Post-treatment method of chinlon superfine denier fiber fabric

A technology of fiber fabric and nylon, which is applied in the post-processing field of nylon ultrafine denier fabric, and can solve the problems of low hydrostatic pressure resistance value of nylon ultrafine denier fabric, insufficient crispness of clothes, and low tear resistance strength, etc. , to achieve good tear resistance, reduce diffuse reflection, and good hydrostatic pressure resistance

Active Publication Date: 2012-06-20
ZHEJIANG TAIHUA NEW MATERIAL
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a method that can not only improve the performance of nylon ultrafine denier fiber fabrics, but also aim at the shortcomings of the prior art production of nylon ultrafine denier fiber fabrics, such as low hydrostatic pressure resistance, low tear resistance, and insufficient crispness of clothes. UV protection rating, hydrostatic pressure resistance and tear strength of fabrics, and post-treatment methods to improve their durability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Post-treatment method of chinlon superfine denier fiber fabric
  • Post-treatment method of chinlon superfine denier fiber fabric
  • Post-treatment method of chinlon superfine denier fiber fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] The base fabric is made of nylon superfine denier fiber. The warp and weft yarns of the base fabric are made of 20D / 24F nylon superfine denier filaments, and the warp and weft density is 720×680 / 10cm; the square meter weight is 56g / m 2 . Post-processing proceeds as follows:

[0052] 1. Desizing: use open width desizing machine. The temperature of the desizing tank is 98°C; the running speed of the fabric is 30m / min, and the processing time is 3min.

[0053] The formula of the treatment solution is based on the mass of each component per liter of water: liquid caustic soda 240g / L, refining agent 50g / L, penetrant 16g / L, chelating dispersant 8g / L. After desizing treatment, the residual size rate is 1.7%.

[0054] 2. Calendering treatment: High-temperature and high-pressure double-roll calender is used, the fabric running speed is 35m / min, and the pressure is 80kg / m 2 , the temperature is 160°C.

[0055] 3. Coating finishing: Floating knife coating at room temperature...

Embodiment 2

[0061] 1. Desizing: use open width desizing machine. The temperature of the desizing tank is 100°C; the running speed of the fabric is 27m / min. The formula of the treatment liquid is based on the mass of each component per liter of water: liquid caustic soda 260g / L, penetrant 19g / L, refining agent 55g / L, chelating dispersant 10g / L. After desizing treatment, the residual pulp rate is 1.1%

[0062] 2. Calendering treatment: high temperature and high pressure calendering machine is adopted, the fabric running speed is 30m / min, and the pressure is 100kg / m 2 The temperature was 170°C.

[0063] 3. Coating finishing: Floating knife coating at room temperature is adopted, the fabric running speed is 25m / min, and the baking temperature is 170°C. The front side of the cloth is coated with finishing agent A, and the reverse side of the cloth is coated with finishing agent B.

[0064] The components of the finishing solution and their contents in parts by weight are: finishing agent A...

Embodiment 3

[0068] 1, desizing: with embodiment 2. The residual pulp rate after desizing treatment is 1.2%

[0069] 2. Calendering treatment: high temperature and high pressure calendering machine is adopted, the fabric running speed is 23m / min, and the pressure is 90kg / m 2 , the temperature is 168°C.

[0070] 3. Coating finishing: the fabric running speed is 32m / min, and the baking temperature is 165°C.

[0071] The components of the finishing liquid and their contents in parts by weight are: finishing agent A has a viscosity of 20000 cps and 88 parts of polyurethane resin with a solid content of 31%; solvent A is 6 parts of dimethylformamide; 4 parts of isocyanate; 1 part of hypophosphorous acid parts; 1 part of titanium dioxide. Finishing agent B: 84 parts of organopolysiloxane and hydrophilic polysiloxane resin mixture; Solvent B: 11 parts of toluene; 2 parts of isocyanate; 3 parts of sodium dihydrogen phosphate.

[0072] The preparation process of the finishing liquid is as follo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention aims at the shortages that chinlon superfine denier fiber fabric of the prior art is easy in adhesive failure, low in hydrostatic pressure resistance, non-washable, low in tearing strength, , easy in impregnation of adhesive and inverse adhesion in the coating process, and the clothes made of the fabric is not stiff and smooth enough. Provided is a post-treatment method of the chinlon superfine denier fiber fabric. The method comprises three steps including desizing, calendering treatment and coating finishing, wherein, in the coating finishing step, one surface of the fabric is coated with a finishing agent A which is composed of components by weight part as follows: 86-90 parts of polyurethane resin, 4-8 parts of solvent A, 3-6 parts of bridging agent, 1-2 parts of promoter and 2-4 parts of titanium dioxide; the other surface of the fabric is coated with a finishing agent B which is composed of components by weight part as follows: 81.5-92.5 parts of silicone resin, 3-11 parts of solvent B, 2-5 parts of cross-linking agent and 2-5 parts of cross-linking catalyst. The fabric treated by the method disclosed by the invention is obviously improved in anti-tearing performance, anti-ultraviolet ray performance, static pressure resistance, stiffness and smoothness.

Description

technical field [0001] The invention relates to a post-treatment method for nylon superfine denim fiber fabrics. Background technique [0002] With the rapid development of social economy and the continuous improvement of people's material life, people have higher and higher requirements for outdoor leisure sportswear. Those heavy and monotonous clothing can no longer meet people's requirements. As consumers have higher and higher requirements for clothing comfort and personalization, nylon superfine denim fiber fabrics have emerged as the times require. Nylon ultra-fine denim fiber fabric has been widely used in outdoor leisure clothing because of its light weight, wear resistance, no insects, easy care and other excellent characteristics that natural fiber fabrics cannot match. [0003] Nylon ultra-fine denier fabric generally refers to the fabric whose yarn denier number is less than or equal to 20 denier. At present, there are mainly several specifications such as 10 d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/564D06M15/643D06M13/364D06M13/395D06M11/46D06L1/14D06M101/34
Inventor 沈卫锋许斌徐丽亚
Owner ZHEJIANG TAIHUA NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap