Polyamide resin capacitor aluminium shell film mulching paint and its preparation method
A technology of polyamide resin and capacitor, applied in the direction of polyamide paint and coating, can solve the problems of high production cost and poor temperature resistance, and achieve the effect of increasing service life, reasonable formula and good curing effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0011] Example 1: Polyamide resin capacitor aluminum shell film coating, the weight parts of its raw materials are: comprising composition A and composition B, described composition A: 60 parts of polyamide resin, 20 parts of ketone, 5 parts of polyethylene wax , 15 parts of nano carbon powder, 5 parts of ethanol, 15 parts of glycerol and 10 parts of attapulgite; described composition B: 20 parts of acrylate copolymer modifier, 5 parts of silane coupling agent, graphite powder 5 parts and 5 parts of tetramethylsilane.
[0012] The preparation method of polyamide resin capacitor aluminum shell film coating, comprises the following steps:
[0013] (1) Weigh each raw material according to the weight of the constituent raw materials, add polyamide resin, ketone, polyethylene wax, nano carbon powder, ethanol, glycerin and attapulgite into the mixer, and stir at room temperature for 30-45 minutes, Mix uniformly to obtain composition A, then add acrylate copolymer modifier, silan...
Embodiment 2
[0016] Example 2: Polyamide resin capacitor aluminum shell film coating, the weight parts of its raw materials are: including composition A and composition B, the composition A: 70 parts of polyamide resin, 30 parts of ketone, 10 parts of polyethylene wax , 25 parts of nano carbon powder, 15 parts of ethanol, 25 parts of glycerol and 15 parts of attapulgite; described composition B: 30 parts of acrylate copolymer modifier, 10 parts of silane coupling agent, graphite powder 10 parts and 10 parts of tetramethylsilane.
[0017] The preparation method of polyamide resin capacitor aluminum shell film coating, comprises the following steps:
[0018] (1) Weigh each raw material according to the weight of the constituent raw materials, add polyamide resin, ketone, polyethylene wax, nano carbon powder, ethanol, glycerin and attapulgite into the mixer, and stir at room temperature for 30-45 minutes, Mix uniformly to obtain composition A, then add acrylate copolymer modifier, silane c...
Embodiment 3
[0021] Example 3: Be coated with embodiment 1 and embodiment 2 polyamide resin capacitor aluminum casing film-coated paint, wherein curing temperature, time and the capacitor film-coated aluminum casing technical index that gained film-coated aluminum casing are made are:
[0022] Example 1 Example 2 Curing temperature (°C) 198 216 Curing time (s) 60 60 Requirement index conform to conform to aspect ratio 2.6:1 3.2:1
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com