Exterior Flat and smooth with a metallic effect Flat and smooth with a metallic effect Adhesion Level 1 Level 1 Water resistance (168h) n...

Embodiment 1

[0045] Waterborne fluorocarbon flash paint

[0046] Fluorocarbon emulsion 60.0%

[0047] Aluminum silver paste (metallic pigment) 8.0%

[0048] Solvent 8.0%

[0049] Orienting agent 3.0%

[0050] Wetting and dispersing agent 0.5%

[0051] Defoamer 0.3%

[0052] Thickener 1.8%

[0053] Coalescent 1.2%

[0054] Antifreeze 1.0%

[0055] Deionized water 16.2%

Embodiment 2

[0057] Water-based fluorocarbon white paint

[0058] Fluorocarbon emulsion 55.0%

[0059] Dispersant 0.5%

[0060] Wetting agent 0.2%

[0061] Defoamer 0.4%

[0062] Neutralizer 0.1%

[0063] Thickener 1.0%

[0064] Rutile titanium dioxide 24.3%

[0065] Superfine Barium Sulfate 8.0%

[0066] Preservatives 0.2%

[0067] Coalescent 1.1%

[0068] Antifreeze 1.2%

[0069] Deionized water 8.0%

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an acid rain resistant aqueous fluorocarbon coating used for external walls. The coating consists of the following raw materials in the following percents by weight: 55-75 percent of fluorocarbon emulsion, 5-35 percent of pigment, 0.2-2.2 percent of wetting and dispersing agent, 0-0.5 percent of neutralizing agent, 0.1-0.5 percent of antifoam agent, 0-0.5 percent of preservative, 0.1-5.0 percent of thickening agent, 0-5.0 percent of orienting agent, 0-10.0 percent of solvent, 1-6 percent of film forming agent, 1-3 percent of anti-freezing agent, and deionized water as the rest, wherein, the pigment is aluminum paste, pearl pigment, ceramic pigment, rutile titanium dioxide powder, chrome oxide green, cobalt blue, high quality carbon black or phthalocyanine blue. The acid rain resistant aqueous fluorocarbon coating for external walls can permanently protect the decorated buildings against corrosion of acid rain.

Description

technical field [0001] The invention relates to a coating, in particular to a coating for exterior walls. Background technique [0002] In my country's Southwest, Central China, and East China, there are three major acid rains, and the erosion of the outer wall by acid rain is increasing day by day. The use of common water-based coatings cannot meet the protection requirements of harsh acid rain for decorated buildings. How to manufacture a water-based coating with acid rain resistance is a problem for technicians to solve. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a water-based fluorocarbon coating with acid rain resistance function for exterior walls, aiming to solve the above-mentioned problems. [0004] In order to solve the above technical problems, the present invention is achieved through the following technical solutions: [0005] The present invention is made up of following raw material by mass ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D127/12C09D5/00C09D5/02
Inventor 黄银贤何生才马安荣池钟慷
Owner 上海三银制漆有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com