Nano zirconia alcohol slurry and preparation method thereof

A technology of nano-zirconia and slurry, applied in chemical instruments and methods, mixing methods, dissolution, etc., can solve the problems of complex preparation, affecting the use effect and performance of powder, high production cost, etc., and achieve low light transmittance and practical Great value, easy-to-manipulate effects

Inactive Publication Date: 2012-02-15
BEIJING NACHEN TECH DEV
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The preparation of this method is relatively complicated, and the powder needs to be coated. The coating process introduces other substances on the surface of the powder, which affects the use effect and performance of the powder.
In addition, a high-speed disperser is required for dispersing and then grinding, and the production cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A nanoscale ZrO 2 Ethanol slurry, by weight (g) of the nanoscale ZrO 2 The slurry consists of the following components: Nanoscale ZrO with a particle size of 20 nm 2 The powder is 30, the polyethylene glycol 800 is 2, and the ethanol is 95;

[0029] The preparation method of the above-mentioned nano-aluminum slurry comprises the following steps:

[0030] (1) Polyethylene glycol 800 is added to ethanol according to the proportioning, stirring is uniform;

[0031] (2) Nanoscale ZrO 2 The powder is put into the above-mentioned mixed solution;

[0032] (3) The ball mill is dispersed for 30 minutes, and the finished slurry is made;

[0033] (4) Remove the ball mill tank, pour out the slurry through the sieve, and leave the grinding balls on the sieve.

[0034] The prepared slurry is a white emulsion, and the light transmittance of the slurry is determined to be 19% by an ultraviolet-visible spectrophotometer. Take 20ml of slurry and pour it into a test tube. The inner...

Embodiment 2

[0036] A nanoscale ZrO 2 Ethylene glycol slurry, by weight (g) of the nanoscale ZrO 2 The slurry consists of the following components: Nanoscale ZrO with a particle size of 10 nm 2 The powder is 1, N-(β-aminoethyl)-γ-aminopropyltrimethyl(eth)oxysilane is 0.05, and ethylene glycol is 95;

[0037] The preparation method of the above-mentioned nano-aluminum slurry comprises the following steps:

[0038] (1) N-(β-aminoethyl)-γ-aminopropyltrimethyl(eth)oxysilane is added to ethylene glycol according to the proportion, and stirred evenly;

[0039] (2) Nanoscale ZrO 2 The powder is put into the above-mentioned mixed solution;

[0040] (4) The ball mill is dispersed for 30 minutes, and the finished slurry is made;

[0041] (4) Remove the ball mill tank, pour out the slurry through the sieve, and leave the grinding balls on the sieve.

[0042] The prepared slurry is a white emulsion, and the light transmittance of the slurry is determined to be 15% by an ultraviolet-visible spect...

Embodiment 3

[0044] A nanoscale ZrO 2 Isopropanol slurry, by weight (g) the nanoscale ZrO 2 The slurry consists of the following components: Nanoscale ZrO with a particle size of 20 nm 2 The powder is 25, the dispersant kp110 is 2, and the isopropanol is 85; the chemical composition of the dispersant kp110 is a modified carboxylic acid polymer, Shanghai Deyude Trading Co., Ltd.;

[0045] The preparation method of above-mentioned slurry, comprises and is made up of the following steps:

[0046] (1) adding dispersant kp110 to isopropanol by proportioning, stirring uniformly;

[0047] (2) Nanoscale ZrO 2 The powder is put into the above-mentioned mixed solution;

[0048] (3) The ball mill is dispersed for 40 minutes, and the finished slurry is made;

[0049] (4) Remove the ball mill tank, pour out the slurry through the sieve, and leave the grinding balls on the sieve.

[0050] The prepared slurry is a white emulsion, and the light transmittance of the slurry is determined to be 16% by an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a nano zirconia alcohol slurry and a preparation method thereof. The nano zirconia alcohol slurry comprises, by weight, 1-60 parts of nanometer level ZrO2 powder, 0.05-10 parts of dispersant and 30-99 parts of solvent. The preparation method is as below: the dispersant is added and dissolved in the organic solvent; then the nanometer level ZrO2 powder is added in the mixture and dispersed by a high speed bowl mill for 0.2-10 h, so as to obtain the oil slurry. The technology of the invention is simple, has a short processing time, easily controlled process and high application value. The nano zirconia slurry prepared by the invention is a highly decentralized, uniformized and stabilized slurry, can be widely applied to fields of high strength and high-toughness wear resistant product, functional ceramic, structural ceramic, electric device and refractory material, etc.

Description

technical field [0001] The invention relates to a nanometer material and a preparation method thereof, in particular to a nanometer zirconia oily slurry and a preparation method thereof. Background technique [0002] Nano-zirconia is an important inorganic functional material, which is widely used in precision structural ceramics, functional ceramics, nano-catalysts, solid fuel cell materials, functional coating materials, advanced refractories, optical fiber connectors, mechanical ceramic seals, high Wear-resistant ceramic balls, nozzles, spray sheets and other industrial fields. However, due to the small size of nano-zirconia powder particles, there are stronger interaction forces between particles than micron-sized powders, such as electrostatic force, van der Waals force, capillary force, mechanical entanglement force, etc. Due to the disadvantages of poor fluidity, the nanoparticles cannot be well dispersed, which seriously affects the performance of the powder. For e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01F3/12B02C17/00
Inventor 刘艳翟金玲桂莹芳张波张蕾谷星雪方进轩
Owner BEIJING NACHEN TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com