Composite salt-resistant thickening agent, and preparation method and application thereof

A thickener, salt-resistant technology, applied in detergent compounding agents, chemical instruments and methods, detergent compositions, etc. Stability and other issues, to achieve unique salt resistance, high molecular weight, and improve the effect of viscosity

Inactive Publication Date: 2011-03-16
自贡市轻工业设计研究院有限责任公司 +1
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] At present, there is an important problem in common commercially available thickeners for salt-containing daily chemical products: in daily chemical products with high salt content (salt content exceeds 20% in milky daily chemical products), the thickener will be unstable or invalid Or the suspension stability is not ideal, and it cannot achieve the required viscosity, stability, and suspension, so that the product has quality problems such as yellowing, layering, salt sinking, and poor fluidity during the she

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0035] Example 1

[0036] Component percentage content / %

[0037] Xanthan gum 0.15

[0038] Guar gum 0.12

[0039] Sodium alginate 0.03

[0040] AES-70 20

[0041] CAB-35 8

[0042] EDTA-2Na 0.5

[0043] Pearlescent 1.0

[0044] IPS 5

[0045] Glycerin 5

[0046] Salt (60 mesh) 25

[0047] Flavor 0.5

[0048] Water up to 100

[0049] The preparation method of this product is to dissolve xanthan gum, guar gum, and sodium alginate in sequence with water, stir and mix uniformly, heat at 50°C for 60 minutes to form a colloid and cool, add it to the washing product formula, adjust the pH to about 6, add Salt, stir and mix well.

Example Embodiment

[0050] Example 2

[0051] Component percentage content / %

[0052] Xanthan gum 0.21

[0053] Guar gum 0.06

[0054] Sodium alginate 0.03

[0055] AES-70 15

[0056] CAB-35 15

[0057] CMEA 2.0

[0058] IPS 8

[0059] Glycerin 3

[0060] OP301 1.0

[0061] Salt (60 mesh) 38

[0062] Flavor 0.5

[0063] Water up to 100

[0064] The preparation method of this product is to dissolve xanthan gum, guar gum, and sodium alginate in water in sequence, stir and mix uniformly, heat at 60°C for 20 minutes to form a colloid and cool, add it to the washing product formula, adjust the pH to about 7, add Salt, stir and mix well.

Example Embodiment

[0065] Example 3

[0066] Component percentage content / %

[0067] Xanthan gum 0.24

[0068] Guar gum 0.15

[0069] Sodium Alginate 0.09

[0070] AES-NA 8

[0071] APG 4

[0072] MAPK-40 16

[0073] CAB-35 10

[0074] Glycerin 3

[0075] Salt (60 mesh) 30

[0076] Deionized water to 100

[0077] The preparation method of this product is to dissolve xanthan gum, guar gum, and sodium alginate in water in sequence, stir and mix uniformly, heat at 80°C for 10 minutes to form a colloid and cool, add it to the washing product formula, adjust the pH to about 8, add Salt, stir and mix well.

[0078] The composite salt-tolerant thickener system provided by the present invention is applied to the above-mentioned several salt-containing washing product formulations, and has a good thickening effect. The weight ratio of addition is (5-8): (2-5): ( 1~3) The product of the composite thickener is placed in a thermostat at 50°C for 7 days, and placed in a refrigerator at (-10)°C for 2 days. When it is taken o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a composite salt-resistant thickening agent, which belongs to the field of daily chemicals. The composite salt-resistant thickening agent consists of xanthan gum, guar gum and sodium alginate, wherein the weight ratio of the xanthan gum to the guar gum to the sodium alginate is (5-8):(2-5):(1-3); and the composite salt-resistant thickening agent is prepared by the following steps of: dissolving the xanthan gum, the guar gum and the sodium alginate into water in turn; stirring and uniformly mixing; adjusting to the concentration for use by using water; and adjusting pH value to be 6 to 8; and heating at the temperature of between 50 and 80 DEG C for 10 to 60 minutes. The amount of the used thickening agent is 0.01 to 1.0 percent of the weight of the salt-containing daily chemical. The composite salt-resistant thickening agent has acid and alkali resistance, high temperature resistance, anti-freezing effect and does not have toxic or side effect, is excellently matched with a common surfactant (such as sodium alcohol ether sulfate AES, sodium ammonium dodecyl sulfate K12A and the like) in the daily chemical and has the advantages of simple manufacturing process, low technological condition and low comprehensive cost.

Description

technical field [0001] The invention relates to an auxiliary material for daily chemical products, in particular to a composite salt-resistant thickener. Background technique [0002] In recent years, the application of salt (i.e. NaCI) in the field of cosmetics has become more and more extensive. Using the functions of sterilization, disinfection, anti-inflammatory, antipruritic, blood circulation, and cleaning of salt, daily chemical products with different functions can be prepared according to different proportions. These salts Similar daily chemical products are a new generation of household daily chemical products that are pollution-free and non-toxic and side effects that have become popular in the world in recent years. [0003] Adding salt (NaCI) to the formula of daily chemical products has a great influence on the quality stability of the formula. A small amount of salt can thicken the daily chemical products. %) of the salt will destroy the micellar structure fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C11D3/22
Inventor 徐粉燕刘昌辉张小军彭传丰陈俊赵晓晓杨贡林郝莉
Owner 自贡市轻工业设计研究院有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap