Waterproof anticracking construction exterior wall paint

A technology for building exterior walls and coatings, applied in the fields of coatings and building materials, can solve the problems of weak weather resistance and water resistance, burst cracking, and poor adhesion, and achieve the effect of good waterproof and crack resistance and good adhesion.

Inactive Publication Date: 2009-05-20
于士井
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing building exterior wall coatings have poor adhesion, weak weather re

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0012] Example

[0013] First put 100 parts of water into the container, add 40 parts of polyvinyl alcohol, 15 parts of bisphenol A epoxy resin, 5 parts of zinc silicate powder, 5 parts of shell powder, 5 parts of methyl cellulose, 3 parts of glass beads, 3 parts of glass fiber and 5 parts of nano silica are mixed and stirred. The temperature is raised until all the objects in the container are dissolved, then cold water and 0.1 part of defoamer are added, and the temperature is continued to eliminate the bubbles that appear with the defoamer. The glue in the container is clear and transparent. After cooling, it is placed in a special container, and it can be equipped with filler and antibacterial agent for scraping.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A waterproof and anti-cracking building exterior wall coating comprises base material, filler and an antibacterial agent and is characterized in that the base material is polyvinyl alcohol, bisphenol An epoxide resin, aluminium silicate powder, oyster shell whiting, methylcellulose, glass microballoon, fiber glass, nanometer silicon dioxide, antibacterial agent and antifoaming agent, the filler is calcium carbonate and the antibacterial agent is calcium sulphate crystal whisker artificially growing. By virtue of methyl silica high polymer formed after the reaction between heated silicate and organosilicone, the coating can form the binding of chemical bonds when being coated on the rigid surface of a concrete wall, with the fastness being far superior to that of the physical covering of a conventional coating; in the coating, nanometer silica powder and calcium sulphate crystal whisker are also adopted as the antibacterial agent, therefore, the coating has good effect on inhibiting and killing bacteria, fungus and mycete and is characterized by good waterproof and anti-cracking performance, no bubbling and cracking and good adhesive force.

Description

Technical field [0001] The invention relates to a coating, in particular to a waterproof and anti-cracking architectural exterior wall coating, which belongs to the category of building materials. Background technique [0002] The existing building exterior wall coatings are mainly solvent-based coatings and water-based coatings, which are applied to the outer surface of the wall to achieve decorative effects and prevent erosion by water, air, microorganisms and various corrosive substances. It is composed of base materials, additives and fillers. Existing coatings for exterior walls of buildings have poor adhesion, weak weather resistance and water resistance, and cracks will occur after a long time of use. Contents of the invention [0003] The purpose of the present invention is to overcome the above-mentioned deficiencies of the prior art, and provide a waterproof and anti-cracking architectural exterior wall coating by improving the formula. Oxygen polymer, coated o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D129/04C09D7/12C09D5/16C09D163/02
Inventor 于士井
Owner 于士井
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products