Manufacturing method of X65 pipeline steel longitudinal submerged arc welded pipe for undersea use
A technology of straight seam submerged arc and manufacturing method, applied in manufacturing tools, arc welding equipment, welding equipment, etc., can solve problems such as destructive damage and leakage of production environment in sea areas, and achieve the effect of ensuring performance, uniform performance and uniform deformation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0032] Example 1
[0033] The pipe diameter is Φ762, the wall thickness is 28.6mm, the chemical composition is C 0.06%, Mn 1.61%, Si 0.19%, S 0.0012%, P 0.007%, Mo ≤0.098%, Ni+Cr+Cu 0.157%, V+ Nb+Ti 0.062%, N 0.005%, Ceq 0.36, Pcm 0.15 X65 controlled-rolled steel plate is used to manufacture LSAW pipes. The manufacturing process is as follows:
[0034] Milling: After milling, the steel plate conforms to the upper and lower bevel angle of 35°, and the height of the blunt edge is 9mm.
[0035] Pre-bending: Use a pre-bending machine to pre-bend the edge of the plate, and make the edge of the plate have the required curvature according to the requirements of the pipe diameter.
[0036] JCO forming: adopts the method of gradual pressing, the steel plate is fed by 134mm each time, first half of the steel plate is pressed into a "J" shape after 7 times, and the other half is pressed in the same way to form a "C" shape. Press in the middle to make the entire steel plate pressed into an open ...
Example Embodiment
[0060] Example 2
[0061] The pipe diameter is Φ762, the wall thickness is 30.2mm, the chemical composition is C 0.07%, Mn 1.58%, Si 0.31%, S 0.001%, P 0.007%, Mo ≤0.014%, Ni+Cr+Cu 0.216%, V+ X65 controlled-rolled steel plates with Nb+Ti 0.046%, N 0.004%, Ceq 0.40, Pcm 0.18 are used to manufacture LSAW pipes. The manufacturing process is as follows:
[0062] Milling: After milling, the steel plate meets the upper and lower bevel angle of 35°, and the height of the blunt edge is 9.0mm.
[0063] Pre-bending: Use a pre-bending machine to pre-bend the edge of the plate, and make the edge of the plate have the required curvature according to the requirements of the pipe diameter.
[0064] JCO forming: adopts the method of gradual pressing, the steel plate is fed by 134mm each time, first half of the steel plate is pressed into a "J" shape after 7 times, and the other half is pressed in the same way to form a "C" shape. Press in the middle to make the entire steel plate pressed into an ope...
PUM
Property | Measurement | Unit |
---|---|---|
Wall thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap