Oxygenase-bath alkali-free desizing process for polyester/cotton high-count and high-density fabric

A high-count, high-density, alkali desizing technology, which is applied in the dyeing and finishing process of fabrics, can solve the problems of unsatisfactory hand feeling, many yellow neps in gray fabrics, and high weight loss rate, so as to shorten the production process and save alkali bleaching work Liquid, quality improvement effect

Inactive Publication Date: 2011-04-13
HUAFANG
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the production process, it needs to be stacked for 18 hours, and the fabrics that have undergone the above desizing process have the following quality problems: the handle is not full, the cloth surface is thin, and the weight loss rate is high; the gray fabric has many yellow neps, which cannot be removed cleanly, and the whiteness is not good; Desizing machine alkali spots are not easy to remove after coloring and glazing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The present invention is further described below.

[0016] Production fabric varieties: T / C50×50 40×40+120×90

[0017] The desizing process has the following steps in sequence: seam singeing → three-compartment hot water washing → two-compartment cold water washing → padding and oxygen bleaching working solution → steaming at 102°C for 50 minutes → four-compartment hot water washing → drying → finalizing;

[0018] The formula of the oxygen bleaching working solution used in the padding oxygen bleaching working solution step is:

[0019] High-efficiency refining agent HS-120B: Wuxi Kailai Biotechnology Co., Ltd. 10g / L

[0020] 288 Dispersant Wuxi Kailai Biotechnology Co., Ltd. 65g / L

[0021] Scouring enzyme 188: Wuxi Kailai Biotechnology Co., Ltd. 5g / L

[0022] Wax remover WR: Binzhou Guangda Biotechnology Co., Ltd. 5g / L

[0023] Hydrogen peroxide stabilizer P: Kekai Fine Chemicals (Shanghai) Co., Ltd. 10g / L

[0024] Hydrogen peroxide (concentration is 33%) Jinan Lu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
whitenessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an oxygenase-bath alkali-free desizing process for a polyester / cotton high-count and high-density fabric. The process sequentially comprises the following steps of: sewing and singeing the fabric; washing the fabric with three-grid hot water; washing the fabric with two-grid coldwater; padding oxidation bleaching working solution; steaming at the temperature of 102 DEG C for 50 minutes; washing the fabric with four-grid hot water; drying; and shaping, wherein in the step of padding oxidation bleaching working solution, the formula of the oxidation bleaching working solution comprises 10g / L of high-efficient scouring agent HS-120B, 65g / L of 288 dispersing agent, 5g / L of scouring enzyme 188, 5g / L of wax regent WR, 10g / L of hydrogen peroxide stabilizing agent P and 14.0 to 15.0g / L of hydrogen peroxide (wherein the concentration is 33 percent). Compared with the prior art, the desized fabric has greatly improved quality, namely the handfeel is plump; the fabric surface loss ratio is low; the fabric surface whiteness is good; and the fabric has no cotton, multiple nodes and no alkaline spots.

Description

technical field [0001] The invention relates to a fabric dyeing and finishing process, in particular to an enzyme-oxygen one-bath alkali-free desizing process for polyester-cotton high-count and high-density fabrics. Background technique [0002] Polyester fiber has the characteristics of good strength, body, and poor hygroscopicity, while cotton fiber has the characteristics of softness, heat preservation, and excellent hygroscopicity. Polyester-cotton high-count and high-density fabric has a high density and a thick fabric feel. It has the advantages of both polyester and cotton fibers. The garments made are not deformed, have a body, are soft, moisture-absorbing, wear-resistant, and are comfortable to wear. They are very suitable for use in Make tooling fabrics. The warp yarns of fabrics such as cotton, viscose and synthetic fibers are mostly sizing before weaving. Sizing affects fabric wettability during dyeing and finishing and hinders chemical contact with fibers. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06L3/02D06L3/11D06L1/14D06L1/16D06L4/12D06L4/13D06L4/40
Inventor 王力民罗维新李春光刘涛吕建品
Owner HUAFANG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com