Super heat resistant ceramic wok and manufacturing method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of super heat-resistant ceramic products, applied in cooking utensils, household utensils, applications, etc., can solve the problems of difficult production and processing, ceramic cooking utensils bursting, etc., achieve excellent thermal shock resistance and inhibit grain growth , the effect of not easy to deform
Inactive Publication Date: 2010-02-17
袁勇
View PDF1 Cites 18 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0007] The above ceramic cooking utensils are suitable for cooking methods such as boiling, stewing, steaming, etc. Under the protection of a large amount of soup, these cooking methods will heat the pot more evenly and the temperature difference will be small, so the requirements for the thermal performance of
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0025] Use the following formula:
[0026] Spodumene 49%
[0027] Quartz 16%
[0028] Kaolin 19%
[0029] Talc 8%
[0030] Waste porcelain slag 7%
[0031] Niobium oxide 0.5%
[0032] Polyacrylamine 0.5%
[0033] Adopting the process flow shown in the accompanying drawings, the highest firing temperature is 1320°C, the firing range is about 30°C, the cooling and holding temperature is 1150°C, and the holding time is 30 minutes, the product meeting the purpose of the present invention can be produced.
Embodiment 2
[0035] Use the following formula:
[0036] Spodumene 48%
[0037] Quartz 15%
[0038] Kaolin 20%
[0039] Talc 10%
[0040] Waste porcelain slag 6%
[0041] Niobium oxide 0.7%
[0042] Polyacrylamide 0.3%
[0043] Adopting the process flow shown in the accompanying drawings, the highest firing temperature is 1320°C, the firing range is about 30°C, the cooling and holding temperature is 1150°C, and the holding time is 30 minutes, the product meeting the purpose of the present invention can be produced.
Embodiment 3
[0045] Use the following formula:
[0046] Spodumene 47%
[0047] Quartz 18%
[0048] Kaolin 19%
[0049] Talc 8.1%
[0050] Waste porcelain slag 6.5%
[0051] Niobium oxide 1%
[0052] Polyacrylamide 0.4%
[0053] Adopting the process flow shown in the accompanying drawings, the highest firing temperature is 1320°C, the firing range is about 30°C, the cooling and holding temperature is 1150°C, and the holding time is 30 minutes, the product meeting the purpose of the present invention can be produced.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a super heat resistant ceramic wok and a manufacturing method thereof. The ceramic wok adopts the main raw materials of spodumene, quartz, kaolin, talc and waste ceramic slag, and a high-performance polyacrylamide dispersing agent is also added, thereby the dispersity and the stability of ceramic slurry are improved. Meanwhile, a small amount of niobium oxide is doped so asto restrain material grain growth and reduce an expansion coefficient and ensure that a product has small cracking and deformation and excellent thermal shock resistance. The super heat resistant ceramic wok can be suitable for quick-fry and cannot crack with intense fire and dry burning. The super heat resistant ceramic wok can also resist heat exchange at 650-20 DEG C without cracking, be not easy to have wok sticking and cannot be oxidized or corroded without toxicity and harm. The lead and cadmium dissolution rate of the super heat resistant ceramic wok is zero, and a radio-nuclide limit also conforms to the national standard.
Description
technical field [0001] The invention belongs to the technical field of inorganic ceramic materials, and in particular relates to a super heat-resistant ceramic frying pan and a manufacturing method thereof. This product is suitable for processing dishes in various ways such as frying, frying, deep-frying, stewing, boiling, and steaming. Background technique [0002] Ceramic cooking utensils have unique advantages such as good heat storage, environmental protection, and corrosion resistance. Various ceramic cooking utensils have appeared in common people's homes and catering industries, competing with traditional metal cooking utensils. [0003] In the 1990s, my country began to research and develop ceramic pots and utensils made of new low-expansion materials. New products were put on the market and were well received by consumers. The national light industry standard "QB / T2580-2002 Fine Ceramic Cooker" stipulates the performance requirements of this type of product, and th...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more