Method for preparing self-thermal-insulation concrete building block

A technology of concrete blocks and thermal insulation concrete, which is applied in the manufacture of tools, ceramic products, applications, etc., can solve the problems of high cost, inconvenient construction, and lack of popularization and application, and achieve the effect of strong adaptability and elimination of thermal bridges

Inactive Publication Date: 2012-06-13
徐州东兴能源有限公司
View PDF6 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The implementation of building insulation is a major measure for energy saving and emission reduction and sustainable development in the future. Its development direction is self-insulation. However, due to the defects of various self-insulation building block products: either the structure is not good, or the structure itself is complex and costl

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing self-thermal-insulation concrete building block
  • Method for preparing self-thermal-insulation concrete building block
  • Method for preparing self-thermal-insulation concrete building block

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (1) Fabrication of the main thermal insulation concrete frame:

[0034] Stir and mix the coarse aggregate, fine aggregate, cementing material I, and water. The coarse aggregate is composed of sludge ceramsite and ordinary stones. The sludge dry basis content in the preparation of sludge ceramsite is 30%. The volume ratio of sludge ceramsite to gravel is 1:1, the volume ratio of coarse and fine aggregates is 2:1, and the fine aggregate is river sand. The cementing material I is composed of cement and granular calcium silicate nanofibers, and the cement is labeled 42.5MPa Ordinary Portland cement, the content of granular calcium silicate nanofibers is 0.1wt% of cementing material Ⅰ, and the mass ratio of water to cementing material Ⅰ is 0.4. Before the above concrete ingredients are stirred, the granular calcium silicate nanofibers are treated with sodium methyl siliconate for hydrophobic treatment, and then the cement and the granular calcium silicate nanofibers are ...

Embodiment 2

[0040] (1) Fabrication of the main thermal insulation concrete frame:

[0041] Stir and mix the coarse aggregate, fine aggregate, cementing material I, and water, among which the coarse aggregate is composed of inflamed ceramsite and ordinary stones. The cylinder compressive strength of incinerated ceramsite is 4.5MPa, and the bulk density is 600Kg / m 3 , the volume ratio of swelled ceramsite to stone is 3:1, the volume ratio of coarse and fine aggregate is 2:1, the fine aggregate is composed of river sand and pottery sand, the particle size of pottery sand is 0.5mm~2mm, river sand and pottery sand The volume ratio of sand is 1:1. The cementing material I is composed of 32.5MPa slag Portland cement and granular calcium silicate nanofibers. The content of granular calcium silicate nanofibers is 2.5% of the mass of cementing material I. Water The mass ratio to cementing material I is 0.5. Before the above concrete is mixed, the granular calcium silicate nanofibers are trea...

Embodiment 3

[0047] (1) Fabrication of the main thermal insulation concrete frame:

[0048] Stir and mix coarse aggregate, fine aggregate, cementing material I, and water, among which the coarse aggregate is swelled ceramsite, the cylinder compressive strength of sintered ceramsite is 4.5MPa, and the bulk density is 600Kg / m 3 , the volume ratio of coarse and fine aggregates is 2:1, the fine aggregate is pottery sand, the particle size of pottery sand is 0.5mm~2mm, and the cementing material I is composed of ordinary Portland cement with a label of 42.5MPa and granular calcium silicate nanofibers , the content of granular calcium silicate nanofibers is 5% of the mass of cementing material I, and the mass ratio of water to cementing material I is 0.6. Before the mixing of the above concrete, the granular calcium silicate nanofibers are treated with silicone oil fumigation and hydrophobic treatment, and then the cement and granular calcium silicate nanofibers are fully pre-mixed, and the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Compressive strengthaaaaaaaaaa
Cylinder compressive strengthaaaaaaaaaa
Bulk densityaaaaaaaaaa
Login to view more

Abstract

The invention provides a method for preparing a self-thermal-insulation concrete building block, and belongs to the technical field of preparation of building materials. The main body of the self-thermal-insulation concrete building block is a thermal insulation concrete structural frame; a plurality of sandwich cavities are enclosed on the outer wall and the inner wall of the frame; and organic light materials, inorganic light materials or organic-inorganic composite light materials are packed or filled in the cavities to form a thermal insulation core layer. The self-thermal-insulation concrete building block prepared by the method has high self-thermal-insulation performance, high shock resistance and high tenacity, is a structural material and a thermal insulation material and has remarkable effects of energy conservation, environment friendliness and reduction in building cost after being used.

Description

technical field [0001] The invention belongs to the technical field of building material preparation, and in particular relates to a preparation method of a self-insulating concrete block. Background technique [0002] The implementation of building insulation is a major measure for energy saving and emission reduction and sustainable development in the future. Its development direction is self-insulation. However, due to the defects of various self-insulation building block products: either the structure is not good, or the structure itself is complex and costly. High, or the construction is inconvenient, so it cannot be popularized and applied. The above-mentioned situation of self-insulating blocks has led to most buildings still passively adopting secondary insulation, that is, after the building is completed, light-weight insulation materials such as foam plastic boards and rubber powder polystyrene concrete are applied externally or externally, and the construction vol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B28B1/087B28B3/02B28B1/50B28B1/52C04B28/04C04B28/08C04B38/00
Inventor 樊传刚谢明儿钱伟郭万金
Owner 徐州东兴能源有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products