High-performance acidic transparent silicone sealant
A high-performance, sealant technology, applied in adhesives, non-polymer adhesive additives, adhesive additives, etc., can solve problems such as water resistance, affecting service life, high and low temperature resistance, etc., to improve strength and hardness, Uniform distribution of fillers and the effect of increasing the filling amount
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0022] Example 1 Take the following components by weight:
[0023] Hydroxy-terminated polydimethylsiloxane 10000 mpa.s 20 parts
[0024] Hydroxy-terminated polydimethylsiloxane 700,000 mpa.s 70 parts
[0025] Ethyl silicone oil 50 mpa.s 60 parts
[0026] 2.5 parts of methyltriacetoxysilane
[0027] 2.5 parts of ethyl triacetoxysilane
[0028] Fumed silica 80m 2 / g 10 servings
[0029] Fumed silica 150m2 / g 10 parts
[0030] 0.01 parts of 4-benzoyloxy-2,2,6,6-tetramethylpiperidine
[0031] 0.005 parts of dibutyl tin diacetate
[0032] According to the conventional preparation method, put the above-mentioned raw materials: 20 parts of hydroxy-terminated polydimethylsiloxane 10000 mpa.s, 70 parts of hydroxy-terminated polydimethylsiloxane 700,000 mpa.s, and 60 parts of ethyl silicone oil 50 mpa.s. After arriving in the glue making tank, push the glue making tank into the glue making machine, add 2.5 parts of methyl triacetoxy silane and 2.5 parts of ethyl triacetoxy silane, and vacuum (the vacu...
Example Embodiment
[0033] Example 2 Take the following components by weight:
[0034] Hydroxy-terminated polydimethylsiloxane 20000 mpa.s 100 parts
[0035] Hydroxy-terminated polydimethylsiloxane 400000 mpa.s 10 parts
[0036] Methyl silicone oil 5000 mpa.s 60 parts
[0037] 5 parts of methyl triacetoxysilane
[0038] 10 parts of ethyl triacetoxysilane
[0039] Fumed silica 170m 2 / g 8 parts
[0040] Fumed silica 220m2 / g 80 parts
[0041] 0.5 part of 4-benzoyloxy-2,2,6,6-tetramethylpiperidine
[0042] 0.4 parts of 2-hydroxy-4-methoxybenzophenone
[0043] Dibutyl tin diacetate 0.15 parts
[0044] The above-mentioned raw materials are uniformly mixed according to the method of Example 1 to obtain a high-performance acid structural sealant.
Example Embodiment
[0045] Example 3 Take the following components by weight:
[0046] Hydroxy-terminated polydimethylsiloxane 30000 mpa.s 5 parts
[0047] Hydroxy-terminated polydimethylsiloxane 60000 mpa.s 100 parts
[0048] Methyl phenyl silicone oil 100 mpa.s 60 parts
[0049] 5 parts of methyl triacetoxysilane
[0050] Ethyl triacetoxysilane 5 parts
[0051] Fumed silica 170m 2 / g 40 parts
[0052] Fumed silica 220m2 / g 50 parts
[0053] 0.5 parts of hexamethylphosphoric triamide
[0054] 0.1 part of dibutyl tin dilaurate
[0055] The above-mentioned raw materials are uniformly mixed according to the method of Example 1 to obtain a high-performance acid structural sealant.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap