Tape base paper and production method thereof
A production method and adhesive tape technology, applied in paper, papermaking, paper machines, etc., can solve the problems of affecting product performance, high production cost, high beating degree, etc., achieve the effect of reducing beating degree, guaranteed source, and improving kappa value
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0016] Example 1:
[0017] After preparing materials, 60 parts by weight of masson pine, 20 parts by weight of hardwood, and 20 parts by weight of cedar edge boards are prepared by using low-energy displacement cooking and closed washing to make chemical natural wood pulp with a Kappa number of 40. After oxygen-alkali delignification and hydrogen peroxide bleaching, the whiteness of the slurry is 19% (ISO). The slurry is adjusted to a concentration of 3.4%, the slurry is beaten to 27°SR, and the wet weight is 12g. After dilution, the sand is removed, the online concentration is controlled to 0.25%, the online pH value: 6.5, after the pressure screen, the PEA wet strength agent seasoning with the absolute dry weight ratio of 1% to the pulp, the fourdrinier paper machine forming, pressing, drying, Coiling, rewinding, and packaging into finished products.
[0018] The oxygen delignification and hydrogen peroxide bleaching process includes oxygen delignification time 60 minutes, slurr...
Example Embodiment
[0020] Example 2:
[0021] After preparing materials, 50 parts by weight of masson pine, 30 parts by weight of hardwood, and 25 parts by weight of cedar edge boards are prepared by DDS displacement cooking and closed washing to make chemical natural wood pulp with a kappa value of 50. After oxygen-alkali delignification and hydrogen peroxide bleaching, the whiteness of the slurry is 26% (ISO). The slurry is adjusted to a concentration of 3.0%, the slurry is beaten to 29°SR, and the wet weight is 12.3g. After dilution, remove sand, control the online concentration to 0.22%, and the online pH value: 6.1. After the pressure sieve, the PEA wet strength agent seasoning with the absolute dry weight ratio of 4% to the pulp is used. Fourdrinier paper machine molding, pressing, and extensibility Compression, drying, coiling, rewinding, and packaging into finished products.
[0022] Oxygen delignification and hydrogen peroxide chlorine-free bleaching process is 80 minutes for oxygen deligni...
Example Embodiment
[0024] Example 3:
[0025] 55 parts by weight of masson pine, 25 parts by weight of hardwood, 10 parts by weight of cedar edge boards, and 10 parts by weight of plywood processing residues, after preparing materials, use DDS replacement cooking, closed washing and sieving to make a Kappa number 42 Chemical natural wood pulp. After the pulp has been delignified by oxygen and alkali and bleached by hydrogen peroxide, the whiteness of the pulp will be 27% (ISO). The pulp will be adjusted to a concentration of 4.4%, and the pulp will be beaten to 32°SR, wet The weight is 14g, the slurry is diluted and de-sanded, the online concentration is controlled to 0.2%, the online pH value: 6, after the pressure sieve, the PEA wet strength agent seasoning with the absolute dry weight ratio of 8% to the pulp, Fourdrinier paper machine Forming, pressing, extensible compression, drying, coiling, rewinding, and packaging into finished products.
[0026] Oxygen delignification and hydrogen peroxide c...
PUM
Property | Measurement | Unit |
---|---|---|
Tensile strength | aaaaa | aaaaa |
Tightness | aaaaa | aaaaa |
Wet strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap