A kind of preparation method and application of antibacterial cellulose ester

A technology of cellulose and cellulose derivatives, which is applied in medical science, absorbent pads, bandages, etc., can solve the problems of uneven separation effect of films, inability of samples to enter the separation membrane, failure to achieve separation effect, etc., and achieve good antibacterial effect , Avoid bacteria, excellent antibacterial properties

Active Publication Date: 2021-06-01
深圳市菩安科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Cheng Chi et al. conducted an experimental analysis of the problems that often occur in the separation of serum proteins by cellulose acetate membranes, and obtained the factors that affect the electrophoretic spectrum. , resulting in different brittleness of the membrane, resulting in uneven separation effect of the entire membrane during the protein separation process, so the cellulose acetate membrane should be soaked in buffer before use, and it should not be too much during the process of filter paper drying the membrane. Dry, otherwise the sample will not be able to enter the pores of the separation membrane, and a good separation effect will not be achieved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method and application of antibacterial cellulose ester
  • A kind of preparation method and application of antibacterial cellulose ester
  • A kind of preparation method and application of antibacterial cellulose ester

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] A kind of preparation method of antibacterial cellulose ester:

[0051] (1) Take 1 g of cellulose diacetate (CDA), 0.36 g of phthalic anhydride in an equimolar amount, and 3.38 mL of catalyst triethylamine. The molar number of the catalyst is 10 times the hydroxyl content of cellulose diacetate. First, dissolve 1g of cellulose diacetate in a 100mL three-necked round-bottomed flask filled with 20mL of acetone solution, put it on a magnetic stirrer, heat and stir at 60°C for about 2h, and raise the temperature to 65°C. After the cellulose acetate was completely dissolved, 0.36 g of phthalic anhydride and 3.38 mL of catalyst triethylamine were added to react for 24 hours. After the reaction, the reaction solution was slowly dropped into 100mL of absolute ethanol to precipitate and wash 3 times, and the esterified product was obtained by suction filtration, and the obtained esterified product was vacuum-dried at 40°C for 8 hours to obtain cellulose diacetate and acid anhydr...

Embodiment 2

[0057] A kind of preparation method of antibacterial cellulose ester:

[0058] (1) Weigh 1 g of purified cellulose diacetate, 0.25 g of succinic anhydride in an equimolar amount, and 3.38 mL of catalyst triethylamine, the number of moles of the catalyst being 10 times the hydroxyl content of cellulose diacetate. First, dissolve 1g of cellulose diacetate in a 100mL three-necked round-bottomed flask filled with 20mL of acetone solution, heat and stir for about 2 hours at 60°C on a magnetic stirrer, and raise the temperature to 65°C. After the cellulose was completely dissolved, 1.98 g of succinic anhydride and 3.38 mL of catalyst triethylamine were added to react for 24 hours. After the reaction, the reaction solution was slowly dropped into 100mL of absolute ethanol to precipitate and wash 3 times, and the esterified product was obtained by suction filtration, and the obtained esterified product was vacuum-dried at 40°C for 8 hours to obtain cellulose diacetate and Succinic an...

Embodiment 3

[0064] A kind of preparation method of antibacterial cellulose ester:

[0065] (1) Take 1 g of cellulose diacetate (CDA), 1.34 g of stearic anhydride (SA) in equimolar amounts, and 3.38 mL of catalyst triethylamine. Dissolve cellulose diacetate in 20mL of acetone solution, heat and stir on a magnetic stirrer at 60°C, the temperature rises to 65°C, after the cellulose diacetate is completely dissolved, add 1.34g of stearic anhydride, catalyst triethyl Amine 3.38mL, reacted for 10 hours.

[0066] (2) Add 0.1g N-hydroxysuccinimide (NHS), 0.15g 1-(3-dimethylaminopropyl)-3-ethylcarbodiimide hydrochloride (EDC), 0.3g levofloxacin In 10mL DMF solution, activate overnight under ice bath conditions, add 0.13g Boc-EDA to react for 12h, then add 0.1g trifluoroacetic acid to remove Boc, add 0.3mL triethylamine dropwise after 1h to adjust pH, stir for 1h;

[0067] (3) Dissolve 0.3g of the esterified product CDA-g-SA in 10mL of DMF solution, add 0.1g of N-hydroxysuccinimide (NHS), 0.15g o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing antibacterial cellulose and the application of the prepared antibacterial cellulose in preparing antibacterial fiber dressings. The preparation method is as follows: purification of cellulose derivatives; adding the purified cellulose derivatives and acid anhydrides into an acetone solution for heating and stirring under the condition of a catalyst; Precipitation, washing, suction filtration to obtain the esterified product, and grafted esterified product; grafting ethylenediamine protected by di-tert-butyl dicarbonate with a broad-spectrum antibacterial agent; esterification reaction between the esterified product and the product to obtain antibacterial fiber white. The hygroscopicity of the esterification product prepared by the present invention is enhanced, and the modified product of the grafted antibacterial agent has good antibacterial effect on negative and positive bacteria. At the same time, it also has the advantages of waterproof and moisture permeability, which can form a good protection for the wound area.

Description

technical field [0001] The invention relates to the esterification modification and antibacterial performance research of cellulose diacetate, in particular to the preparation of an electrospun antibacterial fiber and its application in the field of medical dressings. Background technique [0002] Acetate fiber has a luster and feel similar to silk, and is often used as a substitute for silk, as the lining of skirts or coats, and blended with synthetic fibers to produce composite yarns for various high-end clothing. In addition to being used in textiles, acetate fiber is also widely used in medical dressings, cigarette filters and other fields. [0003] Because CA fiber has hydrophilic properties and good hygroscopic properties, it is especially suitable for anti-inflammatory and antibacterial gauze, wound dressings, etc. In a humid environment, various bacteria are easy to breed on the surface of the wound, and the gauze made of CA material can avoid excessive moisture and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08B15/06A61L15/46A61L15/20A61L15/28A61L15/42
CPCA61L15/20A61L15/28A61L15/42A61L15/46A61L2300/216A61L2300/404C08B15/06C08L1/08
Inventor 吴德群汤双双朱婕韩华李发学王学利俞建勇杨占平曹建华陈昀
Owner 深圳市菩安科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com