Method for producing plastic product and plastic product

A plastic product and plastic technology, which is applied in the direction of chemical instruments and methods, layered products, superimposed layer plating, etc., can solve the problems of complex metallization process on the plastic surface, poor adhesion between the plating layer and the plastic substrate, and high energy requirements

Active Publication Date: 2012-02-08
BYD CO LTD
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The invention aims to solve the technical problems of complex plastic surface metallization process, high energy requirements, and poor adhesion between the coating and the plastic substrate in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0014] The present invention provides a method for preparing plastic products, including the following steps:

[0015] 1) Molded plastic matrix; the plastic matrix is ​​a thermoplastic or thermosetting plastic containing an electroless plating accelerator, and the electroless plating accelerator is evenly distributed in the thermoplastic or thermosetting plastic; the electroless plating accelerator is Ni 2 O 3 , Co 2 O 3 , CuSiO 3 , CuC 2 O 4 One or more of Cu / Fe / Mn or Cu / Fe / Al ternary co-sintered oxide, Cu / Fe / Al / Mn quaternary co-sintered oxide;

[0016] 2) Laser vaporizes the surface of the plastic substrate, exposing the electroless plating accelerator;

[0017] 3) In step 2), electroless copper or electroless nickel plating is performed on the surface of the electroless plating accelerator, and the electroless plating and / or electroplating is continued at least once to form a metal layer on the surface of the plastic substrate.

[0018] The inventors of the present invention found t...

Embodiment 1

[0047] (1) Put CuC 2 O 4 ·2H 2 O, vacuum drying to remove crystal water, ball milling to D50 below 1μm, dry; the PP resin, CuC 2 O 4 、Talc powder and antioxidant 1010 according to the mass ratio of 100:15:10:0.2 are mixed with a high mixer, and then extruded into a pipe with a single screw extruder (Nanjing Rubber and Plastic Machinery Factory), and the extrusion temperature is 180℃ .

[0048] (2) An infrared laser (Ted, DPF-M12) is used to irradiate the outer surface of the entire tube. The laser parameters are: wavelength 1064nm, scanning speed 1000mm / s, step length 9μm, delay 30μs, frequency 40KHz, power 3W, filling spacing 50μm; clean the surface of the pipe.

[0049] (3) Immerse in the electroless copper plating solution for 3 hours to form a copper layer with a thickness of 10μm, immerse in the electroless nickel plating solution for 10 minutes, and form a nickel layer with a thickness of 3μm outside the copper layer; electroless copper plating solution: CuSO 4 ·5H 2 O 0.12mo...

Embodiment 2

[0052] The plastic product of this embodiment is prepared by the same method as in embodiment 1, except that:

[0053] In step (1), the CuSiO 3 Ball mill to D50 of 2μm or less, dry; PC resin, CuSiO 3 , Antioxidant 168 and EVA wax are mixed according to the mass ratio of 100:20:0.2:0.1, then extruded and pelletized and then injection molded into the electrical shell;

[0054] In step (2), an infrared laser is used to print a metal circuit pattern on the electrical appliance housing; after the laser vaporization is completed, the electrical appliance housing is ultrasonically cleaned;

[0055] In step (3), the sequence of electroless plating is: first electroless nickel plating for 10 minutes to form a 3 μm thick nickel layer, then electroless copper plating for 3 hours to form an 11 μm thick copper layer, and finally electroless nickel plating for 10 minutes to form a 3 μm thick nickel layer.

[0056] Through the above steps, the plastic product used as the housing of the electrical app...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for producing a plastic product and the plastic product. The production method comprises the following steps: 1) forming a plastic substrate, wherein the plastic substrate comprises a chemical plating enhancer which is one or more selected from Ni2O3, Co2O3, CuSiO3, CuC2O4, Cu / Fe / Mn or Cu / Fe / Al ternary co-sintering oxide, Cu / Fe / Al / Mn quaternary co-sintering oxide; 2) laser gasificating the surface of the plastic substrate, exposing the chemical plating enhancer; 3) performing chemical copper plating or chemical nickel plating, continuously carrying out a chemical plating and / or electroplating, forming a metal layer on the surface of the plastic substrate. The method of the invention has the advantages of simple process, low energy requirement and low cost; in addition, the chemical plating enhancer is distributed in the plastic substrate, thereby a plating layer formed by chemical plating has high binding force with the plastic substrate.

Description

[0001] Related application [0002] This application is a divisional application of a Chinese invention patent application with an application number of 200910238957.9, an application date of December 30, 2009, and an invention title of "a method for preparing a plastic product and a plastic product". Technical field [0003] The invention belongs to the field of surface metallization of non-metallic materials, and in particular relates to a preparation method of a plastic product and a plastic product. Background technique [0004] A metal layer is formed on the plastic surface as a path for electromagnetic signal transmission, which is widely used in automobiles, industry, computers, communications and other fields. The selective formation of a metal layer on the plastic surface is a core link in the manufacture of such plastic products. There are many methods for plastic surface metallization production lines. In the prior art, a metal core is formed on the surface of a plastic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C28/02C23C18/31C23C18/20C25D5/10B32B15/01
Inventor 宫清周良苗伟峰张雄
Owner BYD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com