Preparation method of modified fly ash for treating ammonia nitrogen waste water

A technology of ammonia nitrogen wastewater and fly ash, which is applied in chemical instruments and methods, adsorption water/sewage treatment, water/sludge/sewage treatment, etc., can solve the problems of low adsorption performance of fly ash and less research, etc. Achieve the effect of good ammonia nitrogen removal effect, wide source of raw materials, and reduce the cost of raw materials

Inactive Publication Date: 2012-02-22
HUAQIAO UNIVERSITY
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Fly ash has a special spatial structure of Al-O tetrahedron and Si-O tetrahedron, with negative charges on the surface and ion exchange performance. However, the adsorption performance of the original fly ash is not high, and it needs to be modified to improve the adsorption performance
At present, the modification methods of fly ash mainly include acid modification, alkali modification, salt modification,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Put the raw material fly ash (10μm-300μm) in 0.5 mol / liter sodium hydroxide solution, make the solid-liquid ratio 1:10, soak for 10 hours at the reaction temperature of 90°C, then use soft water to remove calcium and magnesium Wash and dry to obtain modified fly ash.

[0017] Ammonia nitrogen wastewater (pH value is 7, ammonia nitrogen content is more than 150mg / liter) flows through the device equipped with the modified fly ash obtained in embodiment 1, the ammonia nitrogen in the wastewater can be removed, and the ammonia nitrogen removal rate can reach more than 80% .

Embodiment 2

[0019] Put the raw material fly ash (10m-300μm) in a 5 mol / L sodium hydroxide solution to make the solid-liquid ratio 1:5, soak it at a reaction temperature of 50°C for 5 hours, and then use soft water to remove calcium and magnesium Wash and dry to obtain modified fly ash.

[0020] Ammonia nitrogen wastewater (pH value is 5, ammonia nitrogen content is more than 80mg / liter) flows through the device equipped with the modified fly ash obtained in Example 2, the ammonia nitrogen in the wastewater can be removed, and the ammonia nitrogen removal rate can reach more than 75%. .

Embodiment 3

[0022] Put the raw material fly ash (10m-300μm) in 8 mol / L sodium hydroxide solution so that the solid-liquid ratio is 1:3, after soaking for 0.5 hours at a reaction temperature of 10°C, use soft water to remove calcium and magnesium Wash and dry to obtain modified fly ash.

[0023] Ammonia nitrogen wastewater (pH value is 10, ammonia nitrogen content is more than 250mg / liter) flows through the device equipped with the modified fly ash obtained in embodiment 3, the ammonia nitrogen in the wastewater can be removed, and the ammonia nitrogen removal rate can reach more than 88%. .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of modified fly ash for treating ammonia nitrogen waste water. The preparation method comprises the following steps of immersing a raw material of fly ash in 0.5 to 8 mol/L of a sodium hydroxide solution for 0.5 to 10 hours under the conditions of a temperature of 10 to 90 DEG C and a solid-liquid ratio of 1: (2 to 10); washing by soft water which does not contain calcium and magnesium, and drying to obtain the modified fly ash. When ammonia nitrogen waste water flows through a device loaded with the modified fly ash, ammonia nitrogen in the ammonia nitrogen waste water can be removed and an ammonia nitrogen removal rate reaches above 75%.

Description

technical field [0001] The invention relates to a modified fly ash which can be used to treat wastewater containing ammonia nitrogen, in particular to a preparation method of the modified fly ash. Background technique [0002] The discharge of ammonia nitrogen wastewater is a major source of pollution in nitrogen fertilizer plants. After a large amount of ammonia nitrogen wastewater is injected into rivers and lakes, it will cause eutrophication in a large area of ​​natural ecology, which not only destroys the ecological balance, but also brings great difficulties to the pretreatment of industrial water due to serious water pollution in some areas. At present, the treatment methods of ammonia nitrogen wastewater include biological method, break point chlorination method and adsorption method. The biological method has very high requirements in actual production, and the denitrification effect is not stable enough; the breakpoint chlorination method needs to add a large amou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/10B01J20/30C02F1/28C02F101/16
Inventor 李宝霞翁连进陈婉妹
Owner HUAQIAO UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap