A technology of oxidized polyethylene wax and microemulsion, which is applied in textiles, papermaking, fiber treatment, etc., can solve the problems of poor acid resistance stability, microemulsion flocculation, increased dosage, etc., and achieve transparent appearance, good dispersion and stability, The effect of broad application value

Active Publication Date: 2011-01-12
TAICANG BAONI IND CO LTD
View PDF1 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Through a large number of experiments, the inventor found that the oxidized polyethylene wax microemulsion prepared by the above-mentioned patent has defects in stability and application performance.
For example, the acid resistance stability of its finished product is relatively poor, and a small amount of pH value reduction can lead to flocculation or even coagulation o

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Microemulsion composite of polyethylene wax oxide
  • Microemulsion composite of polyethylene wax oxide
  • Microemulsion composite of polyethylene wax oxide

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0076] Example 1

[0077] table 3

[0078] Emulsion formula:

[0079]

[0080] Emulsification method:

[0081] 2.500 kg OA 2. 0.374 kg of polyoxyethylene laureth (3EO), 0.826 kg of polyoxyethylene laureth (20EO), 0.1000 kg of dodecyl trimethyl ammonium chloride, 0.210 kg of lauric acid and 5.990 kg of water added to high temperature In the high-pressure emulsification kettle, the materials are heated to 115°C under high temperature and high pressure, keep a certain stirring to make the heat exchange fully, keep the temperature for 30 minutes, and cool down to 50°C for discharge.

Example Embodiment

[0082] Example 2

[0083] Table 4

[0084] Emulsion formula:

[0085]

[0086] Emulsification method:

[0087] Combine 2.000 kg of AC 629A, 0.748 kg of dodecylamine polyoxyethylene ether (20EO), 0.423 kg of stearylamine polyoxyethylene ether (5EO) and 0.180 kg of cetyltrimethyl chloride Ammonium ammonium is added to the emulsification kettle, the materials are heated to 105°C at high temperature to melt them, the temperature of the materials is cooled to about 100°C, and 1 / 4 of 98°C hot water is slowly added to the emulsification kettle in about 30 minutes , And maintain high-speed stirring, add 1 / 3 of the 90℃ hot water into the emulsification kettle within 20 minutes, while maintaining high-speed stirring, quickly cool the material to 70℃, and add the remaining 5 / 12 of the cold water to the emulsifier The kettle, reduce the stirring speed, and discharge after cooling to 50°C.

Example Embodiment

[0088] Example 3

[0089] table 5

[0090] Emulsion formula:

[0091]

[0092] Emulsification method:

[0093] 0.25 kg palmitic acid polyoxyethylene ether (5EO), 0.75 kg lauric acid polyoxyethylene ether (20EO), 0.05 kg dodecyltrimethylammonium chloride, 0.22 kg palmitic acid, 2.4 kg Licowax PED 522 and 6.33 Kg of water is added to the emulsification kettle, the materials are heated to 115°C under high temperature and high pressure, a certain amount of stirring is maintained for sufficient heat exchange, the temperature is kept for 30 minutes, and the temperature is lowered to 50°C for discharge.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a microemulsion composite of polyethylene wax oxide, comprising 5 to 40% of polyethylene wax oxide in weight, 2 to 20% of nonionic surfactant in weight, 0.1 to 5% of cation surfactant in weight, 0 to 5% of assistant emulsifier in weight and 40 to 92% of water in weight based on the total weight of the microemulsion composite of polyethylene wax oxide. The microemulsion composite of polyethylene wax oxide of the invention has transparent appearance, good dispersibility and stability, and better acid resistance and applicability compared with the conventional microemulsion of polyethylene wax oxide. The microemulsion composite of polyethylene wax oxide of the invention can effectively enhance the sewing smoothness of the knit fabric.

Description

Technical field [0001] The invention relates to an oxidized polyethylene wax microemulsion composition, a preparation method and application thereof. Background technique [0002] Oxidized polyethylene wax is a modified product in which polyethylene wax is oxidized to introduce polar groups such as -COOH, -OH, and -CO-. Compared with polyethylene wax, oxidized polyethylene wax has better emulsifying properties. In recent years, due to the development of microemulsion technology, the preparation of oxidized polyethylene wax emulsion has become a hot spot in the research and development of auxiliary workers. Because of its excellent properties, oxidized polyethylene wax microemulsion has been widely used in leather, papermaking, textile and daily chemical industries. It is often used in acidic conditions when applied in leather, paper, textile and daily chemical industries. Under use. [0003] China Guangdong Textile Vocational and Technical College published CN 101289540 (2008) p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/30C08K5/06C08K5/19C08K5/09C08K5/17C08K5/103C08K5/3445D06M15/227
Inventor 顾喆栋杨晓辉
Owner TAICANG BAONI IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap