Fiber reinforced magnesium oxychloride red mud plate and preparation method

A magnesium oxychloride red mud and fiber-reinforced technology, applied in construction, building structure, covering/lining, etc., can solve the problems of high energy consumption, poor sound insulation effect, low hardness, etc., and achieve excellent mechanical properties and good sound insulation effect , Good bending resistance

Inactive Publication Date: 2010-09-08
NUCLEAR IND YANTAI TONCIN IND GRP CO LTD
View PDF6 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The situation of other patents is due to the high cost and difficulty in forming an effective market, so I won’t repeat them here
To sum up, patents related to the utilization of red mud have high energy consumption and difficult market operations, making it difficult to form a truly effective market space
[0003] At present, the building material gypsum board widely used in the market has the disadvantages of fear of water, poor sound insulation effect, low hardness, poor mechanical properties, and low toughness, which limits its application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiber reinforced magnesium oxychloride red mud plate and preparation method
  • Fiber reinforced magnesium oxychloride red mud plate and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The brine and the solid mixed material are stirred by a mixer at 120 rpm to make a slurry. The weight percentages of the brine and the solid mixed material are 25% of the brine and 75% of the mixed functional material, wherein the concentration of the brine is 28.5°. Add 1 % modifier; the solid mixed material is composed of 55% of wet red mud, 35% of light-burned magnesia and 10% of reinforcing fiber by weight. The prepared slurry mixture is rolled and extruded to form a plate-shaped embryo body. This plate-shaped embryo has the characteristics of fire prevention, waterproof, anti-static, heat insulation, sound insulation, strong pressure resistance, good folding resistance, and corrosion resistance; then it is solidified in an environment of 18-35°C, and cured under natural conditions for 3- After 5 days, after full compounding reaction and curing, the tensile strength of the product is 3.15Mpa, and the compressive strength is 13.67Mpa; the overall mechanical performan...

Embodiment 2

[0021] The brine and the solid mixed material are stirred by a mixer at 120 rpm to make a slurry. The weight percentage of the brine and the solid mixed material is 25% of the brine and 75% of the mixed functional material. The concentration of the brine is 28.5°, and 1.5% The modifier; the solid mixed material is composed of 65% wet red mud, 25% light-burned magnesium oxide and 10% reinforcing fiber by weight. The prepared slurry mixture is rolled and extruded to form a plate-shaped embryo body. This plate-shaped embryo has the characteristics of fire prevention, waterproof, anti-static, heat insulation, sound insulation, strong pressure resistance, good folding resistance, and corrosion resistance; then it is solidified in an environment of 18-35°C, and cured under natural conditions for 3- After 5 days, after full compounding reaction and curing, the tensile strength of the product is 3.05Mpa, and the compressive strength is 12.48Mpa. The overall mechanical performance ind...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fiber reinforced magnesium oxychloride red mud plate and a preparation method, and belongs to the utilization technology of waste material-red mud produced in alumina industry. The plate mainly comprises a solid blending material and brine, wherein the weight ratio of the brine is 15-30%, and the solid blending material comprises the following components by weight ratio: 30-70% of red mud, MgO of 25-60 % and 5-10% of reinforcing fiber; and 0.5-5% of modifier is added into the brine. The wet red mud, the magnesium oxide, the reinforcing fiber and the brine added with the modifier are subjected to extrusion molding by roller pressure after being uniformly mixed, naturally harden after solidification, and form a standard material or profile after shear processing. The plate is of a high-strength solidification plate with high content of red mud, has the advantages of fireproof, waterproof and anti-static performances, heat and noise insulation, strong pressure resistance, good fracture resistance, good corrosion resistance and the like, is widely used in construction, decoration and other industries, and can digest a lot of red mud to truly turn waste into wealth.

Description

technical field [0001] The invention relates to the utilization technology of red mud, a waste material produced in the alumina industry, specifically a high-performance fiber-reinforced magnesium oxychloride red mud plate prepared by using wet red mud as the main raw material and its preparation method, which belongs to the preparation method of using solid waste field of building materials. Background technique [0002] At present, the red mud produced by the alumina industry has piled up into mountains, and the huge amount has caused great harm to the environment. Although the process of selecting iron powder from red mud is mature, the selected red mud still needs to be discharged to red mud storage or red mud storage yard, which cannot have a substantial impact on the hazards of red mud. There is also a method of using red mud to prepare sintered ceramic tiles and building materials, but due to the high water content of red mud, generally more than 20%; the treatment p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/00C04B35/04C04B35/622E04F13/075
Inventor 房永广
Owner NUCLEAR IND YANTAI TONCIN IND GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products