Novel waterproof air previous polyurethane artificial leather and preparation thereof
A waterproof, breathable, and manufacturing method technology, which is applied to chemical instruments and methods, synthetic resin layered products, textiles and papermaking, etc., can solve the problems of performance degradation and destruction of polyurethane bond structure, etc., and achieve high physical properties, plump hand feeling, Excellent waterproof and breathable effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0099] Example 1:
[0100] (1) Wet slurry preparation (weight ratio):
[0101] Thermoplastic polyurethane elastomer resin (SW-2020RH) 100 parts
[0102] N,N-Dimethylformamide (DMF) 70 parts
[0103] Solvent pigment (such as: white paste) 0.5 part
[0104] 15 parts of wood flour
[0105] Anionic surfactant (D-700) 1 part
[0106] Non-ionic surfactant (D-101) 0.5 part
[0107] Water and oil repellent (PF-1108) 2 parts
[0108] Using wet synthetic leather production equipment, the prepared thermoplastic wet polyurethane slurry is coated on the synthetic leather woven fabric and then enters the coagulation tank to solidify, washed and dried to prepare wet synthetic leather semi-finished products.
[0109] (2) Preparation of semi-finished products of waterproof and breathable wet synthetic leather: using a post-processing grinder, the semi-finished products of wet synthetic leather prepared in (1) are subjected to grinding treatment to obtain semi-finished waterproof and breathable wet...
Example Embodiment
[0131] Example 2:
[0132] (1) Wet slurry preparation (weight ratio):
[0133] Thermoplastic polyester polyurethane resin (SW-2020RH) 100 parts
[0134] N,N-Dimethylformamide (DMF) 60 parts
[0135] Solvent color paste (black paste) 0.5 part
[0136] Wood flour 5 parts
[0137] Anionic surfactant (D-700) 2 parts
[0138] Non-ionic surfactant (D-101) 1 part
[0139] Water and oil repellent (PF-1108) 1 part
[0140] Using wet synthetic leather production equipment, the formulated thermoplastic wet polyurethane slurry is coated on the non-woven fabric base fabric for synthetic leather and then enters the coagulation tank to solidify, washed and dried to obtain semi-finished wet synthetic leather.
[0141] (2) Preparation of semi-finished products of waterproof and breathable wet synthetic leather: using a post-processing grinder, the semi-finished products of wet synthetic leather prepared in (1) are subjected to grinding treatment to prepare semi-finished waterproof and breathable w...
Example Embodiment
[0160] Example 3:
[0161] (1) Wet slurry preparation (weight ratio):
[0162] Thermoplastic polyurethane elastomer resin (SW-2020RH) 100 parts
[0163] N,N-Dimethylformamide (DMF) 70 parts
[0164] Solvent pigment (such as: white paste) 0.5 part
[0165] 15 parts of wood flour
[0166] Anionic surfactant (D-700) 1 part
[0167] Non-ionic surfactant (D-101) 0.5 parts
[0168] Water and oil repellent (PF-1108) 2 parts
[0169] Using wet synthetic leather production equipment, the formulated thermoplastic wet polyurethane slurry is coated on the synthetic leather woven fabric and then enters the coagulation tank to solidify, washed and dried to obtain semi-finished wet synthetic leather.
[0170] (2) Preparation of semi-finished products of waterproof and breathable wet synthetic leather: the semi-finished wet synthetic leather prepared by (1) is subjected to acupuncture and perforation treatment using post-processing perforating equipment to obtain semi-finished waterproof and brea...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap