Flake board with ultraviolet photo-curing paint aluminum foil veneer and manufacturing method thereof

A production method and particle board technology, which are applied in chemical instruments and methods, manufacturing tools, wood-layered products, etc., can solve the problems of toxic and harmful decorative materials and finishing materials, poor fire resistance of gorgeous boards and polar boards, and surface strength of decorative materials. problems such as poor hardness and poor hardness, to achieve the effect of improving the working environment and use environment, improving labor productivity and compact structure

Inactive Publication Date: 2012-09-05
HAOJIA WOODEN IND HEILONGJIANG
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] There are many problems in various decorative boards on the existing market, such as gorgeous boards and Polaroid boards have poor fire resistance and are not tough; particleboards and medium density fiberboards have rough surfaces and formaldehyde emissions do not meet indoor environmental protection requirements. The decorative materials and coating materials are toxic and harmful; the surface strength and hardness of the decorative materials are poor, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flake board with ultraviolet photo-curing paint aluminum foil veneer and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Particleboard with ultraviolet photocurable varnish aluminum foil decoration, its composition includes: Particleboard 1, the upper and lower sides of the particleboard are compounded with aluminum foil 2 that has been flow-coated with photocurable varnish, and the aluminum foil is plain foil, colored foil or printed aluminum foil.

[0019] In the method for making the particleboard with the aluminum foil veneer of the ultraviolet light-curing paint, the particleboard has three layers of paint surface, so that the paint surface layer is smooth, plump and uniform, and the paint surface is guaranteed to be continuous and stable without delamination. First coat the metal adhesive on the back of the aluminum foil and wait for it to solidify without pressure, then coat the particleboard with phenolic resin adhesive, and then paste the cured glued surface of the aluminum foil on the particleboard substrate that has been coated with glue, and then use the adhesive force The extr...

Embodiment 2

[0021] Particleboard with ultraviolet photocurable varnish aluminum foil decoration, its composition includes: Particleboard 1, the upper and lower sides of the particleboard are compounded with aluminum foil 2 that has been flow-coated with photocurable varnish, and the aluminum foil is plain foil, colored foil or printed aluminum foil.

[0022] The particleboard with ultraviolet light curing paint and aluminum foil decoration has a sandwich board 3 between the particleboard and the aluminum foil.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a flake board with an ultraviolet photo-curing paint aluminum foil veneer and a manufacturing method thereof and aims to overcome the defects that various prior decorative boards in the markets have many problems. The flake board with the ultraviolet photo-curing paint aluminum foil veneer comprises a flake board (1), wherein the upper surface and the lower surface of theflake board are compounded with aluminum foils (2) which are coated with photo-curing paint. The manufacturing method comprises the following steps: firstly, the back surface of the aluminum foils arecoated with metal binding agents, after the binding agents are solidified without pressure, the flake board is coated with phenolic resin bonding adhesive, and the solidified back surface coated withthe metal binding agents of the aluminum foils are bond to the base material of the flake board, which is coated with binding agent; then a photo-curing roller with extremely strong adhesive force isused for coating a first layer of primer, after the primer is half dried by photo-curing, a second layer of primer is coated by using the photo-curing roller, and finally a third layer of finish paint is sprayed; finally, a hot-stream flattening machine at 80 DEG C is used for flattening the paint surface. The flake board can be used an architectural decoration board.

Description

Technical field: [0001] The invention relates to a fireproof veneer composited with an aluminum foil coated with an ultraviolet photocurable varnish, in particular to a particleboard with an aluminum foil veneer of an ultraviolet photocurable varnish and a manufacturing method of the particleboard. Background technique: [0002] There are many problems in various decorative boards on the existing market, such as gorgeous boards and Polaroid boards have poor fire resistance and are not tough; particleboards and medium density fiberboards have rough surfaces and formaldehyde emissions do not meet indoor environmental protection requirements. The decorative materials and coating materials are poisonous and harmful; the surface strength and hardness of the decorative materials are poor. Invention content: [0003] The object of the present invention is to provide a kind of particleboard with ultraviolet light curing paint aluminum foil facing compounded with the aluminum foil ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B27D1/04B27D1/08B32B21/04
Inventor 丁乃今
Owner HAOJIA WOODEN IND HEILONGJIANG