Polysiloxane coating composition

A technology of polysiloxane and composition, which is applied in the field of polyetheramine resin and coating chemical manufacturing, can solve the problems of impractical industrial anti-corrosion application, and achieve the effect of excellent interlayer adhesion and excellent anti-corrosion performance

Active Publication Date: 2009-09-09
中山大桥化工集团有限公司
View PDF0 Cites 42 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In order to improve the durability of the topcoat in industrial anti-corrosion coatings, the world's major coating companies have made many attempts in inorganic chemistry, but many polymers need to be baked to cross-link to form a film, which is in general industrial anti-corrosion applications. unrealistic in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polysiloxane coating composition
  • Polysiloxane coating composition
  • Polysiloxane coating composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0075] The composition of the present invention is composed of component A and component B. Therefore, it is prepared in two parts during specific preparation, and is placed in two containers. When used, components A and B are mixed and coated. Protective film available.

[0076] 1. Preparation method:

[0077] Add 25 parts of epoxy resin, 15 parts of acrylic resin, 1 part of dispersant, 25 parts of titanium dioxide, 5 parts of talc powder, 10 parts of mica powder, 1 part of rheological additive, and 1 part of anti-settling agent into a 1000-liter reactor , 10 parts of xylene solvent, 7 parts of butyl acetate. Then stir at a high speed until the fineness is less than or equal to 30um, and pack separately to obtain the main ingredient component A.

[0078] Add 30 parts of solid agent 1 and 10 parts of solid agent 2 into a 1000-liter agitator, stir and disperse evenly, filter and package, and obtain component B.

[0079] 2. Coating method:

[0080] The composition of the prese...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a polysiloxane coating composition belonging to a coating chemical manufacturing technology. The polysiloxane coating composition is obtained by reacting hydrogenated epoxide resin and amino-functionalized siloxane and combining acrylic resin with good coating performance and weatherability and polyetheramine resin with excellent flexibility and adhesion. The invention particularly relates to a polysiloxane coating composition applied to offshore oil platforms. The polysiloxane coating composition has weather-proof, water-proof and corrosion-resistant performances, good flexibility and excellent ply adhesion. The polysiloxane coating composition comprises the following ingredients of 12-50 of epoxide resin, 10-40 of acrylic resin, 0.5-1.5 of dispersant, 20-30 of titanium pigment, 5-25 of French chalk, 5-15 of mica powder, 0.5-1.5 of rheological agent, 0.5-2 of anti-settling agent, 2-10 of dimethyl benzene, 5-10 of butyl acetate, 15-40 of curing agent 1 and 5-25 of curing agent 2 according to the weight percent.

Description

【Technical field】 [0001] The invention is a hydrogenated epoxy resin reacted with amino-functional siloxane, and combined with an acrylic resin with excellent recoating performance and weather resistance and a polyetheramine resin with excellent flexibility and adhesion, especially for marine The polysiloxane coating composition for an oil platform belongs to the coating chemical manufacturing technology. 【Background technique】 [0002] In order to improve the durability of the topcoat in industrial anti-corrosion coatings, the world's major coating companies have made many attempts in inorganic chemistry, but many polymers need to be baked to cross-link to form a film, which is in general industrial anti-corrosion applications. unrealistic. However, polysiloxane coatings have always been considered as a potential technical route for air-drying and curing into films. However, little progress was made in this area until the first patent was issued in 1981 for an interpenetr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D183/04C09D163/02C09D133/02C09D7/12C09D5/08
Inventor 范国栋夏必来朱龙晖
Owner 中山大桥化工集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com