Antibacterial fiber, its preparation method and pillow and quilt containing the antibacterial fiber

A technology of antibacterial fiber and pillow core, applied in the field of pillow core and quilt core, can solve problems such as unsuitable for industrialized large-scale production and safety performance problems.

Active Publication Date: 2011-12-07
SHANGHAI SHUIXING HOME TEXTILE
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] One of the technical problems to be solved by the present invention is to provide an antibacterial fiber to overcome the sa...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The antibacterial fiber contains 20% chitosan, 3% sodium polyacrylate PAAS, 5% acetic acid, 2%-maleic anhydride and PET in the weight percentage.

[0029] The method for antibacterial fiber, comprises the following steps:

[0030] (1) preparation contains chitosan eutectic composition

[0031] In terms of weight percentage, mix 20% chitosan, 3% sodium polyacrylate PAAS, 5% acetic acid, 2% maleic anhydride and part of PET, and knead at 170-200°C to obtain a chitosan co-melt combination. The material is then cooled and discharged, and crushed by a plastic crusher to a chitosan-containing eutectic composition powder below 5 mm for subsequent use; wherein the weight ratio of chitosan to PET is 1: 2.5;

[0032] (2) Prepare chitosan-containing antibacterial masterbatch, mix the chitosan-containing eutectic composition powder prepared in step 1 with PET in a weight ratio of 1-3, melt and co-extrude through a co-rotating twin-screw extruder, water-cool, and cut Granules, drie...

Embodiment 2

[0036] The antibacterial fiber contains 25% chitosan, 4% sodium polyacrylate PAAS, 7% acetic acid, 3%-maleic anhydride and PET in the weight percentage.

[0037] The method for antibacterial fiber, comprises the following steps:

[0038] (1) preparation contains chitosan eutectic composition

[0039] In terms of weight percentage, mix 25% chitosan, 4% sodium polyacrylate PAAS, 7% acetic acid, 3%-maleic anhydride and part of PET, and knead at 170-200°C to obtain chitosan co-melting The composition is then cooled and discharged, and pulverized by a plastic crusher to a chitosan-containing eutectic composition powder below 5 mm for subsequent use; wherein the weight ratio of chitosan to PET is 1: 2.5;

[0040] (2) Preparation of chitosan-containing antibacterial masterbatch

[0041] Mix the chitosan-containing co-melt composition powder prepared in step 1 with PET in a weight ratio of 1-3, melt and co-extrude through a co-rotating twin-screw extruder, water-cool, pelletize, and...

Embodiment 3

[0045] The antibacterial fiber contains 30% chitosan, 5% sodium polyacrylate PAAS, 10% acetic acid, 5%-maleic anhydride and PET in the weight percentage.

[0046] The method for antibacterial fiber, comprises the following steps:

[0047] (1) preparation contains chitosan eutectic composition

[0048] In terms of weight percentage, mix 30% chitosan, 5% sodium polyacrylate PAAS, 10% acetic acid, 5%-maleic anhydride and part of PET, and knead at 170-200°C to obtain chitosan co-melting The composition is then cooled, discharged, and pulverized by a plastic crusher to a chitosan-containing eutectic composition powder below 5 mm for subsequent use; wherein the weight ratio of chitosan to PET is 1: 2.5;

[0049] (2) Preparation of chitosan-containing antibacterial masterbatch

[0050] Mix the chitosan-containing co-melt composition powder prepared in step 1 with PET in a weight ratio of 1-3, melt and co-extrude through a co-rotating twin-screw extruder, water-cool, pelletize, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Loftaaaaaaaaaa
Air permeabilityaaaaaaaaaa
Login to view more

Abstract

The invention provides an antibiotic fiber. The antibiotic fiber comprises, by weight, 20-30% of chitosan, 3-5% of a dispersant, 5-10% of a fusogen, 2-5% of a grafting modifier, and the balance PET. The invention also provides a preparation method of the antibiotic fiber, and a pillow core and a quilt core containing the antibiotic fiber as a filling material. Present antibiotic products have safety performance problems and defects which are not adapted to industrial production, so the antibiotic fiber of the invention which can highly effectively inhibit more than twenty harmful bacteria of escherichia coli, staphylococcus aureus, Candida albicans and the like with an average bacteriostasis rate of equal to or more than 98%, and can not generate side effects to beneficial flora in human bodies has the effect of ecological bacteriostasis, and is adapted to industrial production.

Description

technical field [0001] The invention relates to an antibacterial fiber, a preparation method thereof, a pillow core and a quilt core containing the antibacterial fiber. Background technique [0002] At present, most of the fiber raw materials used in the textile products of underwear, hosiery and bedding in the world are cotton fibers or blended with other chemical fibers. These fibers do not have a good function of inhibiting and killing bacteria. After entering the 21st century, people put forward higher requirements for home textile products such as underwear, hosiery, bedding, etc.: moisture guide, water absorption, perspiration, antibacterial, personal comfort and hygiene, while the existing These cotton fibers or blended products with other chemical fibers cannot meet these needs. [0003] The macromolecular structure of PET fiber itself has strong antimicrobial properties, but because it will be "contaminated" with various oils, auxiliaries and finishing agents durin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F6/92D01F1/10D01D5/08B29B9/06B29C47/92A47G9/10A47G9/00B29C48/92
CPCB29C48/04B29C48/40B29C48/875B29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895
Inventor 沈义贵梅山标袁波舒朝夕
Owner SHANGHAI SHUIXING HOME TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap