Method for preparing auricularia polytricha culture material

A preparation method and a technology for preparing nutrients, which are applied in the directions of botanical equipment and methods, fertilizer mixtures, superphosphate, etc., can solve the problems of unfavorable growth of Auricularia auricularia, small size of Auricularia auricularia, low nutritional content, etc., and achieve a formula and a preparation method. Simple, fast growth, good quality results

Inactive Publication Date: 2009-11-11
孙伟
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, when people are cultivating Auricularia auricula, they generally use straw material as the basis, adding some manure, chaff, etc., although the effect is very good, but the content of nutrients in the ingredients is relatively low, which is very harmful to the growth of Auricularia auriculae. Unfavorable, the fungus produced is small, thin, light in weight, slow in growth, prone to disease

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0007] Embodiment 1: 35% of cottonseed hulls, 45% of rice bran, 13% of miscellaneous sawdust, 2% of corncobs, 0.8% of straw, 1% of superphosphate, 0.6% of gypsum, 1.5% of bean straw powder, 0.1% of oxygen-increasing powder, nitrogen 0.2% of phosphorus and potassium compound fertilizer, 0.3% of canmexyl solution, and 0.5% of superphosphate, and the stated percentages are percentages by weight.

[0008] Take cottonseed hulls, rice bran, miscellaneous wood chips, corncobs, rice straw, and bean straw powder in proportion and combine them together, pour them into a grinder and grind them into particles of about 80 meshes, and then add superphosphate, gypsum, oxygen-increasing powder, Nitrogen, phosphorus and potassium compound fertilizer, Kempirin liquid, superphosphate, and then pour it into the blender and stir for 70 minutes, take it out, put it into the fermentation tank, add 1:1.2-1:1.3 water in proportion and mix well to form a heap, use a thick The plastic thin mold is tight...

Embodiment 2

[0012] Embodiment 2: 55% of cottonseed hulls, 27% of rice bran, 10% of miscellaneous sawdust, 1.6% of corncobs, 1% of straw, 0.8% of superphosphate, 1% of gypsum, 2% of bean straw powder, 0.3% of oxygen-increasing powder, nitrogen 0.3% of phosphorus and potassium compound fertilizer, 0.2% of canmexyl solution, and 0.8% of superphosphate, and the stated percentages are percentages by weight.

[0013] Take cottonseed hulls, rice bran, miscellaneous wood chips, corncobs, rice straw, and bean straw powder in proportion and combine them together, pour them into a grinder and grind them into particles of about 80 meshes, and then add superphosphate, gypsum, oxygen-increasing powder, Nitrogen, phosphorus and potassium compound fertilizer, Kempirin liquid, superphosphate, and then pour it into the blender and stir for 70 minutes, take it out, put it into the fermentation tank, add 1:1.2-1:1.3 water in proportion and mix well to form a heap, use a thick The plastic thin mold is tightly...

Embodiment 3

[0015] Embodiment 3: 45% of cottonseed hulls, 33% of rice bran, 16% of miscellaneous sawdust, 1.7% of corncobs, 0.5% of straw, 0.5% of superphosphate, 0.5% of gypsum, 1.8% of bean straw powder, 0.2% of oxygen-increasing powder, nitrogen 0.1% of phosphorus and potassium compound fertilizer, 0.1% of canmexyl solution, and 0.6% of superphosphate, and the stated percentages are percentages by weight.

[0016] Take cottonseed hulls, rice bran, miscellaneous wood chips, corncobs, rice straw, and bean straw powder in proportion and combine them together, pour them into a grinder and grind them into particles of about 80 meshes, and then add superphosphate, gypsum, oxygen-increasing powder, Nitrogen, phosphorus and potassium compound fertilizer, Kempirin liquid, superphosphate, and then pour it into the blender and stir for 70 minutes, take it out, put it into the fermentation tank, add 1:1.2-1:1.3 water in proportion and mix well to form a heap, use a thick The plastic thin mold is t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing auricularia polytricha culture material, needing the following materials by the weight percent: 35-55 of cotton seed hulls, 25-45 of rice bran, 10-16 percent of mixed wood dust, 1.5-2 percent of corn cob, 0.5-1 of straw, 0.5-1 calcium superphosphate, 0.5-1 of plaster, 1.5-2 of beanstalk powder, 0.1-0.3 of oxygen increasing powder, 0.1-0.3 of nitro-phosphor-potash compound fertilizer, 0.1-0.3 of mold resisting liquid and 0.5-0.8 of calcium superphosphate. The method for preparing auricularia polytricha culture material comprises the following steps: the cotton seed hulls, the rice bran, the mixed wood dust, the corn cob, the straw and the beanstalk powder are taken according to the weight percent, mixed together and poured into a pulverizer to be pulverized into mixture with granules of about 80 meshes; the mixture is taken out; the superphosphate, the plaster, the oxygen increasing powder, the nitro-phosphor-potash compound fertilizer, the mold resisting liquid and the calcium superphosphate are added to the mixture; the new mixture is poured into a stirrer to be stirred for about 70 min; the stirred mixture is taken out and then put into a fermentation tank; water is added to the stirred mixture at the ratio of 1:1.2-1.3; and the stirred mixture is stirred again and stacked; and the stacked mixture is sealed by a thick plastic film to be fermented for 10-12h, therefore, the qualified auricularia polytricha culture material is prepared.

Description

technical field [0001] The invention relates to a nourishing material for fungus, in particular to a method for preparing the nourishing material for fungus. Background technique [0002] Auricularia auricula is a medium-high ear type, which is very suitable for cultivation in summer. The fungus has strong viability, strong anti-mildew ability and high biotransformation rate. At present, when people are cultivating Auricularia auricula, they generally use straw material as the basis, adding some manure, chaff, etc., although the effect is very good, but the content of nutrients in the ingredients is relatively low, which is very harmful to the growth of Auricularia auriculae. Unfavorable, the fungus produced is small, thin, light in weight, slow in growth and prone to disease. Contents of the invention [0003] The purpose of the present invention is to provide a kind of: the cost is low, the high-quality compound nourishment that is especially suitable for the rapid gro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C05G3/00C05B1/02A01G1/04
Inventor 孙伟
Owner 孙伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap