Environmental-friendly casein insulating paste

A technology of insulating glue and casein, which is applied in the direction of adhesives, non-polymer adhesive additives, adhesive additives, etc., can solve problems affecting health, synthetic glue pollutes the environment, and achieves the effect of not polluting the environment

Inactive Publication Date: 2011-07-13
甘肃省商业科技研究所有限公司
View PDF1 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a healthy and environment-friendly casein insulating glue to solve the problem that the existing synthetic glue pollutes the environment and affects health.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] (a) dissolve

[0028] Weigh 100kg of casein and add it to the reaction kettle, then add 500kg of water and stir evenly, then add NaOH solution with a mass percentage concentration of 15%, adjust the pH value to 7.5, and heat up while stirring. When the temperature reaches 55°C, the solution as a whole is Colloidal, keep stirring at constant temperature until the casein particles are completely dissolved;

[0029] (b) Add excipients

[0030] In the colloidal solution dissolved in step (a), add 50kg methyl acrylate, 100kg starch, 10kg zinc oxide, 150kg urea, 10kg dimethyl silicon oxide oil, 30kg paraffin oil and 50kg ethylparaben in sequence, stirring Raise the temperature, when the added auxiliary materials are completely dissolved, the temperature of the colloidal solution is raised to 80°C, and the constant temperature stirring is continued for 30 minutes, and the final pH value of the colloidal solution is kept at 7.5;

[0031] (c) cool down

[0032] Stop heating t...

Embodiment 2

[0039] (a) dissolve

[0040] Weigh 150kg of casein and add it to the reaction kettle, then add 600kg of water and stir evenly, then add NaOH solution with a mass percentage concentration of 15%, adjust the pH value to 7.8, and heat up while stirring. When the temperature reaches 60°C, the solution as a whole is Colloidal, keep stirring at constant temperature until the casein particles are completely dissolved;

[0041] (b) Add excipients

[0042] In the colloidal solution dissolved in step (a), add 75kg ethyl acrylate, 150kg starch, 15kg zinc oxide, 175kg urea, 25kg dimethyl silicon oxide oil, 50kg paraffin oil and 75kg ethylparaben in sequence, stirring Raise the temperature, when the added auxiliary materials are completely dissolved, the temperature of the colloidal solution is raised to 83°C, and the constant temperature stirring is continued for 40 minutes, and the final pH value of the colloidal solution is kept at 7.8;

[0043] (c) cool down

[0044] Stop heating th...

Embodiment 3

[0052] (a) dissolve

[0053] Weigh 300kg of casein and add it to the reaction kettle, then add 700kg of water and stir evenly, then add NaOH solution with a mass percentage concentration of 15%, adjust the pH value to 8.0, and heat up while stirring. When the temperature reaches 65°C, the solution as a whole is Colloidal, keep stirring at constant temperature until the casein particles are completely dissolved;

[0054] (b) Add excipients

[0055] In the colloidal solution dissolved in step (a), add 100kg propyl acrylate, 300kg starch, 30kg zinc oxide, 350kg urea, 50kg dimethyl silicon oxide oil, 70kg paraffin oil and 100kg ethylparaben in sequence, while stirring Raise the temperature, when the added auxiliary materials are completely dissolved, the temperature of the colloidal solution is raised to 85°C, and the constant temperature stirring is continued for 45 minutes, and the final pH value of the colloidal solution is kept at 8.0;

[0056] (c) cool down

[0057] Stop h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Conductivityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environmental-friendly casein insulating paste, which is prepared by adopting the steps of: adding water in casein for dissolving, regulating pH value to 7.5-8.0, enabling a solution to be integrally shaped as a colloid when stirring and raising the temperature to 55-65 DEG C, and continuously stirring at constant temperature until casein particles are completely dissolved; sequentially adding acrylate, starch, zinc oxide, urea, dimethyl oxidized silicone oil, paraffin oil and ethylparaben, stirring and raising temperature; after auxiliary materials are completely dissolved, raising the temperature to 80-85 DEG C, stirring at constant temperature for 30-45min, and keeping pH value between 7.5 and 8.0; reducing the temperature to 35-40 DEG C, and filtering to obtain milk white or light yellow uniform semi-transparent viscous fluid without impurities; and packaging, closely storing, and placing and ageing for 24-72h at normal temperature to obtain a finished product of the environmental-friendly casein insulating paste. The environmental-friendly casein insulating paste is prepared from the raw material of casein in the milk, has the characteristics of no toxicity, no taste, easy degradation, no pollution to environment, and the like, can be used for replacing chemically synthesized glue of epoxy resins, urea-formaldehyde resin adhesives, amino resins, polyvinyl alcohols, and the like, and can be widely applied to fields of electric appliances, laminated plates and the like.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to an environment-friendly casein insulating adhesive produced from casein. Background technique [0002] At present, epoxy resin glue, silicone resin glue, nitrile-phenolic resin glue, urea-formaldehyde resin glue, amino resin and white latex are mainly used in the field of domestic insulating glue and laminated board. Resin glue and amino resin, the specific process is as follows: ①In neutral or weakly alkaline (pH=7~8) medium, urea and formaldehyde undergo methylolation reaction (addition reaction), which can produce Hydroxymethylurea. ②Carry out polycondensation reaction under acidic conditions. When the molecular weight reaches a certain level, adjust the pH value of the reaction solution to 8-9, and cool down to normal temperature to obtain the initial condensation liquid of urea-formaldehyde resin. Synthesize urea-formaldehyde resin under such strong acidic conditions The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J4/02C09J4/06C09J11/04C09J11/06
Inventor 牛犇
Owner 甘肃省商业科技研究所有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com